退火温度对低温生长MgxZn1－xO薄膜光学性质的影响

用射频磁控溅射法在80℃衬底温度下制备出Mg_xZn_1-xO(x=0.16)薄膜，用X射线衍射(XRD)、光致发光(PL)和透射谱研究了退火温度对Mg_xZn_1-xO薄膜结构和光学性质的影响.测量结果显示，Mg_xZn_1-xO薄膜为单相六角纤锌矿结构，并且具有沿c轴的择优取向；随着退火温度的升高，(002)XRD峰强度、平均晶粒尺寸和紫外PL峰强度增大，(002)XRD峰半高宽(F 关键词： xZn_1-xO薄膜')" href="#">Mg_xZn_1-xO薄膜 射频磁控溅射 退火     

Fabrication and characterization of sputtered titanium dioxide films

TiO₂ thin films were prepared under various conditions by using a reactive RF sputtering technique. The structural, optical and electrical characteristics of the films have been investigated. All as-deposited films were amorphous. After annealing at T > 673 K, the crystallinity of the observed tetragonal anatase phase appeared improved. The optical band gap, determined by using Tauc plot, has been found to amount to 3.38 ± 0.03 and 3.21 ± 0.03 eV for the direct and indirect transition, respectively. Also the complex optical constants for the wavelength range 300-2500 nm are reported. Using the two-point probe technique, the dark resistivity has been measured as a function of the film thickness, d. The resistivity, ρ, of the samples has been found to decrease markedly with increasing thickness, but only for d < 100 nm. The behaviour of ρd versus d was found to fit properly with the Fuchs and Sondheimer relation with parameters ρ_o = 4.95 × 10⁶ Ω cm and mean free path, l = 310 ± 2 nm. The log ρ versus 1/T curves show three distinct regions with values for the activation energy of 0.03 ± 0.01, 0.17 ± 0.01 and 0.50 ± 0.02 eV, respectively.     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO₂纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO₂的沉积时间及SiO₂的沉积时间一定而改变薄膜厚度时，多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明：具有纳米层状结构的Au/SiO₂多层薄膜在560 nm波长附近有明显的表面等离子共振吸收峰，吸收峰的强度随Au颗粒的浓度增加而增强，在Au颗粒浓度相同的情况下，复合薄膜 关键词： 2纳米复合薄膜')" href="#">Au/SiO₂纳米复合薄膜 多靶磁控溅射 吸收光谱 有效介质理论     

射频磁控溅射法制备薄膜电池电极的计算机模拟初步

计算机模拟仿真射频磁控溅射实验制备薄膜及离于电池电极,研究了在特定实验条件下薄膜的生长过程,并分析了影响薄膜生长的部分因素。     

Effects of UV photon irradiation on SiOx (0 < x < 2) structural properties

Thin films of a-SiO_x (0 < x < 2) were prepared by reactive r.f. magnetron sputtering from a polycrystalline-silicon target in an Ar/O₂ gas mixture. The oxygen partial pressure in the deposition chamber was varied so as to obtain films with different values of x. The plasma was monitored, during depositions, by optical emission spectroscopy (OES) system. Energy dispersive X-ray (EDX) measurements and infra-red (IR) spectroscopy were used to study the compositional and structural properties of the deposited layers.Structural modifications of SiO_x thin films have been induced by UV photons’ bombardment (wavelength of 248 nm) using a pulsed laser. IR spectroscopy and X-ray photoemission spectroscopy (XPS) were used to investigate the structural changes as a function of x value and incident energy. SiO_x phase separation by spinodal decomposition was revealed. The IR peak position shifted towards high wavenumber values when the laser energy is increased. Values corresponding to the SiO₂ material (only Si⁴⁺) have been found for laser irradiated samples, independently on the original x value. The phase separation process has a threshold energy that is in agreement with theoretical values calculated for the dissociation energy of the investigated material.For high values of the laser energy, crystalline silicon embedded in oxygen-rich silicon oxide was revealed by Raman spectroscopy.     

