基于声发射原理监测涂层疲劳磨损的研究

采用超音速等离子喷涂设备在45^#钢基体上制备了铁基自熔剂合金涂层,通过球盘式接触疲劳试验机考察了喷涂层的疲劳磨损行为,利用声发射技术实时监测涂层的疲劳磨损过程,使用扫描电子显微镜对涂层不同疲劳磨损阶段的损伤形貌进行表征,并分析了涂层损伤机理.结果表明:转速2 000 r/min和应力水平1.848 9 GPa条件下,剥落是涂层失效的主要形式.声发射幅值和绝对能量可以反映涂层的疲劳磨损过程.涂层的疲劳磨损过程主要包括弹塑性变形、裂纹萌生、裂纹稳定存在、裂纹稳定扩展、裂纹失稳扩展5个阶段,其中裂纹稳定存在时间是影响疲劳寿命长短的关键.     

Third body modeling in fretting using the combined finite-discrete element method

A new approach was developed for modeling the effect of the third body on fretting. This was accomplished using the combined finite-discrete element method (FDEM) in which the third body is analyzed as discrete elements while the first bodies are modeled using finite elements. This approach provides a link between large scale models which treat the mass of wear debris as a single or small number of bodies and small scale models which only study a control volume. The FDEM was used to analyze the behavior of third body particles between flat sliding surfaces. When the third body mass is composed of unconnected particles, it behaves as a Newtonian fluid, but this behavior ceases when the particles are connected into platelets. The FDEM was also used to study the behavior of third body particles inside a Hertzian line contact. As the number of particles and platelet size increase the load carried by the worn slip zone grows larger in relationship to the unworn stick zone.     

TC4钛合金超高周次轴向振动疲劳试验

应用基于压电超声疲劳试验技术开发的20kHz轴向振动疲劳试验系统,完成了室温下TC4钛合金超高周疲劳试验,获得了TC4合金在107～109周次范围内的轴向振动疲劳寿命曲线(S-N曲线);运用C.Paris推导公式预测了TC4合金材料的寿命,得到各应力水平下破坏率为50％、95％、99％的安全寿命.结果表明:在疲劳循环大于107周次时,试件仍会发生疲劳断裂,疲劳强度随循环次数的增加而下降,并不存在明显的疲劳极限.TC4合金的S-N曲线在107～109周次的范围内呈连续下降型.在轴向振动超高周疲劳试验中,试件的裂纹扩展寿命只占其在50％破坏率下疲劳安全寿命的一小部分,其疲劳寿命主要由试件的裂纹萌生寿命决定.     

滚滑工况弹流反常温度场的研究

研究了弹流反常温度场的形成机理及影响因素，指出入口温升是压缩功发热和逆流剪切热所致，而出口局部低温是负压缩功吸热的结果，出口温度的再次微幅上升则是压缩功消失后剪切热作用的结果．研究结果表明，入口温升随载荷的增加而增大，随卷吸速度的增加显著升高而几乎与滑滚比无关；在高速小滑滚比工况下，接触区的最高温度有可能出现在入口位置；入口温升增加了材料在工作中经受高温的次数，对其接触疲劳寿命有不利影响；在保证润滑性能的前提下，适当减少供油量可以减小逆流，从而降低入口温升。     

一种经验型疲劳小裂纹扩展模型

金属材料疲劳寿命由裂纹萌生和裂纹扩展寿命两部分组成,其中对于萌生寿命中的小裂纹分析是精确描述裂纹萌生寿命的关键．而小裂纹在扩展过程中由于尺寸相对较小,导致传统线弹性断裂力学预测方法失效,需要对其进行改进,考虑裂纹尖端塑性区引起的残余压应力对小裂纹扩展速度的影响．本文针对此问题进行了初步分析,通过对塑性区引起的残余应力的量化,结合小裂纹门槛值特性,提出了一种经验型修正的小裂纹扩展模型,用于定量预测裂纹的萌生寿命．使用铝合金6082-T6缺口试样进行了疲劳实验,并与理论结果进行了对比,验证了所提模型的有效性．     

