模具法制备CVD金刚石热沉片的温度场与流场研究

本文通过有限元仿真研究了模具法制备CVD金刚石热沉片的温度场和流场,并对制备参数进行了优化.实验与仿真的结果均表明,进气量的大小对衬底附近流场的均匀性影响显著,热丝温度、热丝间距以及热丝到衬底的距离对衬底的平均温度影响显著,热丝间距和热丝温度对衬底温度的均匀性影响显著;模具法制备的CVD金刚石复制了模具型腔,保证了热沉片的结构完整性和尺寸精度,最终制备了精度较高的小型CVD金刚石热沉片.     

山东蒙阴金刚石多晶的显微红外光谱研究及其成因意义

山东蒙阴金刚石多晶可划分为多角刻面状和浑圆状金刚石多晶两大类,它们的显微红外光谱研究结果表明,金刚石多晶中的氮含量较低,介于16.69～72.81μg.g-1之间,且同一金刚石多晶的不同金刚石晶粒(或部位)中的氮含量不相同;刻面状金刚石多晶均为ⅠaAB型,且A心的浓度大于B心的浓度。浑圆状金刚石多晶也多为ⅠaAB型,但具有更高浓度的B心,且存在少数同时包含单替代氮、A心和B心的浑圆状金刚石多晶;金刚石多晶不是在金刚石颗粒的成核阶段所形成的,而是在金刚石长大期间或金刚石颗粒形成后的某个特殊条件下聚集而成;山东蒙阴金刚石多晶可能形成于氮浓度较低的较深部地幔。同时,多角刻面状金刚石多晶的形成时间稍晚于金刚石单晶体,浑圆状金刚石多晶的形成时间明显早于金刚石单晶体。     

退火时间对硼掺杂纳米金刚石薄膜微结构和电化学性能的影响

采用高分辨透射电镜、紫外和可见光Raman光谱及循环伏安法研究了1000 ℃下退火不同时间的硼掺杂纳米金刚石薄膜的微结构和电化学性能. 结果表明,随退火时间的延长,薄膜中纳米金刚石晶粒尺寸逐渐减小.当退火时间为0.5 h时, 金刚石晶粒尺寸由未退火样品的约15 nm减小为约8 nm, 金刚石相含量增加;当退火时间为2.0 h时,金刚石晶粒减小为2—3 nm, 此时晶界增多,金刚石相含量减少;退火时间为2.5 h时纳米金刚石晶粒尺寸和金刚石相含量又略有上升.晶粒尺寸和金刚石相含量的变化表明薄膜在退火过程中发生了金刚石和非晶碳相的相互转变.可见光Raman光谱测试结果表明,不同退火时间下, G峰位置变化趋势与I_D/I_G值变化一致,说明薄膜内sp²碳团簇较大时, 非晶石墨相的有序化程度较高.退火0.5, 1.0, 1.5和2.0 h时, 电极表面进行准可逆电化学反应,而未退火和退火时间为2.5 h时电极表面进行不可逆电化学反应.退火有利于提高薄膜电极的传质效率, 退火0.5 h时薄膜电极的传质效率最高,催化氧化性能最好.较小的晶粒尺寸、 较高的金刚石相含量以及纳米金刚石晶粒的均匀分布有利于提高电极表面反应的可逆性和催化氧化性能.     

化学气相沉积金刚石X射线探测器相对标定

利用神光Ⅱ激光装置,开展了化学气相沉积金刚石X射线探测器的相对标定技术研究。实验得到了金刚石X射线探测器与已绝对标定的平响应X射线二极管对X射线辐射的测量结果,计算得到金刚石X射线探测器平均灵敏度为1.19610-5 C/J,不同发次得到的灵敏度与平均值之间的偏差不大于13%。     

氧回旋离子束刻蚀化学气相沉积金刚石膜

利用非对称磁镜场电子回旋共振等离子体产生的氧回旋离子束刻蚀了化学气相沉积金刚石膜,研究了工作气压和磁电加热电压对金刚石样品附近的离子温度和密度的影响,并分析了金刚石膜的刻蚀和机械抛光效果。结果表明:当工作气压为0.03 Pa,磁电加热电压为200 V时,离子温度和密度最大,分别为7.38 eV和 23.81010 cm-3 。在此优化条件下刻蚀金刚石膜4 h后,其表面粗糙度由刻蚀前的3.525 m降为2.512 m,机械抛光15 min后,表面粗糙度降低为0.517 m,即金刚石膜经离子束刻蚀后可显著提高机械抛光效率。     

