采用紧束缚原子间作用势，利用分子动力学模拟(MD)的方法研究了Al5Fe2合金熔体的微观结构，发现在结构因子的小角部分(Q=15.7nm^-^1)出现了一个明显的预峰(FSDP)，并得到X射线衍射实验的进一步印证，在实验测得的合金衍射图样中，液态衍射曲线与固态衍射曲线间存在着很好的对应关系，它们在小角部分都存在峰位，这表明Al5Fe2合金熔体与其固态在结构上存在着很大的相似性。通过对化学短程序参数α及Bhatis-Thornton(BT)结构因子的分析计算，发现熔体中存在较强的化学序，并认为正是这种化学序导致了中程有序结构(MRO)的产生。Faber-Ziman(FZ)偏结构因子的SFe-Fe(Q)和SAl-Fe(Q)在Q=15.7nm^-^1处分别存在最大值与最小值，也是熔体中存在着超结构的表征。同时，我们还给出了体系的配位数及代表中程有序的原子团簇的结构模型。     

酰胺-尿素-NaBr熔体中电沉积Tb-Co合金的研究

在353K的乙酰胺 尿素 NaBr熔体中,Co(Ⅱ)一步不可逆还原为金属Co,测得α为0.23和D0为1.25×10-6cm2·s-1;Tb(Ⅲ)不能单独还原为Tb,但是可以被Co2+诱导而共沉积。由恒电位电解法得到非晶态的Tb Co合金;Tb的含量随阴极电位的负移、Tb3+ Co2+摩尔比增大及电解时间延长而增大,Tb的最大含量可达83.91wt%。Tb Co合金膜经高温晶化后用X射线衍射分析其组成为(TbCo3)12R。     

Spectral investigation of Sm3＋/yb3＋co-doped sodium tellurite glass

YAG-Ce,Nd,and Yb phosphors with a triple-doped system are prepared by conventional solid-state reaction method.The fluorescence emission and excitation spectra are measured and analyzed.The influences of Yb3+ doping concentration on the emission of Yb3+ and Nd3+ in YAG-Ce,Nd,and Yb are studied.The fluorescence decay spectra,lifetime,and energy transfer efficiency of Ce3+ in different host materials of YAG-Ce and Yb,and YAG-Ce,Nd,and Yb are also compared.Furthermore,the trends of fluorescence decay spectra and the lifetimes of Nd3+ and Yb 3+ in YAG-Ce,Nd,and Yb with the increase of Yb3+ concentration are discussed.Results indicate that YAG-Ce,Nd,and Yb are good candidates for downconverting phosphor,with energy transfer efficiency reaching as high as 82.8%.     

Preparation of Thermo-Stable Bulk Metallic Glass of Nd10Cu20Ni10Al10 by Rapid Compression

Melt of Nd60Cu20NiloAl10 alloy is solidified by rapid compression from 0.1 to 5.5 GPa at 793K and from 0.1 to 3.2GPa at 873K within 20ms, separately. A fully bulk metallic glass is obtained by the rapid compression method. By comparing with as-cast bulk metallic glass （BMG）, it is found that Nd60Cu20Ni10Al10 BMG prepared by rapid compression exhibits a higher thermodynamic stability and a paramagnetic property. The relationship between the glass-formation temperature and the pressure in rapid compression for the BMG is demonstrated in the P - T phase diagram.     

Preparation of High-Density Nanocrystalline Bulk Selenium by Rapid Compressing of Melt

The melt＇s solidification behavior of elemental selenium is investigated by a series of experiments including rapid compressing to 2.8 and 3.5 GPa within 20ms respectively, slow compressing to 2.8 GPa for 20 min and natural cooling at ambient pressure. Based on the x-ray diffraction, scanning electron microscope and transmission electron microscope results of the recovered samples, it is clearly shown that homogenous nanostructures are formed only by the rapid compression processes, and that the average crystal sizes are about 18.7 and 19.0 nm in the samples recovered from 2.8 and 3.5 GPa, respectively. The relative density of the nanocrystalline bulk reaches 98.17% of the theoretical value. It is suggested that rapid compression could induce pervasive nucleation and restrain grain growth during the solidification, which is related to fast supercooling, higher viscosity of the melt and lower diffusivity of atoms under high pressure.     

CuSn合金熔体结构转变及其动力学行为探索

迄今为止,人们对合金在液相线之上的熔体结构转变过程的认识仍不清晰. 本文运用电阻法、DSC热分析等实验手段,对CuSn60wt%二元合金熔体在升温及保温条件下的结构转变动力学过程进行了研究,并通过相变动力学理论探讨了转变过程的特征与微观物理机制. 分析表明：合金熔体中温度诱导的结构转变过程符合“形核-长大”类型,其动力学过程为自动催化转变模式,其中液相中新结构原子团簇的“形核率”为转变速率的主导控制因素.     

聚乳酸-聚乙二醇嵌段共聚物晶行为研究

用1H NMR, SEC, XRD和DSC对聚乳酸(PLLA)-聚乙二醇(PEG)二嵌段共聚物进行了表征. 由于共聚物中两种组分比例的不同, 表现出某组分单独结晶或两种组分共同结晶. 用DSC和POM方法, 对两组分含量相当的共聚物进行了熔体结晶行为研究, 并采用Avrami方程进行了结晶动力学计算. 用Lauritzen-Hoffmann理论对PLLA-PEG结晶机理进行了分析. 在70~94 ℃范围内, 得到成核参数Kg(POM)=5.23×105 K2. 共聚物的Kg和链折叠自由能σe都比均聚物的文献报道值高, 表明PEG链段的存在影响了PLLA的结晶, 使得其成核较均聚物困难.     

稀土催化材料--铈锆固熔体的研究与应用

用助表面活性剂法制备一系列CexZr1-xO2固熔体, 对固熔体结构进行XRD表征(600和900 ℃焙烧), 研究了固熔体的结构、晶相,并进行储氧量、比表面积的测定和催化活性评价. 结果表明, 含铈锆固熔体的三效催化剂催化活性明显高于纯氧化铈的催化活性.     

用动态粘弹函数关系表征PMMA/α-MSAN共混物的相分离

测定了聚甲基丙烯酸甲酯／聚（α－甲基苯乙烯丙烯腈）共混物熔体的动态粘弹性．考察动态储能模量Ｇ′与动态损耗模量Ｇ″的关系，发现在终端区域两种聚合物的ｌｇＧ′～ｌｇＧ″关系曲线与温度无关，其外推直线斜率接近２；而其共混物的斜率明显小于２，并随组成变化呈现温度依赖性，由此得到的“临界温度”可用于表征这种具有ＬＣＳＴ行为的共混物的相容性．     

顺丁橡胶挤出过程中熔体不稳定流动的研究

<正> 在高聚物挤出过程中,当挤出速率在一定条件下增大到某一数值时,挤出物表面将出现竹节状或鲨鱼皮状、扭曲等现象,此即为熔体破裂或不稳定流动。它严重影响着高聚物制品的外观质量,并限制了生产速率的进一步提高。所以,深入探讨不稳定流动产生的机理,进而建立判定不稳定流动的临界条件,对指导高聚物压出成型加工过程参数的选择及过程控制,具有实际意义。