Chemical environment of copper at the surface of a CuAl2 model alloy: XPS,MEIS and TEM analyses

Air‐formed oxide on a CuAl₂ model alloy is shown to be free of copper species, with copper enriching in the alloy. With thickening of the oxide by anodizing, copper enriches further to a critical concentration at which its oxidation proceeds with incorporation of Cu(II) species into the film. Such species migrate more rapidly through the film than aluminium species. Incorporation of copper species is associated with generation of oxygen gas within the film and subsequent film rupture is due to release of the gas. Reduction of Cu(II) to Cu(I) species during XPS analysis is characterized and the accelerating role of charge neutralizing is highlighted. Copyright © 2004 John Wiley & Sons, Ltd.     

Formation of Bi-Sb, Bi-Sn, and Bi-Sb-Sn Nanoclusters in Silica Xerogel Matrices from Mixed-Metal Oxide Precursors

Homogeneous mixed-metal oxides of the general formula (Bi/E/Si)O _x , where E represents a dopant element (E=Sb, Sn, or Sb/Sn), can be prepared using typical sol-gel processing techniques. Reduction of the in-situ Bi(III) and E ions by hydrogen affords nanocomposites of Bi-Sb, Bi-Sn, or Bi-Sb-Sn widely dispersed throughout the silica xerogel matrix. The materials prepared have high Bi-E metal loading of 52–60 wt. % containing Bi-E alloy nanoclusters of 12–15 nm average diameter. These results demonstrate a convenient method for the production of practical quantities of nanostructured bismuth alloy ceramic composites at high metal content.     

N,N-二甲基甲酰胺中电沉积制备镁镍储氢合金

采用恒电位沉积法, 选用适宜的添加剂和络合剂, 成功地从N,N-二甲基甲酰胺(DMF)中沉积出致密的黑色Mg-Ni储氢合金膜. 并初步探讨了其共沉积机理. XRD显示沉积层中含有非晶态Mg-Ni相和微晶态Mg相. SEM图及相应能谱图分析表明合金颗粒以团聚状态存在, 合金成分不是很均匀. AAS分析表明沉积合金中Mg的原子摩尔分数达27.3%. LAND电池测试系统测得所镀合金膜的放电比容量最高为172.4 mAh/g.     

Silica-supported PtSn alloy doped with Ga, In or, Tl: Characterization and catalytic behaviour in n-hexane dehydrogenation

Silica-supported trimetallic catalysts containing Pt, Sn and a group 13 metal (PtSnM, M=Ga, In, Tl) were prepared by consecutive impregnation steps from cis-[PtCl₂(PPh₃)₂] and chloride precursors. X-ray diffraction (XRD), transmission electron microscopy (TEM), selected-area electron diffraction (ED) and energy dispersive X-ray analysis (EDX) showed large platelet-like particles of PtSn_1−xM_x phases. PtSnGa catalyst with a Pt/(Sn+Ga) molar ratio of 1.72 showed a bimodal particle distribution and a Pt phase was identified. Differences in surface structures were also revealed by the performance of catalysts in the dehydrogenation of n-hexane. For PtSnIn and PtSnTl (Pt/(Sn+M) molar ratio of about 1) the dehydrogenation was favoured. In contrast, PtSnGa catalyst yielded hydrogenolysis products. Photoelectron spectra showed the Pt 4f_7/2 level at a binding energy of 70.0–71.8 eV in all cases. Moreover, the FT-IR spectra of chemisorbed CO on the PtSnGa showed a slight shift in the ν(CO) toward higher values with respect to the monometallic catalyst, pointing to an electronic effect in accordance with photoelectron spectroscopy.     

硅锗合金Seebeck系数影响因素的研究

作为一种洁净能源,硅锗合金的热电转换性能的研究越来越受到人们的重视.本文重点研究了不同Ge浓度的硅锗合金以及Si、Ge单晶在300～1100K温度范围内,Seebeck系数随温度的变化.并对组分相同导电类型不同、晶向不同以及结晶状态不同的样品的Seebeck系数进行了比较.在研究温度区间,Seebeck系数的绝对值大小一般在200～600μV/K之间,随温度不同连续变化.通过对比发现SiGe合金的Seebeck系数大小不仅与Ge的浓度和温度有关,其他因素对其绝对值也有影响,其中晶向最为明显,表现出了明显的各向异性.此外,材料本身的电阻率除了作为一个热电参数影响最优值外,其大小还对Seebeck系数的绝对值有影响,即掺杂济浓度对Seebeck系数的影响.     

