反应性复合乳液的合成、表征及其交联反应

利用种子半连续乳液聚合方法合成了核层或壳层带有环氧基以及壳层带有羧基的3种不同核/壳结构的乳胶粒子,通过物理共混带环氧基和羧基的乳胶粒子,得到了两种反应性复合乳液.利用透射电镜和激光动态光散射对乳胶粒子进行了表征,其粒径分布较窄,粒径分布的多分散系数为0.062,平均粒径约76 nm,乳胶粒子具有明显的核/壳结构.通过胶膜的凝胶率和膨胀率的测定和红外光谱分析对反应性复合乳液中乳胶粒子的扩散及交联反应进行了研究,并探讨了不同核壳结构复合乳液对涂膜机械性能的影响.研究表明,当反应性复合乳液中的环氧基和羧基分别分布在乳胶粒子的核层和壳层时,有利于聚合物分子链的充分扩散和化学交联反应的进行,从而提高涂膜的物理化学性能,当甲基丙烯酸缩水甘油酯(GMA)含量为10 wt%时,涂膜的拉伸强度达20.3 MPa.     

Use of α‐diketones as visible photoinitiators for the photocrosslinking of waterborne latex paints

The efficiency of several α‐diketones as visible light photoinitiators for the crosslinking of waterborne latex dispersions in the presence of acrylic monomers was evaluated. Among the eight α‐diketones studied, camphorquinone allows the fastest curing speed, and the curing of the acrylic waterborne coating is not affected by the presence of oxygen. The properties of the sunlight‐cured volatile organic compound (VOC)‐free pigmented paints prepared from the waterborne latex are as good or better than the equivalent conventional paint containing VOCs. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3171–3181, 2002     

混合溶剂对磺化聚苯乙烯水基微乳液体系形态的影响

利用相反转技术制备磺化聚苯乙烯(SPS)水基微乳液,研究发现,通过选择溶剂和控制混合溶剂的组成,可制备不同颗粒形态结构的SPS水基微乳液,并研究了相反转过程、乳液稳定性与混合溶剂组成之间的关系。     

聚苯乙烯乳胶球三维有序体的制备及其显微形貌表征

A three-dimensional (3D) ordered structure was achieved by self-organization of monodisperse polystyrene latex about 250nm in diameter after being ambient dried. The stacked morphology was investigated by scanning electron microscopy(SEM) observation. It is shown that the face-centered cubic(FCC) phase dominantly exists. This finding presents a potential template for preparing an inverse FCC structure as a photonic crystal of full band gap if the index contrast is higher than 2.8.     

含羧基/环氧树脂的丙烯酸酯共聚物乳液的制备和交联——1.含羧基丙烯酸酯共聚物乳液的分子设计和制备

以在低温下(<100℃)实现含羧基/环氧树脂的丙烯酸酯共聚物乳液的交联固化为目的,进行了分子设计;估算了共聚物的组成,用碱滴定法测定了乳胶粒表面的羧基数,并比较了不同单体配比所得乳液的成膜性能.     

Prevulcanisation of skim latex: morphology and its use in natural rubber based composite material

The prevulcanisation of skim latex, a by-product of field natural rubber (NR) latex concentrated by centrifugation, using sulphur and peroxide systems was investigated. Compared to the peroxide prevulcanisation, the lower swelling ratio of film casted from sulphur-prevulcanised skim (SPVS) latex was observed. The latter was then employed for preparation of NR/SPVS core–shell particles by using heterocoagulation technique whose driving force was an interpolymer complex between poly(ethylene oxide) (PEO) moieties of a non-ionic surfactant (Nonidet) adsorbed on small SPVS particles and the indigenous surfactant (protein–lipid) on a large NR particle. The value of zeta potential of heterocoagulated particle and the better oil resistance of films casted from the composite latex when compared to that of the NR film revealed the NR/SPVS core–shell structure.     

Polymer dispersions from catalytic polymerization in aqueous systems

By contrast to traditional free radical emulsion polymerization, catalytic polymerization allows for polymer microstructure control. In terms of polymerizable monomers, both techniques are largely complementary. Since the beginning of this decade, an increasing number of reports on polyolefin, polybutadiene, polyalkenamer, polynorbornene, polyketone, and polyacetylene dispersions prepared by catalytic polymerization in disperse aqueous systems has appeared. This contribution reviews the preparation of these dispersions, their colloidal properties, particle formation mechanisms, particle morphologies, and polymer microstructures.     

Preparation of multihollow P(St-MAA) particles by sequence soap-free/soap emulsion polymerization and followed by stepwise alkali/acid posttreatment

The effects of ionic emulsifier, sodium dodecylbenzene sulfate (SDBS), on the formation of the multihollow structures in sub-micron sized polymer particles produced by alkali/acid posttreatment were investigated. The original latex particles with narrow size distribution were synthesized by a new sequence emulsifier-free/emulsifier emulsion copolymerization of styrene (St) and methacrylic acid (MAA). Results indicated that the pore size decreased and the pore number increased with the increase of SDBS amount, and the morphology of the posttreated latex particles was also significantly influenced by the introducing time of SDBS in the preparation of the original latex particles, and a suitable introducing time was 3 h of polymerization.     

P(St-co-MAA)乳液体系对CaCO3结晶的调控

大量研究表明, 有机/无机界面上的相互作用[1]是控制无机结晶的晶型、形貌、粒径等特征的决定因素. 本文利用乳液聚合方法合成了在诱导无机矿化后依然保持较为刚性界面的、能与无机离子作用的微球, 并在乳液中进行碳酸钙结晶实验, 用XRD, FTIR和SEM等手段对结晶进行了表征.     

Dual-Phase structure of polymer electrolytes comprised of NBR/SBR latex films swollen with lithium salt solution

Dual-phase polymer electrolytes (DPE) that have high ionic conductivity (> 10^?3 S/cm) and good mechanical strength were prepared by mixing NBR and SBR latices and casting films. The latex films absorbed large quantities of lithium salt solution (e.g., 1M lithium perchlorate in γ-butyrolactone) to obtain DPE films but did not dissolve with swelling. The NBR phase is polar and was impregnated selectively with the polar lithium salt solution, whereas the SBR phase is nonpolar and formed a mechanically-supportive matrix. Transmission electron microscopic (TEM), electron energy loss spectral (EELS), and energy-dispersive x-ray (EDX) analyses showed microscopically the dual-phase structure. Evidence for swelling by lithium salt solution was found only in the NBR phase and not in the SBR phase by EDX microanalysis. Ionic conductivity as a function of NBR content or swelling degree showed clearly that a percolation threshold for ionic conductivity exists. © 1994 John Wiley & Sons, Inc.