Study of Manganese Promoter on a Precipitated Iron-Based Catalyst for Fischer-Tropsch Synthesis

The effects of Manganese(Mn)incorporation on a precipitated iron-based Fischer-Tropsch synthesis(FTS)catalyst were investigated using N_2 physical adsorption,air differential thermal analysis (DTA),H_2 temperature-programmed reduction(TPR),and M(?)ssbauer spectroscopy.The FTS perfor- mances of the catalysts were tested in a slurry phase reactor.The characterization results indicated that Mn increased the surface area of the catalyst,and improved the dispersion ofα-Fe_2O_3 and reduced its crystallite size as a result of the high dispersion effect of Mn and the Fe-Mn interaction.The Fe-Mn inter- action also suppressed the reduction ofα-Fe_2O_3 to Fe_3O_4,stabilized the FeO phase,and(or)decreased the carburization degree of the catalysts in the H_2 and syngas reduction processes.In addition,incorporated Mn decreased the initial catalyst activity,but improved the catalyst stability because Mn restrained the reoxidation of iron carbides to Fe_3O_4,and improved further carburization of the catalysts.Manganese suppressed the formation of CH_4 and increased the selectivity to light olefins(C_(2-4)~=),but it had little effect on the selectivities to heavy(C_(5 )) hydrocarbons.All these results indicated that the strong Fe-Mn interaction suppressed the chemisorptive effect of the Mn as an electronic promoter,to some extent,in the precipitated iron-manganese catalyst system.     

包覆Y(OH)3的球形Ni(OH)2的电化学性能

利用软嵌式粉末电极技术研究了Y(OH)3包覆对球形Ni(OH)2电化学性能的影响. 循环伏安结果表明, 在球形Ni(OH)2的氧化过程中存在Ni(Ⅲ)和Ni(Ⅳ)的两步氧化反应, 产生的Ni(Ⅳ)不稳定, 能分解产生NiOOH和氧气, 所以可将Ni(Ⅲ)→Ni(Ⅳ)看作副反应. Y(OH)3包覆层对Ni(OH)2氧化过程后期的副反应, 特别是Ni(Ⅲ)→Ni(Ⅳ)具有较好的抑制作用. 由包覆后的Ni(OH)2制成的模拟电池表现出很好的高温性能, 在1C充放电条件下, 当Y的摩尔分数为1.61%时, 在60 ℃时所对应的容量保持率可达到25 ℃的92.7％; 当Y的摩尔分数仅为0.55 %时, 在60 ℃时所对应的质量比容量也可达到241.3 mA·h/g.     

现场表面拉曼光谱研究Fe-Mo合金诱导共沉积

现场表面拉曼光谱结果显示，在0．2mol·L-1Na2MoO4,pH＝4．0的溶液中，电位正于0．5V（vsSCE）时只观察到多钼酸盐的拉曼峰（940、880和450cm-1）．负于-0．5V时，出现中心位于730cm-1的宽峰．同时电极表面有蓝色膜生成．表明混合氧化态（MO（Ⅳ），MO（Ⅴ））氧化膜的形成．730cm-1的峰在-1．9V时仍然存在，说明氧化膜没有被进一步还原．在钼酸钠溶液中同时含有0．1mol·L-1FeSO4和0．2mol·L-1柠檬酸时，中间态氧化膜的拉曼峰的中心移到740cm-1．且峰强度随着电位从-1．3V负移到-1．9V而逐渐减弱并最终消失．电极表面沉积层呈银白色，说明由于Fe2 的存在，钼的中间态氧化膜的结构发生了变化，能够被进一步还原形成Fe－Mo合金，表现出诱导共沉积的特征．     

电化学合成聚苯胺粉末电极的电化学行为研究

我们曾用慢速动电位扫描法研究化学合成聚苯胺粉末的电化学行为.本文对恒电位电解合成聚苯胺粉末进行了研究.用这种方法制备的粉末由于合成溶液中不含氧化剂因而纯度高.本文还报导了这种聚苯胺粉末电极的交流阻抗测量结果.交流阻抗法曾用于聚苯胺膜的电导和化学合成聚吡咯的电阻测定. 所用盐酸、氟硼酸、硅氟酸、苯胺均为分析纯;苯胺经常压蒸馏提纯;硫酸为超纯;磷酸为分析纯;高氯酸为优级纯.溶液皆用两次蒸馏水配制.     

5—（4‘—溴—2’—羧基苯偶氮）罗丹宁与铜（Ⅱ）的显色反应及其应用

本报道了新显色剂５－（４’－溴－２’－羧基苯偶氮）罗丹宁的合成及在水溶液中的离解常数Ｋ１和Ｋ２，研究了该显色剂与铜（Ⅱ）的显色反应，在弱酸性时，试剂与铜（Ⅱ）形成摩尔比２：１的络合物，摩尔吸光系数为８．９×１０＾４Ｌ．ｍｏｌ＾－１．ｃｍ＾－１。当铜的浓度在０～２．７ｍｇ／Ｌ的范围内符合比耳定律。用分光光度法测定了合金中铜的含量。     

Enhanced Acid/Base Catalysis in High Temperature Liquid Water

High temperature liquid water (HTLW), as an environmentally benign medium, has drawn increasing attention for organic chemical reactions and biomass conversion1-3. HTLW has a strong tendency to ionize and can act as an acid and/or base catalyst. In addition, HTLW can dissolve organic compounds to some extent allowing for a homogenous reaction within an aqueous phase. Extensive researches4-10 have been pursued on acid/base-catalysis reactions in HTLW without addition of acid or base. Howe…     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33,用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体.采用这些固溶体作载体,以Fe2O3为活性组分,用浸渍法制备了一系列催化剂.BET结果显示,将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积.TPR结果显示,载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能.XRD结果表明,Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况,老化前后催化剂的晶相结构基本无明显变化.特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时,Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

注入Y离子对Ni3Al合金高温氧化行为的影响

以40 KeV的能量和3×1017 /cm2的剂量在Ni3Al合金中注入Y离子, 利用热重分析、 X射线衍射、扫描电镜、能谱分析和划痕分析等技术研究了离子注入对其900 ℃恒温氧化行为的影响. 结果表明 注入Y离子不仅改变了合金的氧化动力学, 而且改变了其氧化机理. 注入Y离子后合金氧化产物中的NiO含量大为增加, 从而降低了合金的抗氧化性能. 但Y离子的注入使NiO晶粒细化, 增强了氧化膜的塑性和粘附性.     

高电导率的a—SiHY合金的低温电导特性

用射央求地在硅单晶衬底上沉积出电导率高达６０Ｓ／ｃｍ的ａ－ＳｉＨＹ合金薄膜。在２０－３００Ｋ，对于钇含量高的样品，其电导仍是热激活的。ｌｇσ与１／Ｔ的关系曲线能够被拟合成斜率不同的两条直线，直线的斜率和两直线间拐点所地 温度依赖于膜中钇的含量。但对钇含量低的薄膜，电导对温度的依赖关系度为σ∝ｅｘｐ（－１／Ｔ＾１／４）。结果表明，这些钇含量不同的样品在没的温度范围内具有不同的导电机制。     

配位-沉淀法制备Ni(OH)2和NiO超微粉

本工作采用配位 -沉淀法成功的制备了薄片形氢氧化镍和氧化镍超微粉末 ,通过 XRD、TG-DTA、IR及 TEM等实验手段对超微粉的组成结构进行分析表征。