Magnetic properties of La-Co substituted M-type strontium hexaferrites prepared by polymerizable complex method

Magnetic properties of La-Co substituted M-type strontium hexaferrites were studied. The samples were prepared by polymerizable complex method. Crystal structure of samples has been investigated by powder X-ray diffraction (XRD). Single-phase M-type strontium hexaferrites with chemical composition of Sr_1.05−xLa_xFe_12−xCo_xO₁₉ (x=0-0.4) were formed by heating at 1173 K for 24 h in air. Magnetic properties were discussed by measurements of M-H curves with vibrating sample magnetometer (VSM). La-Co substituted M-type strontium hexaferrites prepared by polymerizable complex method showed typical magnetic hysteresis of hard ferrite. The coercive force increased significantly by La-Co substitution with polymerizable complex method. Maximum coercive force achieved in this study is 8.0 kOe (640 kA/m). Scanning electron microscopy revealed that the prepared ferrite particles have plate-like shape of diameter range between 20 and 500 nm.     

Alkaline Earth–Olefin Complexes with Secondary Interactions

Strontium and calcium (alkaline earth: Ae) olefin complexes stabilised by secondary Ae???F?C and β‐agostic Ae???H?Si interactions are presented. Olefin coordination onto the alkaline earths is plain in the solid state, and it is thermodynamically favoured over the coordination of THF. The existence of the Ae???olefin interactions is corroborated by solution NMR data and DFT computations. The coordination mode of the olefin varies with steric effects and, if enforced, olefin dissociation can be compensated by the other non‐covalent interactions, as supported by DFT computations.     

Unusual Behavior of Nanocrystalline Strontium Oxide Toward Hydrogen Sulfide

The thermodynamically favored reaction of solid strontium oxide with gaseous hydrogen sulfide is kinetically enhanced to a large degree by the use of higher surface area nanocrystalline SrO in the form of brush-like collections of metal oxide fibers. An unusual feature is that the reaction SrO + H₂S SrS + H₂O proceeds stoichiometrically at room temperature, but at higher temperatures the reaction efficiency goes down, apparently due to rapid temperature induced crystal growth of the nanocrystalline SrO. The samples studied vary in crystallite size from 20 to 27nm, while average particle size (nanocrystal aggregates) varies in the following order; aerogel prepared SrO (100nm) 相似文献   

Cerium effect on the phase structure, phase stability and redox properties of Ce-doped strontium ferrates

Nanostructured perovskite-type Sr_1−aCe_aFeO_3−x, (0?a<0.15) powders have been prepared by citrate-nitrate smoldering auto-combustion. Their phase structure and stability, surface and morphological properties, reduction behavior and interaction with oxygen have been investigated by X-ray Powder Diffraction combined with Rietveld Analysis, ⁵⁷Fe Mössbauer and X-ray Photoelectron Spectroscopies, N₂-adsorption method, Temperature Programmed Reduction and Oxidation experiments. Our results reveal that citrate-nitrate auto-combustion method is effective in obtaining single phase Sr_1−aCe_aFeO_3−x. The Sr_1−aCe_aFeO_3−x structure is cubic only for a?0.06, while for a<0.06 remains tetragonal. Moreover, for a?0.06 after semi-reductive treatment under inert gas, an expanded cubic phase is obtained instead of the brownmillerite-type structure, which is known to have ordered vacancies. Stabilization of octahedral Fe³⁺ by cerium doping appears to be the main factor in determining the structural properties of Sr_1−aCe_aFeO_3−x. The highest oxygen consumption for Ce-doped SrFeO₃ occurs for a=0.06. Preliminary impedance measurements show that Sr_0.94Ce_0.06FeO_3−x has the lowest area-specific resistance.     