摩托车传动用滚子链磨损特性的研究

道路行驶磨损试验结果表明，摩托车传动用滚子链套筒和销轴零件的主要磨损形式是磨粒磨损，并伴随有疲劳磨损的特征．由微观分析和链条的磨损伸长量可知：套筒和销轴的初始表面硬度较高，有利于改善其磨损表面形貌状态和耐磨性；在磨粒磨损机制下，套筒和销轴零件的表面硬度较低，容易产生“犁切”，表面层的循环硬化现象比较明显，磨损严重；在油池润滑条件下，套筒和销轴零件的表面硬度较高，裂纹的扩展速率较快，循环软化现象也较明显，当表面硬度较低时发生循环硬化．循环软化与循环硬化是导致磨损严重的原因之一．     

一种基于材料韧性耗散分析的疲劳损伤定量新方法

依据疲劳过程中结构钢力学性能的变化规律,从反映疲劳损伤机理、对损伤过程表现敏感且便于实验测试等方面对上述材料弹性、塑性、强度和韧性等参量进行综合考察后指出,韧性是一个适合作为疲劳损伤表征的力学参量,并进一步建立了韧性随疲劳损伤演化的耗散模型。从交变载荷下材料韧性耗散规律出发,结合疲劳损伤的能耗过程分析,系统研究并提出了以韧性为基本参量的疲劳损伤变量、损伤临界值、损伤演化方程和累积损伤模型,据此建立了一种新的疲劳损伤定量方法,并在实验中得到了验证。通过与其它方法比较表明：根据韧性耗散定义损伤变量优于基于延性、强度和弹性模量变化的损伤度量方法,由此得到的累积损伤模型较Ｍｉｎｅｒ线性法则与Ｍａｎｓｏｎ双线性累积损伤法则更符合实验结果。因此,上述疲劳损伤定量方法可为现阶段工程结构的抗疲劳设计与寿命估算提供新的研究手段     

Fatigue damage behavior of a surface-mount electronic package under different cyclic applied loads

This paper studies and compares the effects of pull-pull and 3-point bending cyclic loadings on the mechanical fa- tigue damage behaviors of a solder joint in a surface-mount electronic package. The comparisons are based on experimental investigations using scanning electron microscopy （SEM） in-situ technology and nonlinear finite element modeling, respec- tively. The compared results indicate that there are different threshold levels of plastic strain for the initial damage of solder joints under two cyclic applied loads; meanwhile, fatigue crack initiation occurs at different locations, and the accumulation of equivalent plastic strain determines the trend and direction of fatigue crack propagation. In addition, simulation results of the fatigue damage process of solder joints considering a constitutive model of damage initiation criteria for ductile materials and damage evolution based on accumulating inelastic hysteresis energy are identical to the experimental results. The actual fatigue life of the solder joint is almost the same and demonstrates that the FE modeling used in this study can provide an accurate prediction of solder joint fatigue failure.     

强激光冲击铝合金改性处理研究

利用新型聚偏1.1-二氟乙烯（PVDF）压电传感器,实现了对激光引发的冲击波压力的实时测量,得到激光引发的冲击波峰压在铝中成指数型的衰减规律;观测了不同约束层材料在铝靶表面产生的激光冲击波,研究了不同约束层对冲击效果的影响;最后用激光冲击强化装置对7050-T7451航空铝合金结构材料进行了冲击强化处理,对试件激光冲击区存在的残余压应力及位错密度进行了测量。结果显示经激光冲击处理的试件表面具有极高的残余压应力,可达-200MPa以上。激光冲击处理后铝合金的位错密度得到显著的提高,疲劳寿命提高到175％～428％。这些重要结果对激光冲击改性处理技术的实际应用具有指导性作用。     

二代高温超导带材的机械特性研究进展

以 YBCO(YBa2Cu3 O7 -δ ) 为代表的二代高温超导带材因具有高临界转变温度、 高临界磁场和强载流能力,受到了国际学界高度关注, 在各个领域具有广泛的应用前景. 二代高温超导带材在绕制、 冷却和运行过程中会受到不同来源的外力作用, 且超导带材的韧性、 延展性较差, 因此其机械性能是影响安全性与设备运行可靠性的关键.本文基于二代超导带材各向异性的特点, 对超导带材轴向、 横向、 弯曲三个方向的静态机械性能及疲劳性能进行了介绍. 同时, 也对超导带材各方向机械性能的测试方法、 影响因素及机理进行了总结