偶联剂对玻璃纤维/环氧树脂基复合材料介电性能的影响

偶联剂对玻璃纤维／环氧树脂基复合材料介电性能的影响陈平刘胜平张明艳（哈尔滨理工大学电工材料系哈尔滨１５００４０）关键词环氧树脂基复合材料，介电性能，偶联剂，浸润性玻璃纤维／环氧树脂基复合材料（ＧＦＲＰ）具有优异的电气和力学性能．然而孔隙的存在强烈地...     

双端正离子活性链的研究——α,ω—二胺基聚丁二醇-聚酯-聚丁二醇三嵌段低聚物的合成

<正> 本实验室前项工作曾证明用脂肪二酰氯与高氯酸银引发四氢呋喃(THF)在0—50℃下聚合可形成没有链终止和链转移反应的活性聚合链.为了减少聚丁二醇醚结晶趋势,又制备了双端活性的THF-环氧丙烷无规共聚醚链.本文则通过THF的开环聚合,将一个非“活性”的聚酯转变成为双端活性链,合成了伯胺端基聚丁二醇-聚酯-聚丁二醇遥爪低聚物,并用以增韧环氧树脂.     

Porous epoxy thermosets obtained by a reaction-induced process and their characterizations

A novel reaction-induced method with the aid of solvent for porous thermosetting epoxy was first carried out. Investigations of pore structure using scanning electron microscope （SEM） showed that porous epoxy networks with average pore size ranging from 3 to 20 μm were obtained. The pore structure generated by this method can be tailored by changing the solvent content.     

PU/EP互穿网络聚合物的协同效应

本文以光固化型的聚醚氨酯（PU）与环氧树脂（EP）为体系,由不同的组成比制备了一系列PU／EP的IPN材料,经力学性能测试,均显示正协同效应,且协同效应的大小与聚合物网络的互穿程度有关,而PU／EP交联网络结构的材料只显PU／EP的加和性而不显协同效应,从而进一步证明IPN的协同效应源于IPN的网络互锁环连的结构,并对其结构所产生的协同效应的机理进行了探讨。     

聚苯基磷酸酯(PPP)的合成及其阻燃机制

阻燃剂;环氧树脂;聚苯基磷酸酯(PPP)的合成及其阻燃机制     

INVESTIGATION ON STABILITY OF PZT/EPOXY PIEZOCOMPOSITE WITH PRESSURE AND TEMPERATURE

With the universal test machine and temperature test chamber, the effect of pressure and temperature on the behavior of 1-3 and 1-3-2 piezocomposites prepared with PZT/epoxy in our lab has been investigated through electrical impedance and dielectric analysis. The permittivity, resonant frequency and dielectric loss of the composites have been measured under vertical stress and temperature, and the variety of the material properties under pressure and temperature could also be obtained. The pressure and temperature stability of the composites have been assessed through experiments. The data of these two types of composites indicated that the stability of 1-342 composite with pressure was better than that of 1-3 composite, and two composites have almost the same dielectric stability with temperature. However, 1-3-2 composite showed slower frequency variation than 1-3 composite.     

环氧树脂-聚醚-三乙烯四胺嵌段聚合物的表面活性研究

本文对含有环氧树脂分子链段、聚醚链段及三乙烯四胺链段的系列多嵌段聚合物（TETA-DGEPG-EPON828、TETA-DGEPG-EPON834及TETA-DGEPG-EPON1001加成物）进行了合成与表征。其HLB的估算值分别为16.6、15.8、13.0;浊点分别为91.0℃、89.0℃、81.0℃,它们能将水溶液表面张力从74mN•m-1降低到36.4~39.4mN•m-1。通过其理化性能的研究,结果表明TETA-DGEPG-EPON834具有优良的水溶性和良好的表面活性。选用它作为相反转乳化剂,可制备出稳定的纳米级的CARDURA E-10封端的EPON828-TETA加成物的水性环氧固化剂胺基分散体乳液。     

混合条件对环氧有机土纳米复合材料插层剥离行为及性能的影响

采用X 射线衍射仪、透射电镜 (TEM )研究了混合条件 ,即混合温度和时间 ,对环氧 /16 烷基胺有机蒙脱土体系在固化前的混合物以及加入固化剂、促进剂固化后有机土的插层与剥离行为的影响 .同时采用拉伸试验机、冲击试验机和热机械分析仪测定了插层与剥离型纳米复合材料的物理力学性能 .从X 射线衍射看出 ,有机土很容易在混合过程被环氧所插层 .混合物经固化后可以形成插层型或剥离型纳米复合材料 .存在一个混合温度 时间 插层剥离转变的 3 T图 .只有在一定的混合条件的区域内才能形成剥离型纳米复合材料 .剥离型比插层型纳米复合材料具有较高的力学性能     

粉末涂料的改性研究

简述了粉末涂料改性的研究进展。重点介绍了环氧树脂在丙烯酸树脂 /环氧树脂混合型粉末涂料中的作用 ;无封端剂的聚氨酯粉末涂料交联和 1 ,4-环己烷二甲醇酯二苯甲酸酯作为粉末涂料改性剂的研究进展     

环氧树脂水基分散体系的相反转乳化

以聚乙二醇－邻苯二甲酸酐－环氧树脂Ｅ－４４多元嵌段共聚体为乳化剂,将环氧树脂Ｅ－４乳化成水包油的稳定水基乳液。用乳液体系电导率和粘度的变化表征了相反转乳化过程。研究了乳化剂浓度、三元多嵌段共聚体中亲水嵌段分子量和乳化温度对相反转乳化过程的影响。实验结果表明,体系在较高乳化剂浓度（９．１％）下为完全相反转,在低乳化剂浓度（４．１％）下为不完全相反转。相反转时水与环氧树脂Ｅ－４４的重量比值随乳化剂浓度