采用交替沉积磁控溅射工艺制备了超薄多层的FeCoB SiO2 磁性纳米颗粒膜 .利用x射线衍射仪、扫描探针显微镜、透射电子显微镜分析了薄膜的微结构和形貌特征 .采用振动样品磁强计、四探针法、微波矢量分析仪及谐振腔法测量薄膜试样的磁电性能和微波复磁导率 .重点对SiO2 介质相含量、薄膜微结构对电磁性能产生重要影响的机理做了分析和探讨 .结果表明 :这类FeCoB SiO2 磁性纳米颗粒膜具有良好的软磁性能和高频电磁性能 ,2GHz时的磁导率 μ′高于 70 ,可以应用于高频微磁器件或微波吸收材料的设计     

红光激发下掺Ho3+氟化物薄膜的上转换发光

利用激光脉冲沉淀法制备了稀土Ho~(3 )掺杂的氟化物薄膜。观测到处于薄膜中的Ho~(3 )离子在632.8nm红光激发下的上转换发射。这些上转换发射包括:~5S_2→~5I_7,~5F_4→~5I_7和~5S_2→~5I_8。     

热丝加热电流对CH薄膜沉积速率和表面形貌的影响

 热丝辅助裂解法是结合气相沉积制备聚对二甲苯薄膜和热丝化学气相沉积而形成的一种制-CH薄膜的新方法。热丝辅助裂解法的最大特点就是在保持低衬底温度情况下可以获得高沉积速率，而热丝加热电流对薄膜沉积速率和薄膜表面形貌具有重要影响。研究表明，热丝加热电流越大，薄膜沉积速率越高，在加热电流9A时，薄膜沉积速率可达0.002mm/min，同时薄膜表面粗糙度随之增加，薄膜表面也开始出现其它元素污染，因此，一般热丝加热电流选择为7A附近。     

Fabrication and transport properties of multiwall carbon nanotube crossroads

A multiwall carbon nanotube crossroads has been fabricated by a manipulation technique using a glass microcapillary, and the low temperature transport properties investigated. The two-terminal conductance of an individual tube shows Tomonaga–Luttinger liquid behavior G∝T^α at high temperature and dI/dV ∝V ^α at low temperature. However, no evidence of such a power-law behavior is obtained in the four-terminal conductance at the junction, where the conductance shows an almost metallic behavior ‘corrected’ by weak localization. Weak localization would essentially appear in electron states at the junctions of MWNTs.     

蓝光相变光盘的多层膜结构设计

为了使光盘获得优良的记录／读出性能并能够长期稳定地使用，必须优化设计相变光盘的多层膜结构。采用自行设计的模拟分析相变光盘读出过程设计软件，从光学角度出发模拟计算了蓝光(405nm)相变光盘的膜层结构，研究了多层膜系的反射率和反射率对比度等光学参量与各层膜厚度和槽深的关系。研究得出的最佳多层膜结构为：下介电层／记录层／上介电层／反射层的厚度对于台记录为100nm／10nm／25nm，／60nm，而对于槽记录则为140nm／15nm／30nm，／60nm，槽深为50nm。模拟计算结果对于将来高密度蓝光相变光盘的制备具有一定的指导意义。     

Photo-induced evolution of copper sheets from cluster molecules and its application to photolithographic copper patterning

UV photoexcitation of (t-butylethynyl copper)₂₄ cluster films induces segregation of the crystals into metallic and organic phases and leads to evolve the metallic sheets sandwiched by organic polymers. The growth of the metallic crystals in the plane of the photo-electromagnetic field is attributed due to plasmon-plasmon interaction among nanoparticles embedded in dielectric polymer matrices. The surface enhanced photochemical reaction of residual cluster molecules on the photon incident direction is expected to take an important role for joining the metal particles to produce a metallic sheet. We can apply this phenomenon for photolithographic copper pattern generation on a flexible base plate.     

Covalent functionalization of multi-walled carbon nanotubes by lipase

Lipase from Candida rugosa was covalently anchored onto acid-treated multi-walled carbon nanotubes (MWNTs) through a self-catalytic mechanism. A variety of characterization techniques including FTIR, Raman spectroscopy, and XPS were employed to demonstrate the formation of the ester linkage between lipase and MWNTs. The MWNTs-lipase biocomposites showed significantly increased solubility in some common-used organic solvents, such as THF, DMF and chloroform. This study may offer a novel and facile route for covalent modification of carbon nanotubes, and expand the potential utilization of both lipases and MWNTs in the fields of biocatalyst and biosensor.     

基片温度对坡莫合金薄膜结构和磁电阻的影响

用磁控溅射方法制备了系列坡莫合金Ni80Fe20薄膜。利用X射线衍射、扫描电子显微镜和原子力显徽镜分析了薄膜的结构、晶粒取向、薄膜厚度、截面结构和表面形态。用4点探测技术测量了薄膜的电阻和磁电阻。结果表明：随衬底温度的升高，晶粒明显长大。膜内的缺陷和应力显著减小，而且增强了薄膜晶粒的[111]择优取向。结果表明，薄膜电阻率显著减小，而磁电阻显著增大。     

2,3-二硫甲基-6,7-二硫十六烷基四硫代富瓦烯的合成

Langmuir-Blodgett(简称LB)法作为分子水平的成膜技术,能制备纳米级几乎无缺陷的单分子层或多分子层膜,在微电子学,分子器件,磁性有序材料,生物膜等方面有广泛的应用前景。目前,四硫富瓦烯类衍生物作为导电LB膜材料的研究,引起人们极大的兴     

Wavelength dependence in photochemical vapor deposition of aluminum film using dimethylaluminum hydride

In photochemical vapor deposition of aluminum film on silicon using dimethylaluminum hydride, (CH₃)₂AlH, a surface reaction dominated below a (CH₃)₂AlH pressure of 0.3 m Torr at 200°C, which was induced only with the 160 nm band emitted from a deuterium lamp. A gas-phase reaction occurred above 0.3 mTorr at 200°C, which could be induced by both 160 nm and 240 nm emission bands from the lamp. To distinguish between surface ad gas-phase reactions, a thickness profile was used. At 240°C the surface reaction could be induced even by the 240 nm band, while the deposits formed under illumination of the two bands were thinner than those obtained with only the 240 nm band, indicating occurrence of vacuum ultraviolet (VUV)-enhanced desorption. The mechanism responsible for the observed wavelength dependence in unclear. The electrical resistivity of the films deposited at 200°C was 4.5 μΩ cm, which did not change with wavelength.