Photografting of vinyl polymers onto ultrafine inorganic particles: Photopolymerization of vinyl monomers initiated by AZO groups introduced onto these surfaces

The photografting of polymers onto ultrafine inorganic particles, such as silica and titanium oxide, initiated by azo groups introduced onto these surfaces was investigated. The introduction of azo groups onto the particles was achieved by the reaction of 4,4′-azobis(4-cyanopentanoic acid) with surface isocyanate groups, which were introduced by the treatment with tolylene 2,4-diisocyanate. It was found that the photopolymerization of vinyl monomers, such as methyl methacrylate (MMA), styrene, and N-vinylcarbazole, is initiated by ultrafine particles having azo groups. The corresponding polymers were effectively grafted onto these surfaces through the propagation of the polymer from the surface radicals formed by the photodecomposition of the azo groups: e.g., the percentage of grafting of PMMA and polystyrene onto silica was reached to 112 and 176%, respectively. The percentage of grafting onto silica in the graft polymerization initiated by photodecomposition of surface azo groups was much larger than that initiated by thermal decomposition. Polymer-grafted ultrafine particles thus obtained gave a stable colloidal dispersion in good solvents for the grafted chain. © 1994 John Wiley & Sons, Inc.     

La2Zr2O7催化剂结构相变对甲烷氧化偶联反应性能的影响

采用共沉淀法并通过改变焙烧温度制备了一系列具有不同晶相结构的La₂Zr₂O₇催化剂，在微型固定床反应器上评价其甲烷氧化偶联反应性能，并利用XRD、Raman、CO₂-TPD、XPS等表征手段，探究催化剂的物相结构、表面碱性以及表面氧物种的变化规律。结果表明，随着焙烧温度从700℃逐渐升高到1200℃，La₂Zr₂O₇催化剂结晶度不断提高，晶相发生明显变化，从无定形结构逐渐向缺陷萤石结构过渡，最终转变成烧绿石结构。焙烧温度提高促使La₂Zr₂O₇晶相转变过程中，催化剂表面的碱性强度减弱，中等碱性位数量以及具有催化活性的表面氧物种O₂^2-和O₂^-的相对含量不断减少，致使催化剂的CH₄转化率和C₂₊选择性不断降低。其中，无定形LZO-CP-700催化剂表现出最佳的甲烷氧化偶联反应性能。     

Theoretical study of the reaction of Sc with SCO in gas phase

In order to elucidate the mechanism of reaction M⁺ + SCO, both triplet and singlet potential energy surfaces (PESs) for the reaction of Sc⁺ + SCO have been theoretically investigated using the DFT (B3LYP/6-311+G*) level of theory. The geometries for reactants, intermediates, transition states and products were completely optimized. All the transition states were verified by the vibrational analysis and the intrinsic reaction coordinate calculations. The involving potential energy curve-crossing dramatically affects reaction mechanism, reaction rate has been discussed, and the crossing points (CPs) have been localized by the approach suggested by Yoshizawa et al. The present results show that the reaction mechanism are insertion–elimination mechanism both along the C–S and C–O bond activation branches, but the C–S bond activation is much more favorable in energy than the C–O bond activation. All theoretical results not only support the existing conclusions inferred from early experiment, but also complement the pathway and mechanism for this reaction.     

水相湿法改性纳米碳酸钙表面性质的研究

用特定的表面改性剂在水相中对纳米碳酸钙的悬浮液进行了湿法改性。红外光谱和热失重分析证明,改性剂与碳酸钙之间以化学键结合;沉降体积和接触角的测定结果说明改性粒子在液体石蜡中的润湿性和疏水性得到了提高;透射电子显微镜照片显示改性粒子在液体石蜡中有更好的分散性;体系粘度实验表明改性粒子与液体石蜡之间有较好的相容性。     

表面包覆改性对纳米CeO2分散性的影响

了改善纳米CeO2在Zn-Al类共晶合金中的分散性,采用超声液相包覆法对纳米CeO2进行表面活性剂表面包覆改性,并用AES测定了包覆层的厚度,用TEM研究了CeO2的团聚状况,用TGA分析了有机物包覆层的炭化温度范围,最后用FE-SEM观察了CeO2在复合材料中的分散情况。结果表明,包覆在纳米CeO2表面的厚度约为20 nm的表面活性剂层提高了微粒的分散性,而且该包覆层在495℃时已经炭化。热力学计算的结果也表明,炭化层能与氧化膜反应,该反应提高了CeO2与基体间的润湿性,并使其均匀分布在基体合金中。     

Molecular beams and model catalysis: activity and selectivity of specific reaction centers on supported nanoparticles.