溅射功率对多层膜质量的影响

用磁控溅射技术制备薄膜，用X射线衍射研究在基片和靶间距离固定的情况下不同的溅射功率对薄膜结构的影响。结果表明：过低的溅射功率下淀积的薄膜有畸变的X射线衍射特征峰，特征峰强度小，半峰全宽大。而比较高溅射功率得到的薄膜有比较尖锐的X射线衍射特征峰，强度高和半峰全宽非常窄。研究表明，X射线衍射特征峰强度小和半峰全宽大的薄膜结构疏松，而强度高和半峰全宽非常窄的薄膜结构致密。     

Effect of nonstoichiometry on Raman scattering of VO2 films

We report on Raman scattering of VO2 films prepared by radio frequency magnetron sputtering under different conditions. Our investigations revealed that the dominated Raman peaks shift towards high frequency for both V-rich and O-rich VO2 films, compared with the stoichiometry VO2 films. The experimental evidence is presented and the cause for nonstoichiometry dependence of Raman spectra of VO2 films is discussed.     

后退火温度对溅射沉积Pb(Zr0.52Ti0.48)O3铁电薄膜结构和性能的影响

在具有Ti缓冲层的Pt(111)底电极上,用射频溅射工艺在较低的衬底温度(370℃)和纯Ar气氛中沉积Pb(Zr0.52Ti0.48)O3(PZT)薄膜,沉积过程中基片架作15°摇摆以提高膜厚的均匀性。然后将样品在大气中进行5min快速热退火处理,退火温度550-680℃。用XRD、SEM分析薄膜的微结构,RT66A标准铁电测试系统测量样品的铁电和介电性能。结果表明,所沉积的Pt为(111)取向,仅当后退火温度高于580℃,沉积在Pt(111)上的PZT薄膜才能形成钙钛矿结构的铁电相,退火温度在580-600℃时结晶为(110)择优取向,退火温度高于600℃时结晶为(111)择优取向。PZT薄膜的极化强度随退火温度的升高而增加,但退火温度超过650℃时漏电流急剧上升,因此退火处理的温度对PZT薄膜的结构和性能有决定性的影响。     

Optical properties of In2O3 oxidized from InN deposited by reactive magnetron sputtering

Unintentionally doped and zinc-doped indium nitride (U-InN and InN:Zn) films were deposited on (0 0 0 1) sapphire substrates by radio-frequency reactive magnetron sputtering, and all samples were then treated by annealing to form In₂O₃ films. U-InN and InN:Zn films have similar photon absorption characteristics. The as-deposited U-InN and InN:Zn film show the absorption edge, ∼1.8-1.9 eV. After the annealing process at 500 °C for 20 min, the absorption coefficient at the visible range apparently decreases, and the absorption edge is about 3.5 eV. Two emission peaks at 3.342 eV (371 nm) and 3.238 eV (383 nm) in the 20 K photoluminescence (PL) spectrum of In₂O₃:Zn films were identified as the free-exciton (FE) or the near band-to-band (B-B) and conduction-band-to-acceptor (C-A) recombination, respectively.     

WOx/TiO2光催化剂的可见光催化活性机理探讨

采用磁控溅射技术在用浸渍提拉法制得的TiO2薄膜上，溅射氧化钨层,通过气相反应中光催化降解二甲苯的实验表明，WOx/TiO2薄膜具有可见光活性.通过UV-Vis吸收光谱、X射线光电子能谱（XPS）等方法对其可见光活性的机理进行探索.UV-Vis吸收光谱表明WOx,TiO2对可见光响应的范围有一定的扩展,吸收强度增加.XPS表明WOx/TiO2薄膜表面形成了明显的W杂质能级和Ti缺陷能级,这是WOx/TiO2在可见光范围有一吸收的主要原因,也是光催化剂具有可见光活性的必要条件之一，同时杂质能级的存在使半导体费米能级上移,载流子增加,光催化效率提高.