Epoxy-timber composites have received increasing attention during the last decades because there are many advantages related to their uses as construction materials in applications such as timber bridges. However, the durability of epoxy-timber composites under outdoor conditions has become a concern for many epoxy resins. This study evaluated the chemical, thermal, and mechanical properties of two cured epoxies, the product of the diglycidyl ether of bisphenol A with 2,4-trimethyl-1,6-hexanediamine (DGEBA-TMDA) and the analogous resin prepared with the hydrogenated diglycidyl ether of bisphenol A (HDGEBA-TMDA), each mixed with 2?wt. % calcium sulfate (CS). We hypothesized that the use of CS, as an inorganic UV absorber, could decrease undesirable effects arising from exposure to UV light, moisture, and extreme temperatures.
An accelerated aging chamber simulated natural weathering for 1, 2, 3, 4, and 6?months. Chemical changes in cured epoxy systems over time in the presence and absence of CS fillers were determined using Fourier transform infrared spectroscopy (FT-IR). Thermal degradation profiles before and after exposure to accelerated weathering were followed by thermogravimetric analysis (TGA). The glass transition temperatures (Tg) before and after accelerated weathering were measured, and the effect of accelerated weathering on the surface morphology of the epoxy systems was investigated by scanning electron microscopy (SEM). In the presence of CS, after 6?months accelerated weathering the tensile strength of DGEBA-TMDA reduced by 23.8?±?2.4%, compared to 46.5?±?5.5% in its absence, while the corresponding values for HDGEBA-TMDA were 21.4?±?2.1% and 28.7?±?1.8%. 相似文献
Melt extrusion was used to prepare binary nanocomposites of ethylene copolymers and organoclay and trinary nanocomposites of low-density polyethylene (LDPE), ethylene copolymer and organoclay. X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to analyze the structure of the clay phase and the morphology of the nanocomposites. Influences of the comonomer in the copolymer and the content of the copolymer on the morphology of the resulting nanocomposites were discussed. The binary and the trinary composites may form intercalated or exfoliated structures depending on the interaction between the copolymer and the clay layers and the content of the copolymer. 相似文献
Electrically conductive composites were prepared via the chemical oxidative polymerization of the pyrrole monomer in polystyrene
(PS) and zinc neutralized sulfonated polystyrene (Zn-SPS) films under supercritical carbon dioxide (SC-CO2) conditions. The strong swelling effect of SC-CO2 made polypyrrole (PPy) particles not only form on the surface, but also become incorporated into the film, resulting in a
homogeneous structure with a relatively higher conductivity. By comparison, the composite prepared in aqueous solutions shows
a skin-core structure and a conductivity of 3 to 4 orders of magnitude lower than that of the former due to the diffusion-controlled
process of the pyrrole monomer. The percolation thresholds of PS/PPy and Zn-SPS/PPy composites were 6.2% and 2.7% of the volume
fraction of PPy, respectively, much lower than the theoretically predicted value of 16%. Moreover, the conductive composites
prepared under SC-CO2 conditions showed higher thermal stability, especially in the high-temperature region.
Translated from Chemical Journal of Chinese Universities, 2006, 27(4): 771–774 (in Chinese) 相似文献
We demonstrate a novel strategy for the preparation of mesoporous silica-supported, highly dispersed, stable metal and bimetal nanoparticles with both size and site control. The supporting mesoporous silica, functionalized by polyaminoamine (PAMAM) dendrimers, is prepared by repeated Michael addition with methyl acrylates (MA) and amidation reaction with ethylenediamine (EDA), by using aminopropyl-functionalized mesoporous silica as the starting material. The encapsulation of metal nanoparticles within the dendrimer-propagated mesoporous silica is achieved by the chemical reduction of metal-salt-impregnated dendrimer-mesoporous silica by using aqueous hydrazine. The site control of the metal or bimetal nanoparticles is accomplished by the localization of inter- or intradendrimeric nanoparticles within the mesoporous silica tunnels. The size of the encapsulated nanoparticles is controlled by their confinement to the nanocavity of the dendrimer and the mesopore. For Cu and Pd, particles locate at the lining of mesoporous tunnels, and have diameters of less than 2.0 nm. For Pd/Pt, particles locate at the middle of mesoporous tunnels and have diameters in the range of 2.0-4.2 nm. The Pd and Pd/Pt nanoparticles are very stable in air, whereas the Cu nanoparticles are stable only in an inert atmosphere. 相似文献
Increased attention is being focused on metal-organic frameworks as candidates for hydrogen storage materials. This is a result of their many favorable attributes, such as high porosity, reproducible and facile syntheses, amenability to scale-up, and chemical modification for targeting desired properties. A discussion of several strategies aimed at improving hydrogen uptake in these materials is presented. These strategies include the optimization of pore size and adsorption energy by linker modification, impregnation, catenation, and the inclusion of open metal sites and lighter metals. 相似文献