ICP—MS测定高纯钪,钇,钬,铥和镥氧化物中痕量稀土杂质研究

研究了用电感合等离子体质谱测定高纯钪、钇、钬、铥和镥氧化物中痕量稀土杂质的方法，用内标法有效地校正了基体抑制效应，改善了精密度。与ＩＣＰ－ＡＥＳ分析相比，本法具有灵敏度高、流程简单快速、耗样少等特点，测定下限可降低１－２个数量组。方法可用于９９．９９９％的高纯稀土的分析。     

Al—Mg—Y合金相图中富铝角相边界的X光测定

以Al-Mg为基的合金在工业上有广泛的用途,近年来人们为提高其加工性和强度,往往又添加适量的稀土元素,特别是加微量的钇可提高合金的高温强度,所以测定Al-Mg-Y合金系统的相图是具有实用意义的。本文用X光品格参数方法测定了含钇0.1wt％和0.2wt％的Al-Mg合金相图中富铝角的相边界,这是完全基于实用的考虑,因为工业上广泛应用的合金大都在这个成分区域内。     

介孔分子筛MSU-1的合成

MSU X介孔分子筛具有三维立体交叉排列的蠕虫状孔道结构,有利于客体分子在其孔道内扩散[1]。目前合成MSU X的原料[2 4]TEOS水解速度慢,合成过程较易控制,但价高、易燃、有刺激性。本文采用文献[5 7]法,以水玻璃、A(EO)9为原料,在酸性至近中性的范围里合成了MSU 1介孔分子筛,与TEOS为原料的MSU 1合成进行了比较,考察了pH值和不同类型表面活性剂(脂肪醇聚氧乙烯醚和烷基酚聚氧乙烯醚)对产物结构性质的影响。1　实验部分1 1　试剂和仪器水玻璃(SiO2%≈26、Na2O%≈8),工业级,青岛海洋化工厂生产;脂肪醇聚氧乙烯醚非离子表面活性…     

水合醋酸铈直接热分解制备超细氧化铈及其抛光性能

Ultra fine ceria was prepared by calcining hydrate cerium acetate. The effects of pyrolysis temperature on the particle size, morphology, specific surface area and loose packing density of ceria were investigated, and the removal rate of optical glasses polishing by ceria was determined. The results show that with the increase of pyrolysis temperature, the loose deposit density and crystallinity increases and the specific surface area decreases, however, the particle size decreases firstly and then increases, the minimum medium particle size D₅₀ is 0.47 μm at pyrolysis temperature of 1 000 ℃. The SEM images of ceria prepared by the decomposition at 800 ℃ or at 1 100 ℃ show porous powders or quasi-sphere small particles with loosely agglomeration, respectively. It was found that the removal rate varied with pyrolysis temperature in preparation of ceria and the property of glass polished. The removal rate for three kinds of glasses was in the order of ZF7> F1> K9, and the maximum value appeared at around 1 000 ℃ for ZF7 and F1, and at around 1 100 ℃ for K9.     

一种在线液—液萃取微型多用分相器的设计和应用：IV.流动注射液— …

设计了在线液－液萃取多用重分布相器及相应流动注射流路系统与ＩＣＰ－ＡＥＳ法联用。具有良好的分析性能，通过对矿石中某些重稀土元素在硝酸介质中被ＴＢＰ萃取的应用研究表明钇，镱，铒的检出限（３σ）分别为６．８ｎｇ／ｍＬ，０．２ｎｇ／ｍＬ和１．５ｎｇ／ｍＬ，精密度（ＲＳＤ％）分别为０．２４，０．４７和１．８，进样频率为２５－３０个／ｈ。     

N掺杂可见光化催化剂的研究

The N-doped, yellow colored titanium oxide photocatalysts were prepared with Ti(SO4)2 and NH4HCO3 as precursors by precipitation method. The photocatalytic ability under the irradiation of UV or visible light for the catalysts prepared was studied by degradation of styphnic acid. The materials were characterized by EDS, XRD, FTIR, UV-Vis DRS, and XPS. The results indicate that the photocatalytic ability of catalysts is improved, especially the ability of visible light response. The results of UV-Vis DRS show that the response wavelength range of N-dopped nitrogen is red shifted, the absorption region is expanded to 476 nm.     

