溶胶—凝胶法制备SiO2基片Er^3＋：Al2O3光学薄膜

用溶胶—凝胶法在SiO2基片上提拉制备了掺Er^3 ：Al2O3光学薄膜。采用扫描电子显微镜、原子力显微镜、差热—热重分析仪、X射线衍射仪研究了掺Er^3 ：Al2O3光学薄膜的肜貌和结构特性。在900℃烧结后，SiO2基片上提拉15次形成厚度8μm掺摩尔比0．01Er^3 的面心立方结构γ-Al2O3薄膜具有明显(110)择优取向，掺摩尔比0．01Er^3 对γ—Al2O3的品体结构和结晶生长过程木产生显著影响。薄膜具有均匀多孔结构，平均粒径为30～100nm，平均孔径为50～100nm，表面起伏度为10～20nm。掺摩尔比0．01Er^3 ：rAl2O3薄膜，获得了中心波长为1．534μm(半峰全宽为36nm)的光敛发光谱。     

Study of hot bands in the B2Σ+u-X2Σ+g system of C-2 anion

Optical heterodyne magnetic rotation enhanced velocity modulation spectroscopy was employed to observe the visible absorption spectra of the B^2Σ^+_u-X^2Σ^+_g electronic transition of C^-_2. Four hot bands (0,1), (1,2), (2,3) and (3,4) have been observed and the band (3,4) is measured directly for the first time, so far as we know, by absorption. A rotational analysis was carried out to obtain molecular constants. With the Franck－Condon principle and the vibrational Boltzmann distribution, we have estimated the vibrational temperature of C^-_2 to be about 3000K.     

利用富铈混合稀土改善工业纯铝中富铁相形貌的研究

利用金相分析方法研究了富Ce混合稀土变质对含不同Fe量的工业纯铝的组织和其中富铁相形貌的影响。试验结果表明,随着Fe含量的增加,富铁相由弥散细小的颗粒状向短棒状、长针状转变;富Ce混合稀土变质使铝中的富铁相由长针状变为弥散细小的颗粒状。随着稀土含量的增加,-αAl晶粒逐渐细化,富铁相尺寸及数量逐渐减小。添加0.5%稀土时,-αAl晶粒细化效果最佳,而且富铁相呈细小颗粒状均匀分布在-αAl基体的晶界处。本文还对稀土改善富铁相的机制进行了分析。     

聚变等离子体中的快离子压强

本文运用Fokker-Planck方程的慢化近似,考虑存在多种离子成份(包括杂质),假定它们具有共同的温度,我们得到了聚变产生的快离子压强的简单封闭形式表示式。表明在典型的工作温度下(～60keV),D-~3He等离子体中聚变产生的快离子压强约为本底热压强的20％,这与D-T等离子体工作在20keV时的比值几乎相同。因此,D-~3He和D-T在它们相应的预期工作温度下,它们各自的快离子压强对总压强的影响是类似的,然而在更高的温度下,这个比值将变得更大。     

Magnetically rotational reactor for absorbing benzene emissions by ionic liquids

A magnetically rotational reactor （MRR） has been developed and used in absorbing benzene emissions. The MRR has a permanent magnet core and uses magnetic ionic liquid [bmim]FeCl4 as absorbent. Benzene emissions were carried by N2 into the MRR and were absorbed by the magnetic ionic liquid. The rotation of the permanent magnet core provided impetus for the agitation of the magnetic ionic liquid, enhancing mass transfer and making benzene better dispersed in the absorbent. 0.68 g benzene emissions could be absorbed by a gram of [bmim]FeCl4, 0.27 and 0.40 g/g higher than that by [bmim]PF6 and [bmim]BF4, respectively. The absorption rate increased with increasing rotation rate of the permanent magnet.     

GeⅩⅪ-SeⅩⅩⅢ离子n=3,Δn=0跃迁谱线和振子强度的计算

用HFR方法对CaⅨ-KrⅩⅩⅤ离子3s2,3s3p,3s3d,3p2组态能级结构进行了理论计算.在已有实验研究的基础上,通过分析离子能级沿等电子序列的变化规律,运用最小二乘拟合方法预言计算了GeⅩⅪ-SeⅩⅩⅢ离子3s2,3s3p,3s3d,3p2组态14条精细结构能级值.在此基础上,进一步计算了GeⅩⅪ-SeⅩⅩⅢ离子3s2-3s3p,3s3p-3s3d和3s3p-3p2跃迁的23条谱线波长和相应的振子强度.计算结果与已有的实验值十分吻合,波长的最大不确定度为0.008 nm.