Reaction kinetics on nanometer-scale particles are different from those on extended surfaces of bulk materials. This fact has been utilized for a long time to empirically maximize the performance of heterogeneous catalysts, but the understanding of the underlying effects is poor at the microscopic level. Modern molecular beam-based methods, however, allow us to derive very detailed kinetic information on catalytically active surfaces. In combination with structurally highly controlled model catalysts, microscopic insights into the activity and selectivity of specific reaction centers on catalyst nanoparticles can be obtained. This combined approach is illustrated through simple model reactions.     

原位漫反射红外光谱研究氮氧化物在Ag-ZSM-5催化剂上的吸附态及选择性催化还原反应机理

利用原位分析方法对催化剂表面吸附态进行动态表征，对了解催化反应机理具有重要的意义。漫反射红外光谱是一种理想的原位方法，应用该方法在298－773K范围原位考察了以丙烯为还原剂，NO在Ag-ZSM-5催化剂上的吸附态及选择性催化还原过程。认为NO的选择性催化还原符合直接作用机理，还原的关键是形成有机－氮氧化物（R－NO2或R－ONO）中间体。O2的作用是使C3H6充分活化，并是有效产生有机－氮氧化物不可缺少的条件。     

The effect of covalent surface immobilization on the bactericidal efficacy of a quaternary ammonium compound

This study investigates the effect of surface immobilization on the bactericidal function of a quaternary ammonium compound. Quaternary ammonium silane (QAS) coated planar surfaces did not produce any measurable mortality of Staphylococcus aureus, while 1 µm QAS‐coated microparticles did produce S. aureus mortality. The experiments using QAS‐coated microparticles indicate that the ability of QAS molecules to disrupt the cell wall is not hindered by covalent immobilization of QAS to a surface. These results provide evidence that S. aureus cells on a QAS‐coated planar surface are not exposed to a sufficient number of QAS molecules to produce significant mortality. This result has important implications for the development of self‐decontaminating coatings. Covalent immobilization is used to prevent leaching of the bactericidal compound. However, covalent immobilization may result in a significant tradeoff in bactericidal performance. Published in 2007 by John Wiley & Sons, Ltd.     

硼酸酯偶联剂的合成与表征

通过分子结构设计，合成了一种氮一硼内配位结构的硼酸酯偶联剂，解决了硼酸酯水解稳定性差的问题，同时分子结构中含有氨基、丁氧基等活性基团。用傅立叶变换红外光谱对硼酸酯进行了结构表征，讨论了原料配比、合成工艺等对硼酸酯收率及反应速率的影响，并通过实验确定了最佳配方及工艺。对硼酸酯的物理性能、溶解性、水解稳定性及对硼酸铝晶须的表面处理效果进行了表征。结果表明：合成的硼酸酯偶联剂由于具有氮-硼内配位作用，表现出优良的水解稳定性，并且硼酸酯偶联剂对硼酸铝晶须具有良好的表面改性效果。     

XPS,AFM, ATR and TPD evidence for terraced,dihydrogen terminated, 1×1 (100) silicon

Heating (100) silicon at high temperature (say, higher than 850 °C) in H₂, cooling to 670–700 °C in the same ambient, and quenching to room temperature in N₂ results in environmentally robust, terraced 1 × 1 (100) SiH₂. Evidence for this conclusion is based on angle‐resolved x‐ray photoelectron spectroscopy, atomic force microscopy, infrared absorption spectroscopy in the attenuated total reflection mode, thermal programmed desorption, and reflection high‐energy electron diffraction. Copyright © 2005 John Wiley & Sons, Ltd.