Ce0.6Zr0.35Y0.05O2和Pr0.6Zr0.35Y0.05O2催化剂表面上CO氧化和18O-16O交换反应的研究

测定了在Ce0.6Zr0.4O2,Ce0.6Zr0.35Y0.05O2,Pr0.6Zr0.4O2和Pr0.6Zr0.35Y0.05O2 (分别表示为CZ,CYZ,PZ和PYZ)样品表面上的CO氧化反应和18O-16O 同位素交换反应.结果表明: 在CZ和PZ系列固熔中掺杂Y3 离子可以改善晶格氧的迁移速度;PZ和PZY的晶格氧比CZ 和CZY 的晶格氧具有更高的氧化反应活性.其原因是将Y3 掺杂到Ce0.6Zr0.4O2 或Pr0.6Zr0.4O2晶格中,增加了样品的氧空位浓度,从而提高了晶格氧的迁移性质,而PrOx比CeO2具有更低温度的氧化还原性质,因此PZ和PZY的晶格氧比CZ 和CZY 的晶格氧具有更高的氧化反应活性.     

显微共焦拉曼光谱研究电化学合成聚苯胺膜

显微共焦拉曼技术被用来研究电化学合成的聚苯胺（PANI）膜. 研究结果表明：在不同的激发光聚焦深度，聚苯胺膜的拉曼光谱有明显变化.从而反映出聚苯胺膜的掺杂程度在膜生长过程中随膜厚度的增长而增加. 并由X射线电子能谱（XPS）和紫外吸收光谱（UV）分析证实.     

铈,铝变质奥—贝钢中共晶体异质核心研究

Ｃｅ、Ａｌ复合变质团球状共晶体奥贝钢（简称ＡＢＮＥ钢）中的共晶体是由于Ｃ、Ｍｎ偏析，在凝固后期奥氏体枝晶间形成了渗碳体和奥氏体的伪共晶组织。通过热力学和二维点阵错配度计算，采用透射电镜和扫描电镜观察，发现ＣｅＯ２和ＣｅＡｌＯ３作为共晶体的异质核心而使共晶体球化。     

四氯化铂与铂氯酸掺杂聚乙炔的X射线光电子能谱研究

用 X 射线光电子能谱法对四氯化铂(PtCl_4)及铂氯酸(H_2PtCl_6·6H_2O)掺杂聚乙炔进行了研究.发现Pt4f 与 Cl2p 谱峰均由相距约1.5eV 的两组峰组成.Pt4f 高结合能端的组份可指认为四价铂,而低结合能端的组份为二价铂.对 Pt4f 及 Cl2p 峰积分强度的分析表明,对二价铂有:[Cl]/[pt~(2 )]=2,对四价铂有:[Cl]/[pt4~ ]=6.C 1s 峰也由两个分离约1eV 的峰组成,高结合能端的强度随掺杂浓度的增加而增加.这些结果说明铂盐掺杂聚乙炔通过由高分子链向掺杂剂的电荷转移而使部份高分子链被氧化,部份四价铂盐被还原成 PtCl_2.透射电镜形态观察及选区电子衍射证明膜上存在 PtCl_2的聚集.电荷转移链段在高分子链上的分布是无规的.并由此估计了电荷转移链段上每个碳原子的电荷约为 0.2|e|.由以上结果我们推断 PtCl_4与 H_2PtCl_6·6H_2O 的电荷转移过程可由下式表达.对 PtCl_4 掺杂:2PtCl_4 2e→PtCl_6~(2-) PtCl_2对 H_2PtCl_6掺杂:2H_2PtCl_6 2e→PtCl_6~(2-) PtCl_2 4HCl这两种掺杂剂的对阴离子均是 PtCl_6~(2-)离子.