Organic–Inorganic Hybrid Gold Halide Perovskites: Structural Diversity through Cation Size

Crystal structures of a series of organic–inorganic hybrid gold iodide perovskites, formulated as A₂[Au^II₂][Au^IIII₄] [A=methylammonium (MA) ( 1 ) and formamidinium (FA) ( 2 )], A′₂[I₃]_1−x[Au^II₂]_x[Au^IIII₄] [A′=imidazolium (IMD) ( 3 ), guanidinium (GUA) ( 4 ), dimethylammonium (DMA) ( 5 ), pyridinium (PY) ( 6 ), and piperizinium (PIP) ( 7 )], systematically changed depending on the cation size. In addition, triiodide (I₃⁻) ions were partly incorporated into the AuI₂⁻ sites of 3 – 7 , whereas they were not incorporated into those of 1 and 2 . Such a difference comes from the size of the organic cation. Optical absorption spectra showed characteristic intervalence charge-transfer bands from Au^I to Au^III species, and the optical band gap increased as the size of the cation became larger.     

General Formation of Macro-/Mesoporous Nanoshells from Interfacial Assembly of Irregular Mesostructured Nanounits

Mesoporous core–shell nanostructures with controllable ultra-large open channels in their nanoshells are of great interest. However, soft template-directed cooperative assembly to mesoporous nanoshells with highly accessible pores larger than 30 nm, or even above 50 nm into macroporous range, remains a significant challenge. Herein we report a general approach for precisely tailored coating of hierarchically macro-/mesoporous polymer and carbon shells, possessing highly accessible radial channels with extremely wide pore size distribution from ca. 10 nm to ca. 200 nm, on diverse functional materials. This strategy creates opportunities to tailor the interfacial assembly of irregular mesostructured nanounits on core materials and generate various core–shell nanomaterials with controllable pore architectures. The obtained Fe,N-doped macro-/mesoporous carbon nanoshells show enhanced electrochemical performance for the oxygen reduction reaction in alkaline condition.     

二氧化钒薄膜的低温制备及其性能研究

针对VO₂薄膜在微测辐射热计上的应用，采用射频反应溅射法，在室温下制备氧化钒薄膜；研究了氧分压对薄膜沉积速率、电学性质及成分的影响.通过调节氧分压，先获得成分接近VO₂的非晶化薄膜，再在400℃空气中氧化退火，便可制得高电阻温度系数，低电阻率的VO₂薄膜，电阻温度系数约为-4%/℃，薄膜方块电阻为R_□为100—300kΩ；薄膜在室温下沉积，400℃下退火的制备方法与微机电加工(micro electromechanic 关键词： 二氧化钒 电阻温度系数 氧分压 射频反应溅射法     

溶胶-凝胶VO2薄膜转换特性研究

利用溶胶凝胶法在SiO2Si衬底上沉积高取向的V2O5薄膜,在压强低于2Pa,温度高于400℃的条件下,对V2O5薄膜进行真空烘烤,获得了电阻率变化3个数量级以上、弛豫宽度为62℃的VO2多晶薄膜.以X射线衍射(XRD)、扫描电子显微镜(SEM)图和电阻率转换特性等实验结果为依据,详细分析了溶胶凝胶薄膜在真空烘烤时从V2O5向VO2的转化,它经历了从VnO2n+1(n=2,3,4,6)到VO2的过程.实验证明,根据选择合适的成膜热处理条件和真空烘烤条件是实现溶胶凝胶V2O5结构向VO2结构成功转换的关键 关键词： 溶胶-凝胶法 氧化钒薄膜 VO2膜转换特性     

Effect of nonstoichiometry on Raman scattering of VO2 films

We report on Raman scattering of VO2 films prepared by radio frequency magnetron sputtering under different conditions. Our investigations revealed that the dominated Raman peaks shift towards high frequency for both V-rich and O-rich VO2 films, compared with the stoichiometry VO2 films. The experimental evidence is presented and the cause for nonstoichiometry dependence of Raman spectra of VO2 films is discussed.     

新席夫碱吡哆醛缩邻氨基酚的合成及其分析应用研究

本文研究了新席夫碱吡哆醛缩邻氨基酚的合成及其分析应用，提出了钒（Ｖ）的分光光度测定法，该法简便，灵敏，选择性好。     

A comparative XPS and UPS study of VOx layers on mineral TiO2(001)‐anatase supports

Four vanadium oxide layers on mineral TiO₂(001)‐anatase supports with different thickness (3–33 Å) were prepared with reactive d.c. magnetron sputtering and were extensively studied with photoelectron spectroscopy. Al Kα radiation and 150 eV synchrotron radiation were used as excitation sources. The evolution of the 2p, 3s and 3p core level line shapes of V and Ti as a function of the vanadium oxide thickness was studied, as well as the O1s and O2s core lines and the valence band. All the V2p spectra of the deposited vanadium oxide layers consist of at least 60% V⁵⁺, the rest being V⁴⁺. The V3p region is complicated by multiplet splitting, which prevents the determination of the vanadium oxidation state. The V3p multiplet splitting is different for the two excitation energies. No reduction of the titania support surface due to the vanadium oxide deposition was observed. Copyright © 2006 John Wiley & Sons, Ltd.     

Synthesis in solid state, structural regularity and reaction mechanism for [VS_4-Cu_n] clusters

The reaction system (NH4)3VS4/CuCl/PPh3/Et4NBr afforded a series of [VS4-Cun] dusters with various core configurations in the solid state at low heating temperature. The structural regularity of [VS4-Cun] dusters and the influence of the CuCl:(NH4)3VS4 ratio as well as that of reaction temperature and time on the formation of duster core have been summarized. The reaction mechanism of forming V-Cu-S clusters has also been explored.