Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Studies of photooxidative degradation of poly(vinyl chloride)/poly(ethylene oxide) blends

The photooxidative degradation of blends (in a full range of compositions) of amorphous poly(vinyl chloride) (PVC) with semicrystalline poly(ethylene oxide) (PEO) in the form of thin films is investigated using absorption spectroscopy (UV–visible and Fourier transform infrared) and atomic force microscopy (AFM). The amount of insoluble gel formed as a result of photocrosslinking is estimated gravimetrically. It is found that the PVC/PEO blendsí susceptibility to photooxidative degradation differs from that pure of the components and depends on the blend composition and morphology. Photoreactions such as degradation and oxidation are accelerated whereas dehydrochlorination is retarded in blends. The photocrosslinking efficiency in PVC/PEO blends is higher than in PVC; moreover, PEO is also involved in this process. AFM images showing the lamellar structure of semicrystalline PEO in the blend lead to the conclusion that the presence of PVC does not disturb the crystallization process of PEO. The changes induced by UV irradiation allow the observation of more of the distinct PEO crystallites. This is probably caused by recrystallization of short, more mobile chains in degraded PEO or by partial removal of the less stable amorphous phase from the film surface. These results confirm previous information on the miscibility of PVC with PEO. The mechanism of the interactions between the components and the blend photodegradation are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 585–602, 2004     

多壁碳纳米管膜湿敏特性的研究

研究了多壁碳纳米管(MWNTs)薄膜的湿敏特性，实验所用的多壁碳纳米管是用热灯丝化学气相沉积法(CVD)合成的.分别对未修饰和修饰的多壁碳纳米管膜温度和湿度特性进行研究后发现，修饰的多壁碳纳米管对温度和湿度非常敏感，且对湿度的响应时间和恢复时间短，重复性好.而未修饰的多壁碳纳米管对温度和湿度不太敏感.对修饰多壁碳纳米管的湿敏特性进行了理论分析，给出了其理论表示式. 关键词： 多壁碳纳米管 化学修饰 湿敏特性 物理吸附     

二茂铁在高温热解乙二胺制备CN_x纳米管过程中的催化性能研究

采用高温热解法 ,以二茂铁 乙二胺有机溶剂为前驱液制备CNx 纳米管过程中 ,改变前驱液配比 ,对 86 0℃ ,不同二茂铁含量条件下制备出的CNx 纳米管进行了产量统计、形貌结构观察和拉曼光谱研究。结果显示 :随着前躯液中二茂铁含量的相对增大 ,不但CNx 纳米管产量随之增加 ,而且产物中“竹节状”结构纳米管相对“中空”结构纳米管的比重也增大 ;拉曼光谱结果进一步证实了由于“竹节状”结构CNx 纳米管的含量或比重增加所带来的纳米管样品整体或平均含氮量的升高而导致的样品结晶有序程度的降低。对单独钴粉和二茂铁催化条件下生成CNx 纳米管的形貌观察进一步证实 :二茂铁在热解法制备“竹节状”结构CNx 纳米管过程中的浮动催化作用显著 ,有利于实现含氮量较高、结构均匀的CNx 纳米管的可控制生长。     

Microcalorimetric Adsorption of Alumina Oxide Catalysts for Combination of Ethylbenzene dehydrogenation and carbon Dioxide Shift-reaction

Styrene (STY) is now produced industrially in fairly large quantities by the dehydrogenation of ethylbenzene (EB) using promoted iron oxide catalyst with superheated steam.In this case, small amount of carbon dioxide formed as a by-product was known to inhibit the catalytic activity of commercial catalyst. Recently, there have been some reports which carbon dioxide showed positive effects to promote catalytic activities on the reaction over several catalysts.In this study, we attempted to combine the dehydrogenation of EB to STY with the carbon dioxide shift-reaction. The combine reaction (EB + CO2 → STY + H2O + CO) can be considered as one of the ways of using CO2 resources and can yield simultaneously STY and Carbon oxide.Alumina oxide catalysts such as Al2O3, Na2O/Al2O3 and K2O/Al2O3 were prepared by the usual impregnation method with an aqueous solution of NaNO3 and KNO3, and then calcined at 650℃ for 5 h in a stream of air. The reaction condition is 600℃, flow of CO2 38ml/mon and space velocity (EB) 1.28h-1.     

