Sol-Gel法制备La~(3+)改性的TiO_2纳米粉体

在常用的半导体光催化材料中,研究较多的有TiO2、ZnO、CdS等[1-3],其中TiO2因性能稳定、催化活性高、无毒、不产生二次污染和成本低廉等优点,在光催化降解污染物领域显示出优越的应用前景[3-6].     

Rare earth‐doped calcium‐based magnetic catalysts for transesterification of glycerol to glycerol carbonate

Several rare earth‐doped, calcium‐based magnetic catalysts were prepared for the synthesis of glycerol carbonate. The basicity and basic strength analysis of the catalysts showed that the doping of rare earth improved the basicity of the catalysts, and the doping of lanthanum maximized it. In addition, with the doping of lanthanum, the particle size of the catalyst became smaller to promote the organic reactants near the active sites of catalysts, thereby effectively improving the performance. NiFe₂O₄@[CaO‐La₂O₃] shows better catalytic performance with 99.0% yield of glycerol carbonate compared to the other catalysts. The NiFe₂O₄@(CaO‐La₂O₃) could be reused in six cycles without significant loss in activity.     

β-TCP/HAP多孔生物陶瓷的制备

以牛松质骨为原料,采用低温煅烧工艺,通过调整浸泡溶液浓度及煅烧温度等工艺参数,制备出具有良好生物活性,并保持天然骨多孔结构的β-TCP/HAP双相生物陶瓷。并采用XRD,SEM等手段对其成分、微观结构进行表征。结果表明:所制备的β-TCP/HAP多孔生物陶瓷的大孔孔径在300~500μm之间,微孔孔径在1~5μm之间,具有良好的生物活性和生物可降解性。通过控制煅烧温度和浸泡溶液浓度,制备出含较高TCP的β-TCP/HAP多孔生物陶瓷,而煅烧温度或浸泡溶液浓度过高会导致制备的样品中TCP的含量降低,焦磷酸钙的含量增加。     

天文观测相机低噪声CCD视频处理电路的分析与设计

在讨论天文观测相机低噪声视频处理电路的基础上,对前置放大、差分放大、可编程增益放大、相关双采样及16bit模数转换等关键组成部分进行了分析,给出各组成部分的设计方法。对所设计的低噪声视频处理电路进行了PSPICE仿真和实验测试,仿真和实验结果表明,该视频处理电路在本身引入噪声较小的同时,有效地抑制了CCD的复位噪声和1/f等低频噪声,使天文观测相机的整机噪声<15e-,达到了指标要求。     

基于曲线拟合的亚像素边缘定位方法的研究

图像的边缘定位是图像测量的关键之一,随着测量精度要求的提高,已由早期的像素级边缘定位发展到了现在的亚像素级边缘定位。根据地球在地球敏感器CCD阵面中的成像特性,提出了一种基于曲线拟合的亚像素边缘定位方法以获取地球“灼热圆盘”的边缘。该方法利用曲线拟合获得的拟合斜率以及灰度值来提取图像的边缘。仿真结果表明,采用曲线拟合亚像素边缘定位法可使图像的边缘定位精度达到百分之几个像素,具有较高的精度。     

地球同步轨道二维扫描像移补偿技术建模与分析

在建立二维扫描观测模型的基础上,提出了基于椭球体地球模型的二维扫描像移补偿方案,给出了任意空间观测到的目标位置的快速迭代算法,并以真实轨道和仿真姿态数据验证了像移补偿模型的实际性能。仿真结果表明,对于长周期(大于一个东西方向扫描行周期)轨道和姿态偏差,可以通过调整仪器坐标系内的扫描轨迹来实现像移补偿;同时,在现有轨道测量和控制条件下,轨道因素引起的瞬时方位角和俯仰角补偿量在0.01°~0.1°量级,且随轨道位置不同而变化。FY-2C卫星在轨偏航轴姿态失配修正实例证实了上述模型的有效性。     

铜-康铜热电偶的低温不均匀性实验研究

从冰点到液氮温度的宽低温区内,对随机选取的铜-康铜热电偶进行了重复性精度标定.测试结果表明,多次断偶重复焊接行为将产生约0.272 mV的标准差.这意味着在液氮条件下,温度测量过程的最大误差将达8.98 ℃.所以,对现场、尤其对深冷区的现场进行精确测温实验中出现的断偶故障,重新焊接后必须重新标定才能继续使用.     

低压闪蒸液滴形态和温度变化的研究

将液滴在常压下突然置于低压环境中,液滴由最初的平衡状态变成过热状态,发生闪蒸.本文实验研究了低压闪蒸液滴内部形态和温度的变化,系统描述了液滴闪蒸过程中的各种形态变化,总结了稳态闪蒸和稳态结冰过程中环境压力和初始温度对温度变化的影响.实验结果表明液滴闪蒸分六种形态.稳态闪蒸中环境压力越低,液滴的最终温度也越低;液滴的初始温度越高,降到最低温度的时间越长.稳态结冰过程中,液滴初始温度增加,液滴结冰温度和结冰回升最高温度也随之增加;液滴的结冰温度和回升最高温度随环境压力的增高而减小.     

Classical in-plane negative magnetoresistance and quantum positive magnetoresistance in undoped InSb thin films on GaAs (1 0 0) substrates

Magnetoresistance (MR) effects have been investigated in perpendicular and parallel magnetic fields at 300, 80 K and liquid He temperatures for undoped InSb thin films 0.1–2.3 μm thick grown on GaAs(1 0 0) substrates by MBE. At high temperatures, the intrinsic carriers show the parabolic negative MR observable only in magnetic fields parallel to the film. The skipping-orbit effect due to surface boundary scattering in the classical orbits in the plane vertical to the film has been argued to be responsible for the negative MR. At low temperatures (T=80 K), the transport is dominated by the two-dimensional (2D) electrons in the accumulation layers at the InSb/GaAs(1 0 0) hetero interface; MR is positive and shows a logarithmic increase with anisotropy between parallel and perpendicular field orientation, arising from the 2D weak anti-localization (WAL) that reflects the interplay between the spin-Zeeman effect and strong spin–orbit interaction caused by the asymmetric potential at the interface (Rashba term). The zero-field spin splitting energy of Δ₀13 meV, the electron effective mass of m^*0.10m₀ seven times of the band edge mass in bulk InSb and the effective g-factor of |g^*|15 in the accumulation layer have been inferred from fits of MR for the 0.1 μm thick film to the 2D WL theory.     

Photon interaction studies using 241Am γ-rays

We have carried out some photon interaction measurements using 59.54 keV γ-rays from a ²⁴¹Am source. These include γ attenuation studies as well as photoelectric absorption studies in various samples. The attenuation studies have been made using leaf and wood samples, samples like sand, sugar etc., which contain particles of varying sizes as well as pellets and aqueous solutions of rare earth compounds. In the case of the leaf and wood samples, we have used the γ-ray attenuation technique for the determination of the water content in fresh and dried samples. The variation of the attenuation coefficient with particle size has been investigated for sand and sugar samples. The attenuation studies as well as the photoelectric studies in the case of rare earth elements have been carried out on samples containing such elements whose K-absorption edge energies lie below and close to the γ-energy used. Suitable compounds of the rare earth elements have been chosen as mixture absorbers in these investigations. A narrow beam good geometry set-up was used for the attenuation measurements. A well-shielded scattering geometry was used for the photoelectric measurements. The mixture rule was invoked to extract the values of the mass attenuation coefficients for the elements from those of the corresponding compounds. The results are consistent with theoretical values derived from the XCOM package.