Electrospinning of nylon-6,6 solutions into nanofibers: Rheology and morphology relationships

The relationship between the rheological properties of nylon-6,6 solutions and the morphology of their electrospun nanofibers was established. The viscosity of nylon-6,6 in formic acid(90%) was measured in the concentration range of 5 wt%-25 wt% using a programmable viscometer. Electrospinning of nylon-6,6 solutions was carried out under controlled parameters. The chemical structure, morphology and thermal properties of the obtained nanofibers were investigated using Fourier transform infrared spectroscopy(FTIR), scanning electron microscopy(SEM) and differential scanning calorimetry(DSC), respectively. Entanglement concentration(ce) was found to be 15 wt% and a power law relationship between specific viscosity and solution concentration was observed with exponents of 2.0 and 3.3 for semi-dilute unentangled(c ce) and semi-dilute entangled(c ce) regimes, respectively. The diameter and uniformity of the nanofibers were found to be dependent on the viscosity. Moreover, the average diameter of electrospun nanofibers was found to be dependent on zero shear rate viscosity and normalized concentration(c/ce) in a power law relationship with exponents of 0.298 and 0.816, respectively. For nylon-6,6 solutions, the entanglement concentration(ce = 15 wt%) provides the threshold viscosity required for the formation of a stable polymeric jet during electrospinning and producing uniform beadless fibers. For concentrations less than ce, beaded fibers with some irregularities are formed. DSC analysis showed an increase in crystallinity of all electrospun samples compared to original polymer. Furthermore, Based on FTIR spectroscopy, α phase is dominant in electrospun nanofibers and minor amount of β and γ phases is also available.     

Microstructure characterization of short-chain branching polyethylene with differential scanning calorimetry and successive selfnucleation/annealing thermal fractionation

A series of the copolymers of ethylene with 1-hexene(M1–M9) synthesized by metallocene catalyst Et[Ind]2ZrCl2/MAO was studied by differential scanning calorimetry and successive self-nucleation and annealing(SSA) thermal fractionation. The distribution of methylene sequence length(MSL) in the different copolymers was determined using the SSA method. The comonomer contents of samples M4 and M5 are 2.04 mol% and 2.78 mol%, respectively. Both M4 and M5 have low comonomer content and their MSL distribution profiles exhibit a monotonous increase trend with their MSL. The longest MSL of M5 is 167, and its corresponding molar percent is 43.95%, which is higher than that of M4. Moreover, the melting temperature(Tm) of M5 is also higher than that of M4. The comonomer contents of samples M7, M8, and M9 are 8.73 mol%, 14.18 mol% and 15.05 mol%, respectively. M7, M8, and M9 have high comonomer contents, and their MSL distribution profiles display unimodality. M7 has a lower peak value of 33 and a narrow MSL distribution, resulting in a Tm lower than that of M8 and M9. The MSL and its distribution are also key points that influence the melting behavior of copolymers. Sometimes, MSL and its distribution of copolymers have a greater impact on it than the total comonomer contents, which is different from traditional views.     

骨中铊的微波消解ICP/AES标准加入测定法

建立骨骼的微波消解和金属毒物铊的ICP/AES标准加入分析方法。取0.2g骨粉于聚四氟乙烯消解管中,加入3.0mL浓硝酸及0.5mL双氧水,进行微波消解。结束后,用2%硝酸定容至10.0mL。根据标准加入法进行ICP-AES定量分析。方法的回收率为99.4%,检出限为5.1ng/g,线性范围为5~500 ng/mL。该方法操作简便,回收率高,检出限低,线性范围宽,可多元素同时测定,结果可靠。     

纳米复合材料CdS/TiO2制备与不同模式光催化降解多种染料

采用化学水浴沉淀法再结合溶胶-凝胶和程序升温溶剂热两步法制备了一系列不同比例的CdS/TiO2。通过XRD、XPS、SEM、UV-Vis/DRS等手段对所合成纳米复合材料的组成、结构和形貌等进行了表征。结果表明,该系列CdS/TiO2为锐钛矿TiO2和六方相CdS的混合晶相,其在可见光有较强吸收,并且随着复合材料中TiO2比例的增加,BET值明显增大。另外,所合成CdS/TiO2呈圆球形,颗粒比较均匀。紫外光催化降解甲基橙的实验结果表明,摩尔比为1:4的CdS/TiO2的活性明显高于CdS、P25以及其它不     

