Developing a hybrid emulsion polymerization system to synthesize Fe3O4/polystyrene latexes with narrow size distribution and high magnetite content

A hybrid emulsion polymerization was formulated for synthesizing Fe₃O₄/polystyrene composite latex. This system, containing binary droplets that are magnetic (Mag)‐droplets with a diameter of 100–200 nm and styrene (St)‐droplets with a diameter of 3–4 μm, was obtained by mixing Mag‐miniemulsion and St‐macroemulsion. With extremely low surfactants concentration (?critical micelle concentration, CMC), the nucleated loci are selectively controlled in the Mag‐droplets, as the result of smaller droplet size and larger surface ratio. Both water‐soluble potassium persulfate (KPS) and oil‐soluble 2,2′‐azobis(2‐isobutyronitrile) was adopted to initiate the polymerization. In the presence of KPS, magnetic polystyrene latices with particles size of 60–200 nm, narrow size distribution, and high magnetite content (86 wt % measured by TGA) were attained successfully. The synthesized magnetic Fe₃O_4/polystyrene latices assembled into well‐ordered hexagonal structure in the surface of a carbon supported copper grid. The influence of various parameters on various aspects of the as‐synthesized Fe₃O₄/polystyrene was investigated in detail: type of initiator on composite morphology, feed ratio of Mag‐miniemulsion and St‐macroemulsion on magnetite content, and hydrophobic agent or amount of surfactant on size and size distribution. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5285–5295, 2007     

利用光反射精确测量亚共析碳钢的含碳量

本文从光学角度出发提出了一种经济实用、精度高的测量亚共析碳钢中碳的含量的新方法。阐述了该方法的测量原理，即以金相试样表面对光的反射程度来判定其含碳量，并给出了有关经验公式及数据处理方法。     

江汉平原上空QTEC变化特征的统计分析

提出了一种观测台网用多接收机性能一致性的标定方法，并利用江汉平原GPS接收台网的观测数据，分析了该地区上空QTEC的日变化、季节变化、年变化和逐年变化的统计特征．标定结果表明，不同接收机之间的仪器偏差是从双频GPS卫星信标推算QTEC的主要误差来源之一，必须校正．统计分析证实，江汉平原上空QTEC的日变化特征同时受电离层和等离子层控制，其年变化以半年周期为主，峰值和谷值分别出现在两分点和两至点附近，QTEC值的逐年变化从太阳活动峰年到低年逐年下降，与以太阳黑子数为代表的太阳活动密切相关．     

Studies on calcium‐containing poly(urethane ether)s

The calcium salt of mono(hydroxyethoxyethyl)phthalate [Ca(HEEP)₂] was synthesized by the reaction of diethylene glycol, phthalic anhydride, and calcium acetate. Calcium‐containing poly(urethane ether)s (PUEs) were synthesized by the reaction of hexamethylene diisocyanate (HMDI) or tolylene 2,4‐diisocyanate (TDI) with a mixture of Ca(HEEP)₂ and poly(ethylene glycol) (PEG₃₀₀ or PEG₄₀₀) with di‐n‐butyltin dilaurate as a catalyst. A series of calcium‐containing PUEs of different compositions were synthesized with Ca(HEEP)₂/PEG₃₀₀ (or PEG₄₀₀)/diisocyanate (HMDI or TDI) molar ratios of 2:2:4, 3:1:4, and 1:3:4 so that the coating properties of the PUEs could be studied. Blank PUEs without calcium‐containing ionic diols were also prepared by the reaction of PEG₃₀₀ or PEG₄₀₀ with HMDI or TDI. The PUEs were well characterized by Fourier transform infrared, ¹H and ¹³C NMR, solid‐state cross‐polarity/magic‐angle‐spinning ¹³C NMR, viscosity, solubility, and X‐ray diffraction studies. The thermal properties of the polymers were also studied with thermogravimetric analysis and differential scanning calorimetry. The PUEs were applied as top coats on acrylic‐coated leather, and their physicomechanical properties were also studied. The coating properties of PUEs, such as the tensile strength, elongation at break, tear strength, water vapor permeability, flexing endurance, cold crack resistance, abrasion resistance, color fastness, and adhesive strength, were better than the standard values. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2865–2878, 2003     

