Spin tunneling properties in mesoscopic magnets: effects of a magnetic field

The tunneling of a giant spin at excited levels is studied theoretically in mesoscopic magnets with a magnetic field at an arbitrary angle in the easy plane. Different structures of the tunneling barriers can be generated by the magnetocrystalline anisotropy, the magnitude and the orientation of the field. By calculating the nonvacuum instanton solution explicitly, we obtain the tunnel splittings and the tunneling rates for different angle ranges of the external magnetic field ( θ _H = π/2 and π/2 < θ _H < π). The temperature dependences of the decay rates are clearly shown for each case. It is found that the tunneling rate and the crossover temperature depend on the orientation of the external magnetic field. This feature can be tested with the use of existing experimental techniques. Received 12 March 2001 and Received in final form 18 October 2001     

磁场对四端量子波导中电子输运性质的影响

采用模匹配方法，研究了非均匀磁场下开放的四端量子波导中的电子输运性质. 结果表明，从一端入射的电子可以透射到两个与之垂直的输出端和一个与之平行的输出端. 在没有外加磁场的情况下，两个垂直输出端的输运概率是相同的，但垂直端与水平端的输运概率不同；在外加磁场下，由于磁边缘态效应，两个垂直输出端的输运概率也有着相当大的差别. 通过施加不同的磁场，我们能获得丰富的电子输运结构，如台阶，宽谷，尖峰等；通过调节磁场的大小和比例以及结构参数可控制该量子结构在各输出端的输运概率. 关键词： 电子输运 介观体系 磁效应     

脉冲磁场处理对碳纳米管掺杂MgB2线材临界电流密度的影响

对碳纳米管(CNT)掺杂MgB₂超导体磁场处理后的行为进行了研究. 结果表明，CNT掺杂MgB₂超导体经5T脉冲磁场处理后临界电流密度J_c(H)在低磁场下提高了2—3倍，高场下提高一个数量级以上，扫描电镜结果显示CNT沿着处理磁场方向规则排列并且成为MgB₂基体的形核中心和高效的磁通钉扎中心. 关键词： 2')" href="#">MgB₂ 碳纳米管 脉冲磁场处理     

Adhesion studies of latex film surfaces on the meso- and nanoscale

In this paper the effects of surface roughness and annealing temperature (T) of latex coating films on adhesion are discussed for the different stages of the film formation process. The surface free energy of latex films was assessed in terms of practical work of adhesion (W) (or adherence) using a custom-built adhesion-testing device (ATD), atomic force microscopy (AFM), and contact angle measurements. For preannealed latex films surface roughness averages (R_a) were determined from AFM height images and were related to the values of W obtained from ATD measurements at room temperature. The results obtained using these tests exhibiting surface behavior on different length scales indicate a dependence of the measured adhesion on surface roughness and temperature, as well as on the length scale of the measurements.First preannealed samples were studied, which were obtained by heat treatment above the respective glass transition temperatures (T_g). Increasing the temperature of preannealing resulted in a decrease of the adherence observed in ATD experiments at room temperature. However, on the nanoscale, using AFM, no significant variation of the adherence was observed. This observation can be explained by roughness arguments. Preannealing decreases roughness which results in lower adherence values measured by ATD while for essentially single asperity AFM experiments roughness has an insignificant effect. Specimens were also annealed over a constant period of time (90 min) at different temperatures. At the end of the heat treatment, adhesion was measured at the treatment temperature by ATD. The amplified effect of temperature observed in this case on adherence is attributed to the combination of roughness decrease and increasing test temperature. In a third set of experiments completely annealed samples were studied by ATD as well as by AFM as a function of temperature. With increasing T values ATD showed a decrease in adherence, which is attributed to a decreasing surface free energy of the annealed films at elevated T values. AFM, on the other hand, showed an opposite trend which is assigned to increasing penetration of the tip into the tip/wetting polymer samples versus increasing temperature. Finally, annealing isotherms as a function of time were investigated by ATD in situ at different temperatures. This last set of experiments allowed us to optimize annealing time and temperature to achieve complete curing.     