UV/Fe(Ⅲ)-富马酸盐体系降解对硝基苯酚

研究了在紫外光(UV)照射下,Fe(Ⅲ)-富马酸盐体系对p-硝基苯酚(PNP)的光降解反应,考察了溶液pH、Fe(Ⅲ)、富马酸盐和PNP的初始浓度对PNP降解率的影响。结果表明,UV/Fe(Ⅲ)-富马酸盐体系对PNP有光降解作用,相比于只含Fe(Ⅲ)或者富马酸盐体系,同时加入Fe(Ⅲ)与富马酸盐构成的体系在降解PNP方面有协同作用。在pH 3.0~6.0范围内,PNP的降解率随着pH和PNP初始浓度的增大而降低,而随着Fe(Ⅲ)和富马酸盐的初始浓度的增大而增大。氯仿猝灭法证实,该体系在降解PNP反应过程中产生了超氧负离子自由基;采用荧光法和异丙醇猝灭法证实了该体系在反应过程中产生了羟基自由基,同时证实了羟基自由基为PNP光降解反应的主要反应物质。     

色谱-串联质谱法测定双氧水工作液中的降解物

建立了超高效液相色谱-串联质谱(UPLC-MS/MS)测定双氧水工作液中降解物的分析方法。样品用乙腈溶解后,采用ACCHROM C18(150 mm×4.6 mm,5μm)色谱柱,0.1%甲酸水溶液-乙腈为流动相体系,梯度洗脱,流速0.3 m L/min,柱温30℃,紫外检测波长254 nm;质谱采用电离子喷雾正离子模式检测。结果表明,双氧水工作液中有4种明显的降解物,采用面积归一法计算该4种降解物含量占降解物总量的80%以上;其它一些含量较低的降解物也能定性分析出。实验还采用了气相色谱-串联质谱法(GC-MS/MS)分析双氧水工作液,两种分析方法的结果能相互印证和互补,表明用色谱-串联质谱法能准确、全面地测定双氧水工作液中降解物,能为蒽醌法生产双氧水的企业对工作液中降解物的抑制和脱除提供参考。     

原子荧光法测定茶叶中的硒含量

采用原子荧光法测定茶叶中的硒含量,对样品消解温度及仪器条件进行了优化。还原剂为1.0%硼氢化钾–0.5%氢氧化钾溶液,载流液为3%盐酸溶液。在优化条件下,硒的质量浓度在0~20 ng/mL范围内与荧光强度呈良好的线性关系,相关系数r=0.999,检出限为0.8 ng/mL。该法的加标回收率为88.08%~101.39%,测定结果的相对标准偏差为2.03%~4.84%(n=6)。该方法实际操作性强,准确度高,适用于日常检验工作中对批量茶叶中硒含量的测定。     

热抽取法测定钴块中氢含量

研究了钴块中氢含量的测定方法。采用石英坩埚加载样品,热抽取法进行测定。不加任何助熔剂,分析功率为100%,匹配的分析时间为110 s,比较水平设定为0.1%。在选定的参数下,样品能在完全熔融状态下释放出全部氢。方法加标回收率为80%~119%,测定结果的相对标准偏差小于15%(n=6),检出限为0.5μg/g。热抽取法的精密度优于熔融法的精密度,满足微量气体分析的要求。     

共振散射法测定安乃近含量

在pH=5.0的B-R缓冲溶液中,Fe(Ⅲ)与邻菲啰啉反应生成无色配合物,从而使得体系在374nm波长处产生1个较强的共振散射峰。加入安乃近(或4-甲氨基安替比林)后,其将Fe(Ⅲ)还原成Fe(Ⅱ),而生成一种橙红色配合物,使得体系在374nm(或373nm)波长处的共振散射信号减弱。在最佳实验条件下,当安乃近浓度在0.634~15.2μg/mL范围内,体系的共振散射信号△I与安乃近的浓度之间有较好的线性关系,检出限为5.75ng/mL。该方法可直接用于测定安乃近含量,回收率为100.4%~103.4%。     

火焰原子吸收法测定中药草珊瑚叶中五种金属元素的含量

目的运用火焰原子吸收光谱法测定中药草珊瑚叶中的Fe、Zn、Mg、Ca、Cu 5种金属元素的含量。方法用浓HNO3-HCl O4消解样品,采用标准曲线法测定其5种金属元素含量。结果所测的样品中含有丰富的人体必需微量元素。方法回收率在99.35%-103.30%之间,样品相对偏差小于5%。结论该法简单、准确,结果令人满意。