An Electroacoustic Investigation of Concentrated Aqueous Suspensions of Calcium Pyrophosphate

The zeta potential of concentrated suspensions of calcium pyrophosphate were investigated using electroacoustics. The particles were negatively charged over the entire pH range studied. It proved impossible to reduce the pH of the suspension below 1.8, but the iso electric point could be estimated to occur at approximately pH 1. Two commercially available dispersants (one cationic and one anionic) were then added in small increments to the suspension in order to follow the change in zeta potential as the dispersants adsorbed onto the particles. From the shape of the curve it was possible to estimate the optimum adsorbed amount of dispersant required to fully coat the particles. The cationic dispersant adsorbed strongly and the optimum dosage was estimated at 2.5 ml of active polymer/kg of powder. Anionic dispersants are known to adsorb onto negatively charged ceramic oxide particles, but the anionic dispersant used in this study did not adsorb onto the negatively charged calcium pyrophosphate particles.     

聚异丁烯高活性端基含量及相对分子质量测定方法的研究

综合使用核磁，VPO和近红外光谱分析技术对聚异丁烯活性端基含量以及相对分子质量的测定进行了详细研究，分别建立核测定聚异丁烯活性端基含量以及其他烯键含量和近红外光谱快速测量聚异聚丁烯活性端基含量。其他烯键含量和相对分子质量的分析方法。成对t检验结果表明，近红外光谱分析方法测定结果与核磁和VPO方法测定结果之间无显著性差异。     

空气中水含量的计算及其在色谱分析中的应用

本文介绍了空气中水含量的计算式并编制了空气中的水含量表。实验证明,表上的数据适用于色谱分析。     

Effect of carbon content on the microstructure and the cracking susceptibility of Fe-based laser-clad layer

The laser cladding of Fe-based alloys on a medium carbon steel substrate was performed using a CO₂ laser and Ar shielding gas that was blown into a molten pool. The microstructure and cracking susceptibility of the laser-clad layers were studied in terms of carbon additions. Results show that the small change of the carbon content in the alloy powders can obviously change the microstructure and properties of the layers. When the carbon content is in the range of 0.3–0.4 wt.%, the decrease of the carbon content in alloy powders will increase the hardness and toughness of the layers simultaneously under the same process parameters. As a result, crack-free coatings with high hardness can be obtained. As the carbon content increases from 0.2 wt.% to 0.4 wt.%, the segregation ratio of chromium increases, while the segregation ratios of nickel, manganese, and silicon first decrease and then increase. At the same time, a new designing principle concerning the composition and microstructure has been put forward, and the principal mechanisms of strengthening and toughening of the layers are fine-grain strengthening and low carbon martensitic phase transformation strengthening.     

Effects of barium on the nonlinear electrical characteristics and dielectric properties of SnO2-based varistors

The effects of barium on electrical and dielectric properties of the SnO_2·Co_2O_3·Ta_2O_5 varistor system sintered at 1250℃ for 60min were investigated. It is found that barium significantly improves the nonlinear properties. The breakdown electrical field increases from 378.0 to 2834.5V/mm, relative dielectric constant (at 1kHz) falls from 1206 to 161 and the resistivity (at 1kHz) rises from 60.3 to 1146.5kΩ·cm with an increase of BaCO_3 concentration from 0mol% to 1.00mol%. The sample with 1.00mol% barium has the best nonlinear electrical property and the highest nonlinear coefficient (α=29.2). A modified defect barrier model is introduced to illustrate the grain-boundary barrier formation of barium-doped SnO_{2}-based varistors.     

Ca(NO3)2•4H2O-catalysed Biginelli Reaction: One-pot Synthesis of 1,2,3,4-Tetrahydropyrimidin-2-ones/pyrimidine-2-thiones under Solvent-free Conditions

The synthesis of 1,2,3,4-dihydropyrimidinone/thione derivatives was achieved in good to excellent yields using calcium(II) nitrate as catalyst to promote the Biginelli three-component condensation reaction from a diversity of aromatic aldehydes, β-keto compounds and urea or thiourea. The reaction was carried out under solvent-free conditions.