LLDPE/纳米SiO_2复合材料的力学性能和光学性能研究

采用熔融共混方法制备了LLDPE 纳米SiO2 复合材料 ,并对该体系的力学性能和光学性能进行了系统研究 .结果表明 ,随着纳米SiO2 的加入 ,复合材料的弹性模量显著提高 ,冲击强度与拉伸强度呈峰形变化 ,且均在SiO2 含量为 3phr左右达到最大值 .加入少量的纳米SiO2 后 ,复合材料薄膜对长波红外线 (7～ 1 1 μm)的吸收能力较LLDPE膜有了显著提高 ,透光率略有下降但雾度提高 ,透光质量得到改善 .同时表明 ,纳米SiO2 的表面处理方法对膜的光学性能有显著影响     

Sol-gel polyimide-silica composite membrane: gas transport properties

The effect of introduction of silica particles prepared by the sol-gel technique on the gas transport properties of a polyimide film was studied. The sorption and permeation of N₂, O₂, CO₂, H₂ and CH₄ were studied and correlated with morphological changes in the polymer structure. From sorption isotherms, we observed that the composite membrane presents higher solubility coefficients than the polyimide one. The solubility coefficient ratio between the composite and the polyimide is about 1.5–2.0. The isotherms were analyzed in terms of the dual mode sorption. The Henry's coefficient and the Langmuir's affinity and saturation constants were obtained allowing to calculate the Langmuir to Henry concentration ratios as function of the gas pressure. These ratios decrease until zero within a certain pressure range as long as the Langmuir's mode is acting and they are higher for the polyimide membrane when compared with the composite one. This study was completed with calorimetric measurements during the sorption. The gas interaction energy in kJ/mol decreases within the same pressure range as previously described. The measured energies are higher for the polyimide film when compared with the composite one because the polyimide membrane presents a stronger energetic effect caused by a higher Langmuir's contribution. From permeation studies at 3.15⁵ Pa, the composite membrane showed higher permeability coefficients and permselectivities than the polyimide one. All these results were explained, taking into account the difference on the imidization degree of both membranes and the morphological changes which may be induced by the silica nodules in the organic/inorganic interphases.     

互通多孔碳/二氧化锰纳米复合材料的原位水热合成及电化学性能

以互通多孔碳（IPC）为载体，水热条件下在碳表面原位反应生成纳米结构的二氧化锰（MnO₂），制备互通多孔碳/二氧化锰纳米（IPC/MnO₂）复合电极材料. 采用扫描电镜（SEM），透射电镜（TEM），X射线衍射（XRD），热重分析（TGA）对其结构进行表征；采用循环伏安法、恒流充放电和交流阻抗对其电化学性能进行研究. 结果表明：生成的MnO₂均匀地负载在碳的表面，形成多层次结构，并且随着温度的升高IPC表面负载的MnO₂由纳米颗粒变为纳米片状结构；MnO₂纳米片具有典型的K-Birnessite 型晶体结构；复合物中MnO₂的含量约为34%（w）. 在100 ℃制备的IPC/MnO₂复合材料在三电极系统中最高比电容达到了411 F·g^-1；随着反应温度的升高,比容量先增长后基本保持不变. 以IPC/MnO₂为正极，活性炭（AC）为负极，1 mol·L^-1 Na₂SO₄溶液为电解液组装成IPC/MnO₂//AC 混合超级电容器，发现IPC/MnO₂电极的电容器其电位窗口从1 V扩展到1.8 V，容量可达86F·g^-1，且表现出良好的电容特性和大电流放电性能.     