测量冷原子温度的理论与近似拟合公式的误差分析

对短程飞行时间法(tim e-of-flight,TOF)中推算冷原子温度的理论拟合公式与近似拟合公式进行了误差分析与比较。研究表明:对于使用短程飞行吸收光谱信号推测冷原子团温度,当探测光光斑半径与冷原子团高斯半径之比k小于0.2时,理论拟合公式和近似拟合公式能很好的相符,随着探测光光斑半径与冷原子团高斯半径比值的逐渐增大,用近似拟合公式所得TOF吸收信号与用理论拟合公式所得TOF吸收信号的误差也将逐渐增大,当比值为0.5时,用近似拟合公式所得TOF吸收信号的误差将增大到20%。     

Impact of 100 MeV Au on the surface of relaxed Si0.5Ge0.5 alloy films studied by atomic force microscopy

We demonstrate a gradual surface modification process of relaxed Si_0.5Ge_0.5 alloy films by 100 MeV Au beam with fluence varying between 5 × 10¹⁰ and 1 × 10¹² ions/cm² at 80 K by means of atomic force microscopy (AFM). Presence of Ge quantum dots (QDs) was found in the virgin sample. The disappearance of the QDs were noticed when the samples were irradiated with a fluence of 5 × 10¹⁰ ions/cm². Craters were found developing at a fluence of 1 × 10¹¹ ions/cm². Apart from the evolution of the craters, blisters were also detected at a fluence of 1 × 10¹² ions/cm². Variation of the average root mean square value of the surface roughness as a function of fluence was examined.     

Pt(110)表面自吸附原子能量和力的改进分析型嵌入原子法分析

采用改进分析型嵌入原子法计算了Pt(110)表面自吸附原子的能量和法向力.当Pt吸附原子位于Pt(110)表面第一层原子的二重对称洞位上0.11nm时最稳定.Pt吸附原子的最佳迁移路径是由一个二重对称洞位沿密排方向迁移到最近邻的另一个二重对称洞位.在吸附原子远离表面的过程中，将依次经过排斥、过渡和吸引等三个区域.在排斥区和过渡区，由于吸附原子与表面原子间强的相互作用势，吸附原子的能量和法向力的形貌图均为(110)面原子排列的复形，与对势理论和嵌入原子法得到的结果一致.在吸引区，由于多体相互作用及晶体中原子 关键词： 金属表面 自吸附 能量 力     

核磁共振成像一维空间编码教学实验

利用梯度磁场实现检测信号的空间编码,是核磁共振成像(MRI)的关键技术.本文采用ccc系列样品将二维问题简化为一维,使用超小型教学用核磁共振成像仪进行了一维空间编码实验研究,并对实验过程及实验结果进行了计算模拟和分析.     

The epitaxial sexiphenyl (0 0 1) monolayer on TiO2(1 1 0): A grazing incidence X-ray diffraction study

A para-sexiphenyl monolayer of near up-right standing molecules (nominal thickness of 30 Å) is investigated in-situ by X-ray diffraction using synchrotron radiation and ex-situ by atomic force microscopy. A terrace like morphology is observed, the step height between the terraces is approximately one molecular length. The monolayer terraces, larger than 20 μm in size, are extended along the [0 0 1] direction of the TiO₂(1 1 0) substrate i.e. along the Ti-O rows of the reconstructed substrate surface. The structure of the monolayer and its epitaxial relationship to the substrate is determined by grazing incidence X-ray diffraction. Extremely sharp diffraction peaks reveal high crystalline order within the monolayer, which was found to have the bulk structure of sexiphenyl. The monolayer terraces are epitaxially oriented with the (0 0 1) plane parallel to the substrate surface (out-of-plane order). Four epitaxial relationships are observed. This in-plane alignment is determined by the arrangement of the terminal phenyl rings of the sexiphenyl molecules parallel to the oxygen rows of the substrate.     

Local structure analysis of smoky and colorless topaz using single crystal Al NMR

The angular dependence of the ²⁷Al NMR spectrum was measured for single crystals of smoky and colorless topaz, Al₂SiO₄(F,OH)₂. Smoky topaz was obtained by irradiating high energy neutrons to colorless topaz. The quadrupole coupling constant e²Qq/h and the asymmetry parameter η were obtained from the analysis of the angular dependences of quadrupole splitting of the ²⁷Al NMR spectrum. The local structures around the aluminum atoms in smoky and colorless topaz were discussed from the magnitude and the direction of the electric field gradient. The directions of principal axes of the EFG tensor of ²⁷Al were close to the directions of Al-O and Al-F bonds. The difference in the bond lengths between Al(1)-F(1) and Al(1)-F(2) was found to affect the x and y components of the EFG tensor.