Size-dependent ignition temperature of metallic compounds fabricated by self-propagating high-temperature synthesis

Considering the diffusion reaction at solid interfaces, the ignition temperature of compounds fabricated by self-propagating high-temperature synthesis (SHS) is modelled with the help of size-dependent activation energy. As reactant size decreases, ignition temperature also decreases. This is because of increased contact areas between the reactants and the lowered diffusion barrier, both of which must be calculated specifically for reactants in nanoscale. The model predictions and experimental results are consistent for some metallic compounds.     

Dislocation driven chromium precipitation in Fe-9Cr binary alloy: a positron lifetime study

The influence of initial heat treatment on anomalous Cr precipitation within high temperature solubility region of the Fe–9Cr alloy has been investigated using positron lifetime studies. Air-quenched samples with pre-existing dislocations exhibited a distinct annealing stage in positron lifetime between 800 and 1100?K corresponding to Cr-precipitation. During this stage, Transmission Electron Microscopy showed fine precipitates of average size 4 nm, dispersed throughout the sample and from Energy-dispersive X-ray spectroscopy (EDS) analysis they are found to be Cr-enriched. The presence of dislocations is found to be responsible for Cr precipitation.     

Corrosion inhibition of ammonium molybdate for AA6061 alloy in NaCl solution and its synergistic effect with calcium gluconate

The corrosion inhibition of ammonium heltamolybdate (AH) and calcium gluconate (CG) for AA6061 alloy in 3% NaCl solution was investigated by the electrochemical measurements. It indicates that AH inhibits the corrosion of AA6061 alloy and acts as an anodic inhibitor. Maximum inhibition efficiency reaches 74.3% at the concentration of 1 × 10^?4 mol.l^?1 AH. The results of the electrochemical studies reveal AH is physically adsorbed on the AA6061 alloy surface and the adsorption follows Langmuir isotherm. The combination of AH and CG enhances the inhibition efficiency to 95.9%. The enhanced inhibition is attributed to the promotion of AH adsorption by CG. The mixture of AH and CG is a mixed‐type inhibitor and renders the corrosion potential to more positive values. Copyright © 2011 John Wiley & Sons, Ltd.     

非晶合金条带的爆炸焊接

 报道了利用爆炸焊接技术对铁基、铁镍基非晶合金条带（厚度约25 μm）进行单层和多层爆炸焊接的结果。金相分析结果表明，条带间相互结合良好；X光衍射结果说明，焊接后的条带仍保持非晶态，即使采用表面已有部分晶化德条带进行焊接，焊接后仍转化为非晶态。这说明在焊接过程中条带表面已发生熔化，且冷却速度也可达10⁶ K/s量级。     

Microstructure and wear resistance of laser clad cobalt-based alloy multi-layer coatings

Multi-layer Co-based alloy (HMSP 2537) were deposited on Ni-based superalloy plate with a TJ-TL-T5000 type CO₂ laser. Sections of such coatings were examined to reveal their microstructure and phase composition using optical microscope, scanning electron microscope (SEM), and X-ray diffractometer (XRD). The hardness and wear resistance of the coatings were tested. The results showed that the prime phase (γ-Co dendrite) and other phases, such as CrNi, Co₇W₆, and Cr₂₃C₆ existed in the coatings. Dendrite or cellular microstructures were observed perpendicular to the interface, and coarsening microstructures were obtained as more layers deposited. Dendrite paralleling to laser scan speed was also found near the top surface of the last layer. Fine microstructures of γ-Co dendrite and lamellar eutectic in inter-dendritic regions strengthened the coatings. Microhardness and wear resistance of the coatings were much higher than that of substrate but slightly decreased with layers increased.