Determination of degree of conversion as a function of depth of a photo-initiated dental restoration composite—III application to commercial Prodigy Condensable™

In this third work, we evaluated the degree of conversion (DC) versus depth of dental filling composite named Prodigy Condensable™ using infrared spectroscopy. Confirming previous results, there was a gradual reduction of DC with increasing depth but the composite exhibited extreme values of DC, an upper value (45.9%) on the surface and a lower one (6.1%) at a depth of 5 mm. The composite presented the worst performance among materials studied. The composite formulation was 80% of inorganic fillers and BisfenolA/dimethacrylate (BisGMA) (18%)/triethyleneglycoldimethacrylate (TEGDMA) (2.0%) as monomers. As stated before, type/ratio/viscosity of monomers and type, amount, size and size distribution of fillers all together had an important role in the cure reaction contributing to the final performance of the composite.     

Preparation and characterization of silica—polyimide composite membranes coated on porous tubes for CO2 separation

Silica-polyimide microcomposite membranes were prepared on γ-alumina-coated α-alumina support tubes, and their gas permeation properties were evaluated with He, N₂ and CO₂. Smoothing of the substrate surface and hybridization of silica and polyamic acid were both effective to form defect-free thin composite membranes. The CO₂ permeance of a membrane with a silica content of 68 wt% was one order of magnitude higher than that of a polyimide membrane having the same thickness. The permselectivity of CO₂ to N₂ was 30 at 30°C and 13 at 100°C. Contributions of the silica and polyimide phases to permeance of the composite membrane were analyzed with a two-phase permeation model. The effective thickness of the rate-controlling polyimide phase was less than one-tenth of the total thickness of the silica-polyimide membrane.     

酞菁氧钛/卟啉氧钒复合体系光导性能的协同增强效应

在酞菁氧钛（TiOPc)／卟啉氧钒（VOTPP）复合光生材料中发现了光敏性的非线性增强现象，对复合体系的电子跃迁光谱和X射线衍射图的研究结果表明，在基态下两种材料之间没有明显相互作用，光致放电研究说明，该现象来自光激发状态下复合体系中的隙间态跃迁对光导的贡献，XPS测试结果表明酞菁氧钛与卟啉氧钒分子之间存在着定向的部分电荷转移，光致激发状态下的电荷转移是协同增强效应的起因，这种协同增强效应为利用弱的电子给体与弱的受体复合体系设计新型光导材料与器件提供了新方法。     

Coaxial electrospinning core-shell fibers for self-healing scratch on coatings

Polystyrene (PS) fibers with core-shell structure were prepared by coaxial electrostatic spinning using liquid epoxy or curing agent as the core and PS solution as the shell. Scratch self-healing coatings were realized by using the healant-loaded core-shell fibers in the matrix.     

SDS胶束对孔雀绿褪色反应的影响

研究了十二烷基硫酸钠（SDS）表而活性剂胶束和预胶束对孔雀绿褪色可逆反应的影响，建立了1－1型可逆反应的胶束催化模型和预胶束催化模型，获得了胶束相中正逆反应的速率常数和预胶束的平均聚集数．结果表明，SDS胶束和预胶束对正反应有禁阻作用，而对逆反应有催化作用．     

染料配体脲醛树脂-二氧化锆复合微球的制备及对牛血清白蛋白的萃取性能

采用溶胶-凝胶法制备无孔脲醛树脂-二氧化锆复合微球,在碳酸盐缓冲溶液中,利用微球表面的酰胺键与三嗪染料-活性艳蓝X-BR分子中三嗪环上的活泼氯反应,将染料键合到微球表面,以牛血清白蛋白(BSA)为样品,考察了不同条件下,该萃取剂对BSA的萃取能力。结果表明,该萃取剂对BSA的饱和萃取量达到30.3 mg.g-1,同时萃取的蛋白易于洗脱,1.0 mol.L-1氰化钾的洗脱率达到93.5%。     

肝素化壳聚糖季铵盐／壳聚糖复合膜抗凝血性能的研究

以壳聚糖季铵盐，壳聚糖为基本原材料，选用戊二醛为交剂剂及固定剂，制备一种物理机械性能较优的抗凝血材料。探讨了戊二醛及肝素钠两者用量对肝素化程度及血液生的影响。