Morphological and chemical study of the initial growth of CdS thin films deposited using an ammonia-free chemical process

We study the initial growth stages of CdS thin films deposited by an ammonia-free chemical bath deposition process. This ammonia-free process is more environmentally benign because it reduces potential ammonia release to the environment due to its high volatility. Instead of ammonia, sodium citrate was used as the complexing agent. We used atomic force microscopy (AFM), Rutherford backscattering (RBS) and X-ray photoelectron spectroscopy (XPS) to investigate the morphological and chemical modifications at the substrate surface during the first initial stages of the CdS deposition process. Additionally, X-ray diffraction (XRD) and optical transmission spectroscopy measurements were carried out to compliment the study. XPS results show that the first nucleation centers are composed by Cd(OH)₂ which agglomerate in patterns of bands, as demonstrated by AFM results. It is also observed that the conversion to CdS (by anionic exchange) of the first nucleus begins before the substrate surface is completely covered by a homogenous film.     

动态广义球对称含荷黑洞的统计熵

利用改进了的brickwall膜模型,计算了动态广义球对称含荷黑洞的熵,研究结果表明,对于动态黑洞,将黑洞熵表示为与视界面积成正比时,则比例系数总与动态黑洞的视界速度有关 关键词： 广义球对称黑洞 黑洞熵 brick-wall膜模型 WKB近似     

Improved coating method for uniform polymer layer in infrared hollow fiber

An improved coating method was proposed in order to form a uniform polymer layer in the fabrication of cyclic olefin polymer-coated silver (COP/Ag) hollow fiber. A COP solution was flowed in a closed loop, in which the silver-coated tube was used as a part of the loop. Owing to the constant flowing speed of the COP solution and the airtight flowing environment, a COP layer was uniformly formed. The hollow fibers attain high performance and deliver multi-wavelength laser light from the infrared to the visible simultaneously. The method was successfully applied to the fabrication of practical hollow fibers with 2 m length for the near and mid-infrared lasers.     

Chemical synthesis of p-type nanocrystalline copper selenide thin films for heterojunction solar cells

Nanocrystalline thin films of copper selenide have been grown on glass and tin doped-indium oxide substrates using chemical method. At ambient temperature, golden films have been synthesized and annealed at 200 °C for 1 h and were examined for their structural, surface morphological and optical properties by means of X-ray diffraction (XRD), scanning electron microscopy and UV-vis spectrophotometry techniques, respectively. Cu_2−xSe phase was confirmed by XRD pattern and spherical grains of 30 ± 4 - 40 ± 4 nm in size aggregated over about 130 ± 10 nm islands were seen by SEM images. Effect of annealing on crystallinity improvement, band edge shift and photoelectrochemical performance (under 80 mW/cm² light intensity and in lithium iodide electrolyte) has been studied and reported. Observed p-type electrical conductivity in copper selenide thin films make it a suitable candidate for heterojunction solar cells.     

Characteristics of Ti0.97Co0.03O2:Sb0.01 dilute magnetic semiconducting thin films deposited at 500 °C by pulsed laser deposition

Epitaxial Ti_0.97Co_0.03O₂:Sb_0.01(TCO:Sb) films were deposited on R-Al₂O₃ (1 1 0 2) substrates at 500 °C in various deposition pressures by pulsed laser deposition. The solubility of cobalt within the films increases with decreasing deposition pressure at a deposition temperature of 500 °C. The TCO:Sb films deposited at 5×10⁻⁶ Torr exhibit a p-type anomalous Hall effect having a hole concentration of 6.1×10²²/cm³ at 300 K. On the other hand, films deposited at 4×10⁻⁴ Torr exhibits an n-type anomalous Hall effect having an electron concentration of about 1.1×10²¹/cm³. p- or n-type DMS characteristics depends on the change of the structure of TCO:Sb films and the solubility of Co is possible by controlling the deposition pressure.     