正庚烷相变序列的高压拉曼光谱研究

在室温条件下, 利用金刚石对顶砧超高压实验技术, 对液态的正庚烷进行了原位高压拉曼光谱研究, 采用红宝石荧光压标测压, 实验的最高压力为20.78 GPa。实验中发现, 当压力达到1.2 GPa左右时, 原本透明的样品腔内有小晶粒形成, 此时测量的拉曼谱上发现有许多新的拉曼峰出现。因此, 我们判断正庚烷在此压力下发生了一次相变; 当压力增加到3 GPa左右时, 在92.42 cm-1和2913.6 cm-1处又出现了2个新的拉曼峰, 并且拉曼频移随压力变化的曲线出现拐点, 我们推测在此压力下正庚烷可能又发生第二次相变; 当压力高于14.5 GPa时, 正庚烷发生了第三次压致相变; 而当压力介于7.5~14.5 GPa之间正庚烷处于两相共存的状态。我们给出了液体正庚烷在高压下的相变序列为: 液相-旋转相Ⅲ-旋转相Ⅳ-结晶相。该研究结果为进一步理解和研究其他正烷烃在高压下的结构、物理和化学特性提供了理论基础。     

Global optimization for generalized geometric programming problems with discrete variables

Generalized geometric programming (GGP) problems occur frequently in engineering design and management, but most existing methods for solving GGP actually only consider continuous variables. This article presents a new branch-and-bound algorithm for globally solving GGP problems with discrete variables. For minimizing the problem, an equivalent monotonic optimization problem (P) with discrete variables is presented by exploiting the special structure of GGP. In the algorithm, the lower bounds are computed by solving ordinary linear programming problems that are derived via a linearization technique. In contrast to pure branch-and-bound methods, the algorithm can perform a domain reduction cut per iteration by using the monotonicity of problem (P), which can suppress the rapid growth of branching tree in the branch-and-bound search so that the performance of the algorithm is further improved. Computational results for several sample examples and small randomly generated problems are reported to vindicate our conclusions.     

More on the revised GCH and the black box

We strengthen the revised GCH theorem by showing, e.g., that for , for all but finitely many regular κ<_ω, it holds that “λ is accessible on cofinality κ” in some weak sense (see below).As a corollary, λ=2^μ=μ⁺>_ω implies that the diamond holds on λ when restricted to cofinality κ for all but finitely many .We strengthen previous results on the black box and the middle diamond: previously it was established that these principles hold on for sufficiently large n; here we succeed in replacing a sufficiently large _n with a sufficiently large _n.The main theorem, concerning the accessibility of λ on cofinality κ, Theorem 3.1, implies as a special case that for every regular λ>_ω, for some κ<_ω, we can find a sequence such that , , and we can fix a finite set of “exceptional” regular cardinals θ<_ω so that if Aλ satisfies |A|<_ω, there is a pair-coloring so that for every -monochromatic BA with no last element, letting δ:=supB it holds that —provided that is not one of the finitely many “exceptional” members of .     

不同密度氢吸附金刚石(100)表面的微观结构

利用基于广义梯度近似的密度泛函理论,计算了金刚石(100)表面不同氢吸附密度的平衡态几何结构和态密度.结果表明对于2×1构型,在平行和垂直表面两个方向上发生弛豫,而1×1构型仅在垂直表面方向上发生弛豫.另外,清洁2×1,2×1 ∶0.5H和1×1 ∶1.5H表面,带隙中存在空表面态;而对于1×1 ∶2H和2×1 ∶H两种表面结构,空表面态上移进入导带,带隙中不存在表面态.结合电荷密度分布,探讨了金刚石(100)不同构型和氢吸附密度表面的表面态诱发机理. 关键词： 氢吸附 金刚石 弛豫 表面态     

碳纳米管/金刚石复合材料的场发射特性

采用微波烧结方法制备了碳纳米管/金刚石复合材料。将碳纳米管和纳米金刚石粉末混合后研磨压片,然后在微波等离子气相沉积系统中采用微波烧结。利用扫描电镜对复合材料的表面形貌和微观结构进行了分析,结果显示碳纳米管比较均匀地分散于复合材料中,并在表面形成了发射微尖。利用二极管结构在动态真空室中对复合材料的场发射特性进行了研究,复合材料有较好的场发射特性,电流密度接近15mA/cm2。