<Emphasis Type="Italic">In Situ</Emphasis> Synthesis of Field-responsive Nanocrystalline BaTiO<Subscript>3</Subscript> Particles Modified with Functional Organics

Nanocrystalline BaTiO₃ particles modified with polarizable ligands were synthesized through hydrolysis of modified metal–organics below 100°C. BaTiO₃ precursor was synthesized from barium metal, titanium isopropoxide and polarizable ligands in a mixture of ethanol and 2-ethoxyethanol. The modified Ba–Ti complex alkoxide was hydrolyzed yielding BaTiO₃ particles modified with organics. The crystallinty of nanometer-sized particles was dependent upon the hydrolysis conditions, and increased with increasing water amount and time. The nanocrystalline particles were identified to be BaTiO₃ by X-ray diffraction (XRD) and electron diffraction. A fluid consisting of modified BaTiO₃ particles and silicone oil revealed a typical electrorheological (ER) behavior on applying DC field. The ER behavior was found to depend upon the kind of ligand. 4-Fluorobenzyloxy modifier revealed the highest yield stress in the ER measurement among 4-substitued benzyloxy ligands examined.     

Time-Resolved Vacuum Ultraviolet Spectroscopy of Er<Superscript>3+</Superscript> Ions in the SrF<Subscript>2</Subscript> Crystal

The photoluminescence and photoexcitation spectra as well as the luminescence decay kinetics of Er³⁺ ions in the visible ultraviolet and vacuum ultraviolet (VUV) regions have been studied by the method of low-temperature, time-resolved VUV-spectroscopy on excitation by synchrotron radiation. In the VUV spectral region of the luminescence of SrF₂:1% Er³⁺, the 146.5-nm band with a time of decay of less than 0.6 nsec was revealed together with the well-known emission band at 164.3 nm (decay constant in the microsecond range). Its possible nature is discussed. The specific features of the formation of photoexcitation spectra of the f-f and f-d transitions in the Er³⁺ ion are considered. Competition between the processes of excitation of f-f and d-f luminescence has been revealed. It manifests itself in the inverse relationship of their photoexcitation spectra in a range of energies of incident photons that are close to the position of the 4fⁿ⁻¹5d configuration levels. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 72, No. 4, pp. 519–523, July–August, 2005.     

Coplanar Phase Shifters Based on Ferroelectric Thin Films

Barium strontium titanate (Ba_0.6Sr_0.4TiO₃, short for BST) thin films were prepared by RF-magnetron sputtering. The dielectric tunability, loss tangent, remanent polarization (2Pr) and coercive electric field (Ec) of the BST films are respectively 29.5%, 0.013, 2.29 μC/cm² and 22.27 kV/cm at 1 kHz and 20 V. The designed coplanar waveguide (CPW) phase shifter consists of 56 same sections. It is shown that the fabricated lines of electrodes are smooth and the widths at the tip of bottom electrodes are about 5 μm. At the central frequency of 28 GHz and a bias voltage of 20 V, the figure of merit is approximately 13°/dB.     

Preparation and characterization of titania based nanowires

A new method for preparation of titania nanowires with diameter around 10 nm and length up to 2–3 μm is described. The precursor was prepared from sodium titanate by adding ethylene glycole (EG) and heating at temperature of 198°C for 6 h under reflux. The sodium titanate glycolate formed by this way aggregated into 1D nanostructures and was subsequently transformed into titania glycolate during a chemical treatment with 98% sulfuric acid. Titania nanowires with variable amount of anatase and rutile were prepared by heating to temperatures in the range 350–1000°C. The precursor as well as titania based samples were characterized by X-ray diffraction, Infrared spectroscopy, Scanning electron microscopy, High resolution transmission microscopy, Thermogravimetry, Differential thermal analysis, Evolved gas analysis and Emanation thermal analysis. The nitrogen adsorption/desorption was used for surface area and porosity determination. The photoactivity of the prepared titania samples was assessed by the photocatalytic decomposition of 4-chlorophenol in an aqueous slurry under UV irradiation of 365 nm wavelength.     

Optical and Electrical Properties of Ferroelectric SBN Thin Films Prepared by Sol-Gel Process

Strontium barium niobate thin films were prepared by sol-gel method on various substrates using an improved process, two-step heating process. The two-step heating process applies an additive heat-treatment before crystallization for enhancement of the densification and the nucleation of films. Also, highly c-axis oriented SBN thin films with various compositions were obtained on MgO(100) and Pt(100)/MgO(100) substrates. Their optical and electrical properties such as optical propagation loss, refractive index, P-E hysteresis, and dielectric constant, were characterized as a function of the film composition.