Preparation of micron-sized nonspherical polystyrene/poly(styrene-<Emphasis Type="Italic">co</Emphasis>-ethyleneglycol dimethacrylate) particles by seeded soap-free emulsion polymerization

Micron-sized nonspherical polymer particles having different morphologies were synthesized by seeded soap-free emulsion polymerization of styrene(St) and ethyleneglycol dimethacrylate(EGDMA,used as a crosslinker) on spherical, linear polystyrene(PS) seed particles.The morphology of the resulting PS/poly(St-co-EGDMA) particles was dependent on the crosslinker concentration and polymerization temperature.     

不同尺寸单分散PMMA/GMA/DVB聚合物荧光微球的制备

采用无皂乳液聚合及种子无皂乳液聚合方法制备了200～800 nm四种不同尺寸的单分散PMMA/GMA/DVB (PMGD)复合微球. 用扫描电镜(SEM)和动态光散射(DLS)对粒径尺寸、形貌进行了表征. 实验发现单体滴加速度是影响种子无皂乳液聚合过程二次成核的关键因素. 用乙二胺对微球表面的环氧基团开环后, 通过在微球表面接枝树枝状PAMAM (d-PAMAM)达到微球表面的官能化的目的, 元素分析和红外光谱实验证明了微球表面d-PAMAM的存在. 最后利用微球表面的活性氨基与四甲基异硫氰酸罗丹明(TRITC)反应, 得到四种尺寸的水分散性的红色荧光微球.     

Poly(2-acetoxyethyl methacrylate)/polystyrene latex interpenetrating polymer networks with well-defined phase-separated structure

A series of poly(2-acetoxyethyl methacrylate)/polystyrene(PAEMA/PS) latex interpenetrating polymer networks(LIPNs) were prepared by seeded soap-free emulsion polymerization of styrene on the crosslinked PAEMA seed particles using an oil-soluble initiator.These PAEMA/PS LIPNs showed a well-defined phase-separated structure with PS phase dispersing in continuous PAEMA phase.The domain size of PS phase was found to depend on the crosslinking degree of PAEMA seed particles and the amount of second-stage styrene monomer.     

苯乙烯-甲基丙烯酸羟乙酯无皂乳液聚合过程

苯乙烯-甲基丙烯酸羟乙酯无皂乳液聚合过程;成核机理     

无皂乳液聚合制备硅铝氧烷/PMMA复合体系

硅铝氧烷溶胶;聚甲基丙烯酸甲酯复合体系;无皂乳液聚合制备硅铝氧烷/PMMA复合体系     

聚合工艺及m(MMA)/m(EA)对MMA-Ea-AA三元无皂乳液聚合及乳胶粒性质的影响

聚合工艺及m(MMA)/m(EA)对MMA-Ea-AA三元无皂乳液聚合及乳胶粒性质的影响;甲基丙烯酸甲酯;丙烯酸乙酯     

自交联型含氟丙烯酸酯共聚物的合成与表征

含氟丙烯酸酯;自交联;无皂乳液;接触角滞后     

含稀土铕双功能荧光磁性纳米粒子的制备及性能表征

首先制备了油酸和十一烯酸钠改性的水基磁流体,然后在其存在的情况下,将可聚合的稀土铕配合物单体Eu(AA)3Phen(AA=丙烯酸,phen=邻菲罗啉)与苯乙烯和甲基丙烯酸缩水甘油酯在过硫酸钾的引发下,进行无皂种子乳液聚合来制备荧光磁性高分子微球。 利用透射电子显微镜和动态光散射粒度仪表征了粒子的形貌及粒径,发现荧光磁性微球具有明显的核-壳结构及较窄的粒径分布;通过红外光谱和X射线衍射分析表征了粒子的化学及晶体结构;通过振动样品磁强计和荧光分光光度计表征粒子的磁性及荧光性能,发现荧光磁性微球具有超顺磁性,其荧光发射光谱在594和619 nm处出现Eu3+的特征荧光发射峰。     

无皂乳液聚合法制备Fe3O4@P(St-GMA)复合微球

用化学共沉淀法制备了磁性四氧化三铁纳米粒子. 在油酸和氨水的作用下, 使之分散在水中, 得到了水分散的磁流体. 在水基磁流体的存在下, 进行苯乙烯和甲基丙烯酸缩水甘油酯(GMA)的无皂乳液共聚合, 得到了Fe₃O₄@P(St-GMA)复合微球. 综合考察了反应温度、磁流体和单体的用量、引发剂的用量对聚合转化率的影响, 并用TEM, TGA和VSM对磁性复合微球进行了表征.