Microbial desulfurization of waste latex rubber with Alicyclobacillus sp.

A microbe with desulfurizing capability, Alicyclobacillus sp., was selected to recycle waste latex rubber (WLR). The growth characteristics of the microorganism and the technical conditions in the co-culture desulfurization process were studied. The desulfurization effect of Alicyclobacillus sp. on the WLR was characterized, and the mechanism for the microbial desulfurization of WLR was tentatively explored. The results showed that adding 5% (w/v) WLR into medium had little effect on the growth of Alicyclobacillus sp. The surfactant polysorbate 80 (Tween 80) had a toxic effect on Alicyclobacillus sp., but the growth of the microbe was vigorous if the proper technique was used: the mixing of WLR with Tween 80, followed by the addition of the mixture into the culture media. With the increase of desulfurization time, the swelling value of desulfurizated waste latex rubber (DWLR) increased, but the crosslink density decreased. After co-culture desulfurization for 8–10 days, a DWLR with good desulfurization effect was obtained. The mechanical properties of natural rubber (NR)/DWLR composite improved significantly over those of NR/WLR composite. XPS and FTIR results revealed that Alicyclobacillus sp. could break the crosslinked sulfur bonds and oxidize them to sulfones groups. The increase of O element content on the surface of DWLR was confirmed by water contact angle measurements. The relationship between the crosslink density and sol fraction of DWLR with different desulfurization times agreed with the Horikx equation, an indication that the microorganisms could break the crosslinked sulfur bonds on the surface of WLR, but leaving the main chains intact.     

Oscillatory electrocatalytic oxidation of methanol on an Ni(OH)2 film electrode

A film of Ni(OH)₂ deposited cathodically on a roughened nickel substrate consists of even nanoparticles, which were characterized by atomic-force microscopy (AFM). The mechanism of potential oscillations in the electrocatalytic oxidation of methanol on this film electrode in alkaline medium was studied in situ by means of Raman spectroscopy in combination with electrochemical measurements. The redox change of the nickel hydroxide film, the concentration distribution of methanol in the diffusion layer, and the oxidation products of methanol were characterized in situ by time-resolved, spatial-resolved, and potential-dependent Raman spectroscopy, respectively. Electrochemical reactions, i.e. methanol oxidation and periodic oxygen evolution, coupling with alternately predominant diffusion and convection mass transfer of methanol, account for the potential oscillations that occur during oxidation of methanol above its limiting diffusion current. This mechanism is totally different from that of methanol oxidation on platinum electrodes, for which surface steps, i.e. formation and removal of CO_ad, are essential.This work is dedicated to Professor Gyorgy Horanyi on the occasion of his 70th birthday in recognition of his numerous contributions to field of electrochemical oscillations and electrocatalysis at Ni-hydroxide electrodes.     

The chemical reactivity of a known anti-psoriasis drug. Part 1: Further insights into the products resulting from oxidative cleavage

The oxidative cleavage of the known anti-psoriasis drug 1 to give 2 has been reported previously. Due to the importance of accessing medium-sized ring containing systems via oxidative cleavage, this reaction has been revisited revealing additional information about the structure of 2. Alternative reaction products were identified when the reaction was carried out in the presence of water. The conversion of 1 to 2 has also been carried out using ruthenium tetroxide. A detailed variable temperature NMR and computational study of the restricted rotation of the N-aryl ring in 2 is presented.     

高碳烃宽温度范围燃烧机理构建及动力学模拟

发动机中燃料点火特性以及燃烧能量的释放对于发动机设计具有非常重要的作用,为了提高燃料的燃烧效率以及减少燃料在燃烧过程中污染物的排放,基于反应动力学机理对燃料燃烧过程的模拟就显得十分必要。因此需要更加深入的认识碳氢燃料的燃烧机理,探索其在燃烧过程中十分复杂的化学反应网络。为了发展能够适用于实际燃料多工况条件(宽温度范围、宽压力范围和不同当量比)燃烧的燃烧机理,基于碳氢燃料机理自动生成程序ReaxGen构建了正癸烷燃烧详细机理(包含1499个物种,5713步反应)和正十一烷燃烧详细机理(包含1843个物种,6993步反应)。详细机理主要由小分子核心机理和高碳烃类(C5以上)机理两部分组成。为了验证机理的合理性与可靠性,本文对于高碳烃燃烧新机理在点火延时时间以及物种浓度曲线进行了动力学分析,并与实验数据及国内外同类机理进行了对比,结果表明本文提出的正癸烷和正十一烷燃烧新机理在比较宽泛的温度、压力和当量比条件下都具有较高的模拟精度,为发展精确航空煤油燃烧模型提供了基础数据。同时考虑到详细机理的复杂性以及机理分析的计算量大和时耗长,本文基于误差传播的直接关系图形(Directed Relation Graph with Error Propagation,DRGEP)方法简化得到的包含709组分2793反应的正癸烷和包含820组分3115反应的正十一烷简化机理,使用DRGEP方法时所采用的数据点选自压力范围从1.0×10~5 Pa到1.0×10~6Pa,当量比范围从0.5到2.0,初始温度范围从600到1400时恒压点火的模拟结果在点火延迟时间附近区域的抽样,同时在正癸烷机理简化中选取正癸烷、O_2和N_2作为初始预选组分,正十一烷的机理简化中主要选取正十一烷、O_2和N_2作为初始预选组分,得到的简化机理在比较宽泛的条件下的预测结果与详细机理吻合很好。最后结合敏感度分析方法分析了正癸烷和正十一烷的点火延迟敏感性,考察了机理中影响点火的关键反应。结果表明:这些机理能够合理描述正癸烷和正十一烷的自点火特性,在工程计算流体力学仿真设计中有很好的应用前景。     