In‐line monitoring of UV photopolymerization with a quartz crystal resonator

An in‐line monitoring device using a quartz crystal resonator for thin film polymerization was proposed, and its performance has been evaluated by implementing in the UV polymerization of 2‐hydroxyethyl methacrylate with a photoinitiator of 1‐chloroanthraquinone. Because the variation of resonant resistance of the resonator is proportional to the square root of viscosity change that is closely related to the polymerization degree, the resistance can be used as a measure of the polymerization degree. The resistance measurements were compared with the outcome of instrumental analyses of polymerization degree using an FTIR spectrometer and a gel permeation chromatograph. The experimental results showed that the resistance measurements were consistent with the experimental outcome of the instrumental analyses, and this indicates the effectiveness of the proposed device. Owing to the simplicity and availability of the resonator system, its wide utilization in the monitoring of a variety of film polymerization processes, including photoresistor application, is expected. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2428–2439, 2006     

Differential AC-chip calorimeter for glass transition measurements in ultrathin films

A differential AC-chip calorimeter capable of measuring the step in heat capacity at the glass transition in nanometer-thin films is described. Because of the differential setup, pJ/K sensitivity is achieved. Heat capacity can be measured for sample masses below 1 ng in broad temperature range as needed for the study of the glass transition in nanometer-thin polymeric films. Relative accuracy is sufficient to investigate the changes in heat capacity as the step at the glass transition of polystyrene. The step is about 25% of the total heat capacity of polystyrene. The calorimeter allows for the frequency dependent measurement of complex heat capacity in the frequency range from 1 Hz to 1 kHz. The glass transition in thin polystyrene films (50–4 nm) was determined at well-defined experimental time scales. No thickness dependency of the glass transition temperature was observed within the error limits (±3 K)—neither at constant frequency (40 Hz) nor for the trace in the activation diagram (1 Hz–1 kHz). © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2996–3005, 2006     

Preparation and characterization of mesoporous silica thin films from polyethoxysiloxanes

Tetraethoxysilane (TEOS) and polyethoxysiloxanes (PEOSs; prepared by the acid‐catalyzed hydrolytic polycondensation of TEOS) were subjected to the sol–gel process in the presence of cetyltrimethylammonium bromide (CTAB), respectively. The PEOSs with M_w 700–26,000, as prepared by sol–gel coating of TEOS and PEOS under various conditions, were used. Uniform and crack‐free thin films of thickness 276–613 nm were prepared by spin‐coating of a PEOS solution containing CTAB. When the coating films were sintered at 400 °C, the combustion of ethoxy groups and CTAB took place to provide porous silica thin films. The structure of the thin films was found to be dependent on the molecular weight of PEOS and the molar ratio of CTAB/Si: lamellar or hexagonal phase was observed for M_w less than 15,000 and for CTAB/Si molar ratios greater than 0.10. Honeycomb structures were observed for M_w less than 5000 and for CTAB/Si molar ratios of 0.15. The honeycomb structure was also observed by atomic force microscopy and transmission electron microscope. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2542–2550, 2006     

单层光学薄膜中薄膜－衬底体系的双重干涉效应及其应用

提出了单层光学薄膜中薄膜与衬底反射光之间的双重干涉效应的理论，实验结果证实了理论分析的正确性。双重干涉效应使薄膜－衬底体系的热致反射调制度高达８０％，这一效应可望有极广泛的应用     

热丝CVD生长金刚石薄膜喇曼散射研究

本文报道热丝化学气相沉积法（ＨＦＣＶＤ）生长金钢石薄膜的喇曼散射结果。选取多种峰型，对金钢石薄膜喇曼谱（１１０－１８００ｃｍ－１）采用最小二乘法进行非线性拟合，得到最佳拟合模型，其计算得到的拟合曲线怀实验谱图符合得较好。该模型揭示，石墨Ｄ峰（１３５５ｃｍ－１）是金刚石薄膜喇曼谱中不可缺少的一个组份，并且结合石墨Ｄ峰和金刚石喇曼的空间相关线型，可以解释金刚石喇曼区特殊峰形的物理机制，拟合参量的进一步