Soliton Solution of SU（3） Gauge Fields at Finite Temperature

Starting from a soliton model of SU（3） gauge fields, we investigate the behaviour of the model at finite temperature. it is found that colour confinement at zero temperature can be melted away under high temperatures.     

激光晶体YAG中Er3+的辐射跃迁

本文讨论和分析了激光晶体YAG中Er3+离子的激光上能级的4S3/2、4I11/2和4I13/2辐射跃迁的有关因素。     

Fabrication of Compound Lattice by Holographic Lithography

Some compound lattices in photonic crystals with large complete photonic band gaps, such as the diamond structure and the two-dimensional hexagonal compound structure, is desired for fabrication. A novel method for fabrication of compound lattices by holographic lithography is reported. The key point is phase modulation by photoelectrical control and multiple-exposure techniques. This technique introduces many advances: for instance,using the same coherent beams and without changing the position of the sample during multiple-exposure.     

成分和厚度的依赖

通过调整Mn的成分，系统地研究了Ni81Fe19/Ni100-xMnx双层膜的磁学性质，特别是交换偏置场(Hex)的变化.当Ni100-xMnx中Mn的原子百分比在534%到600%之间时，对于150nm的Ni81Fe19，得到了最大的交换偏置场175kA/m，同时由于Mn对Ni81Fe19层的扩散所造成的磁矩的降低小于20%；高角x射线衍射证明Ni100-xMnx的晶格常数随着Mn成分的改变而变化，Mn含量越多，其晶格常数越大；制备态Ni100-xMnx膜晶格常数与θ相NiMn膜晶格常数的接近程度与NiMn膜θ相形成的容易程度相对应.也研究了交换偏置场随着Ni１００-xMnx厚度的变化，第一次得到了当Ni100-xMnx中Mn的原子百分比为706%时，Ni81Fe19(150nm)/Ni100-xMnx(90nm)双层膜在经过240℃，5h退火后，可以有80kA/m的交换偏置场，此时铁磁层磁矩的大小几乎不变. 关键词： Ni81Fe19/Ni100-xMnx 交换偏置场     

大口径光束波前采样器(孔栅)的研制

应用平面波角谱理论，分析了采样器对光波场采样和分光的基本原理以及对空间采样频率的选择规则，描述了实际研制的大口径采样器的结构设计，并通过数值方法和高能激光大气传输实验研究了高能激光经采样器前／后的远场光斑分布关系。结果表明：利用光束波前采样器能高保真地实现对高能激光束的分光。     

CNx纳米管的制备、结构观察及低场致电子发射性能研究

采用高温热解法，以乙二胺为前驱液，在沉积有铁催化剂的p型硅（111）基底上制备出了定向生长的CNx纳米管.利用扫描电子显微镜、高分辨率透射电子显微镜和拉曼光谱对CNx纳米管进行了形貌观察和表征.CNx纳米管的高度在20?μm左右，直径在50—100nm之间，具有明显的“竹节状”结构，结晶有序度较差.对CNx纳米管薄膜进行低场致发射性能测试：外加电场为1.4V/μm，观察到20?μA /cm2发射电流，外电场升至2.54V/μm时发射电流达到1.280mA/cm2，在较高外电场下，没有发现电流“饱和”.这比 关键词： CNx纳米管 高温热解 “竹节状”结构 场致发射     

Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955 Pb（Zn1/3Nb2/3）O3-0.045PbTiO3 Single Crystals

We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.     

新核素278113的基态特性及其α衰变链的研究

用形变的相对论平均场模型,Skyrme-Hartree-Fock模型及宏观-微观模型研究了新核素²⁷⁸113及其α衰变链的α衰变能和半衰期.计算的α衰变能同实验数据比较符合,相应的半衰期也在合理的范围内.计算进一步表明形变对超重核的基态性质有重要影响.     

Cr3+：MgAl2O4晶体EPR参量及其电子精细光谱的研究

考虑了SS(Spin-Spin)作用和SOO(Spin-Other-Orbit)作用，采用完全对角化方法，结合自旋Hamiltonian理论，研究了Cr³⁺∶MgAl₂O₄晶体EPR参量及其吸收光谱，理论与实验符合甚好. 在此基础上，进一步研究了⁴A₂(3d³)离子EPR参量的微观起源. 研究表明，EPR参量起源于四种微观机制：(1) SO(Spin-Orbit) 耦合机制；(2) SS耦合机制；(3)SOO耦合机制；(4) SO～SS～SOO总联合作用机制. 在这些机制中，SO机制是最主要的.     

坩埚下降法生长的LiNbO3,Fe:LiNbO3,Zn:Fe:LiNbO3单晶的吸收光谱特性

用紫外可见光谱(UV／Visible Spectra)测试并研究了坩埚下降法生长的LiNbO3、Fe：LiNbO3，以及Zn：Fe：LiNbO3晶体的吸收特性。分析了产生这些吸收特性的原因以及与工艺生长方法的内在联系。研究结果表明：LiNbO3单晶沿晶体生长方向，其紫外吸收边向长波方向移动，且在350—450nm波段的吸收也逐渐增大，这是由于Li的分凝与挥发，逐渐产生缺锂所造成的；在Fe：LiNbO3单晶中观察到Fe^2 离子在480nm附近的特征吸收峰，并发现沿生长方向，Fe^2 离子的浓度逐渐增加，这与提拉法生长得到的晶体不同；在Fe：LiNbO3单晶中掺入质量分数为1．7％ZnO后，吸收边位置发生蓝移，而掺杂质量分数达到3．4％时，观察到有红移现象。Fe^2 离子在Zn：Fe：LiNbO3单晶中的浓度与ZnO掺杂量有密切关系。在掺杂质量分数1．7％ZnO的Fe：LiNbO3单晶中，Fe^2 离子从底部到顶部的浓度变化比在掺杂质量分数3．4％ZnO晶体中大，这是由于Zn^2 抑制Fe^2 离子进入Li位的能力随掺杂量的增加而逐渐减弱造成的。就该下降法工艺技术对Fe^2 离子在晶体中的浓度分布的影响作了分析。