Degradation of electrospun SF/P(LLA-CL) blended nanofibrous scaffolds in vitro

Nanofibrous scaffolds of silk fibroin (SF) and poly(l-lactic acid-co-?-caprolactone) (P(LLA-CL)) blends fabricated via electrospinning possessed good mechanical property and biocompatibility, as demonstrated by a previous study in vitro. However, the degradation behavior of the scaffolds, which may significantly influence tissue repair and regeneration, needs further exploration. In this study, in vitro degradation of pure SF, P(LLA-CL) and SF/P(LLA-CL) blended nanofibrous scaffolds were performed in phosphate-buffered saline (PBS, pH 7.4 ± 0.1) at 37 °C for 6 months. A series of analyses and characterizations (including morphologic changes, loss weight, pH changes of PBS solutions, DSC, XRD and FTIR-ATR) were conducted to the nanofibrous scaffolds after degradation and the results showed that the pure SF nanofibrous scaffolds were not completely degradable in PBS while pure P(LLA-CL) nanofibrous scaffolds had the fastest degradation rate. Moreover, the addition of SF reduced the degradation rate of P(LLA-CL) in SF/P(LLA-CL) blended nanofibrous scaffolds. This was probably caused by the intermolecular interactions between SF and P(LLA-CL), which hindered the movement of P(LLA-CL) molecular chains.     

Nanostructure of montmorillonite barrier layers: A new insight into the mechanism of flammability reduction in polymer nanocomposites

This study describes the mechanism of flammability reduction in flame-retarded polymer matrix organo-montmorillonite reinforced nanocomposites. Morphologies of untested polymer nanocomposites and char residues formed by combustion in the mass loss calorimeter are characterized by XRD and TEM techniques. It is postulated that a combination of well-dispersed montmorillonite platelets and flame retardants in the polymer matrix provides nano-structured char formation. Initial montmorillonite dispersion in flame-retarded nanocomposites is found to be a major controlling factor on formed char nanostructures. An initially intercalated structure is invariantly converted to complete montmorillonite collapse whereas an initially exfoliated structure transforms to nano-structured chars demonstrating retained exfoliation or a new state of intercalation via incomplete collapse of montmorillonite layers. It is proposed that nano-structured char formation is the effective mechanism of flammability reduction, i.e. reduction in rate of heat release during combustion, in flame-retarded polymer nanocomposites.     

荧光光谱法研究卟啉与金属离子配位反应机理初探

本文用荧光光谱法初步研究了卟啉与金属离子配位反应机理和部分催化剂的催化机理.实验发现,在一定条件下,卟啉以一种与其主要存在形式不同的变形体H₂P^*存在,根据H₂P^*的存在和产生的条件,对卟啉与金属离子配位反应的一般条件作出了较为满意的阐述.     

Potentiodynamic deposition of Prussian blue from a solution containing single component of ferricyanide and its mechanism investigation

Potentiodynamic techniques were used for the direct electrodeposition of Prussian blue nano-clusters from an acidic solution of ferricyanide. Electrochemical, EQCM, IR, AFM, and UV/vis measurements were carried out to characterize deposited nano-sized Prussian blue and to explore the formation mechanism. Results showed that ferricyanide could partially dissociate to free ferric and cyanide ions. The driving force of this dissociation is the formation of PB and the evolution of HCN. The optimal potential window for the potentiodynamic formation of PB from an acidic solution (pH 1.6) is between –0.5 V and 0.4 V. In addition, the influence of surface adsorption of CN^- ions on the formation of PB was discussed.Dedicated to Professor W. Vielstich on the occasion of his 80th birthday.     

复合还原剂硼氢化钠/三氯化铁对亚砜的还原

硼氢化钠是一种温和、高选择性的亲核还原剂。一般它只能还原醛、酮和酰氯,而对其它功能团不起作用。因而其应用范围有一定的限制。据文献报道,某些金属卤化物能有效地提高硼氢化钠的还原性能^[1]。复合还原剂硼氢化钠/三氯化铁已应用于将β-二烷基氨基共轭烯酮还原为相应的饱和γ-氨基醇^[2]。本文研究了硼氢化钠/三氯化铁对亚砜的还原反应。