五乙烯六胺改性金属有机骨架材料MIL-101(Cr)对CO_2的吸附性能

采用溶剂热法合成金属有机骨架材料MIL-101(Cr),用回流法将五乙烯六胺(PEHA)负载到MIL-101(Cr)孔道中的不饱和金属位点上,使用扫描电镜、粉末X射线衍射、氮气物理吸附、元素分析和傅里叶变换红外光谱等表征手段考察材料的结构和形貌,测试氨基改性前后的MIL-101(Cr)在25℃、不同压力下对CO_2的吸附效果。结果表明,负载0.24 m L五乙烯六胺后的MIL-101(Cr)对CO_2的吸附效果最好,在25℃、常压下对CO_2的饱和吸附量可达58.944 mg/g,相比未负载五乙烯六胺的MIL-101(Cr)吸附量(CO_2饱和吸附量为44.208 mg/g)增加了33%。随着吸附压力的增加,MIL-101(Cr)和0.24PEHAM IL-101(Cr)对CO_2的饱和吸附量逐渐增加,当吸附压力为1.1 MPa时,两者的吸附量分别为1 147.59和1 256.74 mg/g,表明该类材料在高压下对CO_2有着良好的吸附效果。     

Four New Terpenoids from Xylaria sp. 101

One new diterpenoid, xylarenolide ( 1 ), and three new sesquiterpenoids, xylaranol A ( 2 ), xylaranol B ( 3 ), and xylaranic acid ( 4 ), were obtained from the fungal strain Xylaria sp. 101, which was isolated from the fruiting body of Xylaria sp. collected in Gaoligong Mountain, Yunnan Province. Their structures were elucidated by spectroscopic analyses, including 1D‐ and 2D‐NMR experiments, and by HR‐Q‐TOF mass spectrometry. Their antimicrobial activities were evaluated.     

Pt/MIL-101(Cr)在肉桂醛选择性加氢反应中的催化性能

采用简单易行的浸渍法将Pt纳米粒子负载到MIL-101(Cr)上,制备了Pt/MIL-101(Cr)催化剂,并对其在肉桂醛选择性加氢反应的催化性能进行了研究。XRD、N₂吸附、TEM和催化性能的研究结果表明,Pt的负载量对负载于MIL-101(Cr)上Pt纳米粒子的尺寸及所制备催化剂对肉桂醇的选择性有很大影响。低Pt负载量(1.0%)的Pt/MIL-101(Cr)较其他MOFs和无机材料在肉桂醛选择性加氢反应中表现出了高的催化性能,在优化的反应条件下肉桂醛转化率和对肉桂醇的选择性可分别达96.5%和86.2%。Pt/MIL-101(Cr)催化剂具有良好的稳定性。Pt/MIL-101(Cr)所表现出的优良的催化性能同MIL-101(Cr)载体的孔道结构及其表面性质密切相关。     

锐钛矿型TiO2担载的Pd催化剂用于乙炔选择加氢的催化性能及其表征

Anatase TiO₂ nanospindles containing 89% exposed {101} facets (TiO₂-101) and nanosheets with 77% exposed {001} facets (TiO₂-001) were hydrothermally synthesized and used as supports for Pd catalysts. The effects of the TiO₂ materials on the catalytic performance of Pd/TiO₂-101 and Pd/TiO₂-001 catalysts were investigated in the selective hydrogenation of acetylene to polymer-grade ethylene. The Pd/TiO₂-101 catalyst exhibited enhanced performance in terms of acetylene conversion and ethylene yield. To understand these effects, the catalysts were characterized by H₂ temperature-programmed desorption (H₂-TPD), H₂ temperatureprogrammed reduction (H₂-TPR), transmission electron microscopy (TEM), pulse CO chemisorption, X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). The TEM and CO chemisorption results confirmed that Pd nanoparticles (NPs) on the TiO₂-101 support had a smaller average particle size (1.53 nm) and a higher dispersion (15.95%) than those on the TiO₂-001 support (average particle size of 4.36 nm and dispersion of 9.06%). The smaller particle size and higher dispersion of Pd on the Pd/TiO₂-101 catalyst provided more reaction active sites, which contributed to the improved catalytic activity of this supported catalyst.