Shape sensitivity of a plane crack front

The 3D‐elasticity model of a solid with a plane crack under the stress‐free boundary conditions at the crack is considered. We investigate variations of a solution and of energy functionals with respect to perturbations of the crack front in the plane. The corresponding expansions at least up to the second‐order terms are obtained. The strong derivatives of the solution are constructed as an iterative solution of the same elasticity problem with specified right‐hand sides. Using the expansion of the potential and surface energy, we consider an approximate quadratic form for local shape optimization of the crack front defined by the Griffith criterion. To specify its properties, a procedure of discrete optimization is proposed, which reduces to a matrix variational inequality. At least for a small load we prove its solvability and find a quasi‐static model of the crack growth depending on the loading parameter. Copyright © 2003 John Wiley & Sons, Ltd.     

Fracture Model for a Thin Layer of a Fibrous Composite

A model for a flat isolated layer of a unidirectional fibrous composite with a regular structure is constructed to investigate the possible variants of its failure development. An integrodifferential equation for determining the forces in fibers is obtained. Primary attention is focused on examining the failure process after the rupture of one fiber. This causes a drastic redistribution of stresses, which can lead to a failure of adjacent fibers owing to the increased load on them, to an interfacial shear fracture, and to the matrix cracking. It is shown that the development of layer failure is determined by the strength of fibers, the crack resistance of the matrix in axial tension and transverse shear, and also by the adhesion strength of the matrix-fiber interface. The sufficient conditions of applicability of the brittle fracture model are formulated.     

韧脆转变的一种细观随机模糊统计分析

对不同温度和应力状态下40Cr材料进行大子样宏观试验和细观观测,提出了一种新的材料断裂韧脆转变统计随机模糊模型。该模型认为,在统计意义上,材料的韧性断裂为空穴机制,临界空穴扩张比参数可以作为韧性断裂的判据;材料的脆性断裂可以用内嵌币状裂纹的脆性断裂模型来模拟,为此测量断裂特征长度,提出并具体计算了控制币状裂纹失稳扩张的细观临界应力强度因子;在韧脆转变区域内,这两种机理并存并相互竞争,为此提出了模糊准则。对模型参数进行了测量和统计分析,给出分布规律,给出了计算断裂特征的概率模型。计算了韧脆转变区域内的细观机制变化和宏观响应。结果表明,该模型及分析方法可以很好地模拟应力状态及温度对韧脆转变的影响。     

短脉冲载荷下金属材料的层裂破坏

 本文用点炮加载聚酯薄膜飞片撞击金属靶材料，飞片速度0.714~2.24 km/s，脉冲宽度40~80 ns，击靶压力为2.280~11.952 GPa。在回收的铝、铜和钢靶样品上观察到层裂现象。通过金相分析发现它们的破坏方式与在一般较长脉冲加载下的破坏方式相似，铝和铜以延性方式破坏；钢则以脆性方式破坏。一维和二维数值模拟结果表明通常的几种层裂判据在这个应力、应变和应变率范围内也基本上适用。     

各向异性材料中共线刚性线夹杂的纵向剪切问题

本文研究各向异性材料中共线刚性线夹杂，（有时称作“硬裂纹”或“反裂纹”问题）的纵向剪切问题。利用复变函数方法，提出了一般问题的公式和某些实际重要问题的封闭形式解，考察了刚性线端点附近的应力分布．从本文解答的特殊情形，可以直接导出各向同性材料相应问题的公式和结果，包括某些已有的结果￣［７］．     

用概率断裂力学方法预测管状接头的疲劳寿命

本文研究了Ｔ型管状接头在面内和面外弯曲循环载荷作用下的疲劳强度问题，通过将材料常数和初始裂纹尺寸作为随机变量，采用ＭｏｎＣａｒｌｏ模拟方法对疲劳寿命进行了统计分析．同时，对计算结果进行了线性回归，并与实验结果作了比较。     

A model for crack formation during active solid pyrolysis of a char-forming solid: crack patterns; surface area generation; volatile mass efflux

A model is developed for the formation and propagation of cracks in a material sample that is heated at its top surface, pyrolyses, and then thermally degrades to form char. In this work the sample is heated uniformly over its entire top surface by a hypothetical flame (a heat source). The pyrolysis mechanism is described by a one-step overall reaction that is dependent nonlinearly on the temperature (Arrhenius form). Stresses develop in response to the thermal degradation of the material by means of a shrinkage strain caused by local mass loss during pyrolysis. When the principal stress exceeds a prescribed threshold value, the material forms a local crack. Cracks are found to generally originate at the surface in response to heating, but occasionally they form in the bulk, away from ever-changing material boundaries. The resulting cracks evolve and form patterns whose characteristics are described. Quantities examined in detail are: the crack spacing in the pyrolysis zone; the crack length evolution; the formation and nature of crack loops which are defined as individual cracks that have joined to form loops that are disconnected from the remaining material; the formation of enhanced pyrolysis area; and the impact of all of the former quantities on mass flux. It is determined that the mass flux from the sample can be greatly enhanced over its nominal (non-cracking) counterpart. The mass efflux profile qualitatively resembles those observed in Cone Calorimeter tests.     

对薄层柱壳爆炸膨胀断裂过程的研究

 本文提出了一个用于描述动态破坏发展过程的损伤度函数。从这个损伤度函数出发,把材料特征性方程取为强化粘塑性本构方程形式,导出了薄层柱壳爆炸膨胀运动在两种近似下（恒定膨胀速度近似合恒定应变速率近似）断裂判据的解析表达式。结果分析表明,在上述条件下,存在着一个动态断裂“塑性峰”,在这个峰值条件的应变率下,柱壳出现贯穿断裂时刻的应变最大。以软钢为算例,本断裂判据可以比较好地解释Иванов和陈大年等给出的实验结果。这时,动态断裂“塑性峰”对应的应变率为4×10⁴ s^-1,相应的应变约为60%~80%。     

Effect of solute atoms on fracture toughness in dilute magnesium alloys

The effect of alloying elements on the toughness and the fracture behaviour was investigated on seven kinds of Mg-0.3?at.% X (X?=?Ag, Al, Ca, Pb, Sn, Y and Zn) alloys with a grain size of 3–5?μm. The fracture toughness and fracture behaviour in magnesium alloys were closely related to the segregation energy. The Mg–Al and –Zn alloys that had small segregation energy showed high toughness and ductile fracture in most regions, while the Mg–Ca alloy with large segregation energy exhibited low toughness and intergranular fracture. These different tendencies resulted from solute segregation at grain boundaries (GBs). The change in the lattice parameter ratio was the influential material parameter regardless of whether the GB embrittlement was for enhancement or suppression.     

Externally applied stress sign and film elastic properties effects on brittle film fracture

Rectangular stainless steel samples with TiN film deposited on the front lateral surface were loaded in three-point bending to the maximum normal strain of 6%. Scanning electron microscopy showed that vertical cracks appeared in the tension zone when the tensile strain exceeded 1.5%, while horizontal cracks appeared in the compression zone when the compressive strain exceeded –2.9%. Film cracks in the compressive zone originate from the tensile stress imposed by the plastically deformed substrate due to the Poisson’s expansion. Taking plastic deformation and Poisson’s expansion of the substrate in compression into account, theoretical analysis of normal stress distribution along the cracked film segment in compression is presented. Substrate strain and film elastic properties affect film cracking in the compressive zone. At larger compressive strain, some transverse cracks along with buckling cause the film spallation. The presented method is useful for studying brittle film fracture with variable strain levels in a single sample.