Hydroxylation-induced modifications of the Al2O3/NiAl(0 0 1) surface at low water vapour pressure

STM, STS, LEED and XPS data for crystalline θ-Al₂O₃ and non-crystalline Al₂O₃ ultra-thin films grown on NiAl(0 0 1) at 1025 K and exposed to water vapour at low pressure (1 × 10⁻⁷-1 × 10⁻⁵ mbar) and room temperature are reported. Water dissociation is observed at low pressure. This reactivity is assigned to the presence of a high density of coordinatively unsaturated cationic sites at the surface of the oxide film. The hydroxyl/hydroxide groups cannot be directly identify by their XPS binding energy, which is interpreted as resulting from the high BE positions of the oxide anions (O_1s signal at 532.5-532.8 eV). However the XPS intensities give evidence of an uptake of oxygen accompanied by an increase of the surface coverage by Al³⁺ cations, and a decrease of the concentration in metallic Al at the alloy interface. A value of ∼2 for the oxygen to aluminium ions surface concentration ratio indicates the formation of an oxy-hydroxide (AlO_xOH_y with x + y ∼ 2) hydroxylation product. STM and LEED show the amorphisation and roughening of the oxide film. At P(H₂O) = 1 × 10⁻⁷ mbar, only the surface of the oxide film is modified, with formation of nodules of ∼2 nm lateral size covering homogeneously the surface. STS shows that essentially the valence band is modified with an increase of the density of states at the band edge. With increasing pressure, hydroxylation is amplified, leading to an increased coverage of the alloy by oxy-hydroxide products and to the formation of larger nodules (∼7 nm) of amorphous oxy-hydroxide. Roughening and loss of the nanostructure indicate a propagation of the reaction that modifies the bulk structure of the oxide film. Amorphisation can be reverted to crystallization by annealing under UHV at 1025 K when the surface of the oxide film has been modified, but not when the bulk structure has been modified.     

Luminescence properties of anodic aluminum oxide films with organic luminophores embedded into pores

Luminescence properties of porous anodic aluminum oxide films formed in a 0.6 M solution of citric acid and luminescence of paraterphenyl, perylene, coumarin 7, and rhodamine 6G dyes adsorbed by the films are investigated. The nature of emitting centers in anodic aluminum oxide is revealed. Intense photoluminescence of all tested dyes embedded into pores of anodic aluminum oxide has been found. A redshift of fluorescence spectra of dyes adsorbed by the matrix and emergence of an additional longwave band have been detected. Data obtained can be used in developing new thin-film luminescent coatings for future applications in optoelectronics and molecular electronics. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 64, No 4, pp. 483–488, July–August, 1997.     

The 2D Rancieite-type manganic acid and its alkali-exchanged derivatives: Part I — Chemical characterization and thermal behavior

The 2D Rancieite type manganic acid was prepared by reduction of KMnO₄ in acidic medium. Its ion exchange behavior allows to prepare alkali derivatives. All compounds were characterized with use of a combination of X-ray diffraction, chemical analyses, TGA, magnetic measurements and spectroscopic techniques. The evolution of their chemical composition versus temperature was studied between 180 and 400 °C. It shows that the dehydration process is partly reversible in these compounds whereas the weak reduction is irreversible. The 2D Rancieite-type manganic acid is readily different from a Birnessite-type phyllomanganate, as shown by several features: the interlayer distance, the ion exchange capacity, the thermal behavior, the interlayer cation content, the manganese average oxidation state, the magnetic behavior and the IR spectrum.     

Heat-treatment studies of molybdenum oxide-monohydrate

The dehydration of molybdic acid, MoO₃---H₂O, was studied by thermal analysis, X-ray diffractometry and FTIR spectroscopy. The results show that an intermediate phase, MoO₃-2/3H₂O is formed at 216 °C and the monoclinic form of MoO₃ is grown above 350 °C. The mechanism of dehydration and structural rearrangement were confirmed by the features of the infrared spectra showing formation of corner-shared MoO₆ octahedra.