通过电导测量研究了四种钕盐：Nd(CF3SO3)3、Nd(ClO4)3、Nd(NO3)3和NdCl3在极性非质子溶剂DMF中的电导性质.利用线性拟合方法求得在25 ℃下Nd(CF3SO3)3和Nd(ClO4)3的极限摩尔电导率分别为278.8和 280.7 S•cm2•mol－1.用间接方法求得Nd(NO3)3 与NdCl3 的极限摩尔电导率分别为297.2和287.3 S•cm2 •mol－1.在25～65 ℃温度范围内，Nd(CF3SO3)3和Nd(ClO4)3的电导率随温度呈线性变化. Nd(NO3)3和NdCl3的电导行为表现出明显的离子缔合.     

Influence of the texture of chromia catalysts on their activity in synthesis of 2-methylthiophene

The texture of Cr₂O₃-K₂O/Al₂O₃catalysts containing oxides of rare earth elements (REE) was studied. The catalysts are used for the synthesis of 2-methylthiophene by the reaction of H₂S with n-pentane or piperilene. The heterocyclization of n-pentane is a consecutive reaction involving a step of dehydrogenation of initial hydrocarbon. At this step the texture of the catalyst affects the yield of 2-methylthiophene. The yield of 2-methylthiophene obtained from piperilene and I₂S is independent of the catalyst texture.     

Elevated-temperature metathesis syntheses of structurally novel alkali-metal tetrakis(3,5-di-tert-butylpyrazolato)lanthanoidate(III) complexes: toluene-coordinated discrete bimetallic complexes and supramolecular chains

Sodium and potassium tetrakis(3,5-di-tert-butylpyrazolato)lanthanoidate(III) complexes [M[Ln(tBu(2)pz)(4)]] have been prepared by reaction of anhydrous lanthanoid trihalides with alkali metal 3,5-di-tert-butylpyrazolates at 200-300 degrees C, and a 1,2,4,5-tetramethylbenzene flux for M=K. On extraction with toluene (or occasionally directly from the reaction tube) the following complexes were isolated: [Na(PhMe)[Ln(tBu(2)pz)(4)]] (1 Ln; 1 Ln=1 Tb, 1 Ho, 1 Er, 1 Yb), [K(PhMe)[Ln(tBu(2)pz)(4)]].2 PhMe (2 Ln; 2 Ln=2 La, 2 Sm, 2 Tb, 2 Ho, 2 Yb, 2 Lu), [Na[Ln(tBu(2)pz)(4)]](n) (3 Ln; 3 Ln=3 La, 3 Tb, 3 Ho, 3 Er, 3 Yb), [K[Ln(tBu(2)pz)(4)]](n) (4 Ln; 4 Ln=4 La, 4 Nd, 4 Sm, 4 Tb, 4 Ho, 4 Er, 4 Yb, 4 Lu), with the last two classes generally being obtained by loss of toluene from 1 Ln or 2 Ln, and [Na(tBu(2)pzH)[Ln(tBu(2)pz)(4)]].PhMe (5 Ln; 5 Ln=5 Nd, 5 Er, 5 Yb). Extraction with 1,2-dimethoxyethane (DME) after isolation of 2 Ho yielded [K(dme)[Ho(tBu(2)pz)(4)]] (6 Ho). X-ray crystal structures of 1 Ln (=1 Tb, 1 Ho; P2(1)/c), 2 Ln (=2 La, 2 Sm, 2 Tb, 2 Yb, 2 Lu; Pnma), 3,4 Ln (=3 La, 3 Er, 4 Sm; P2(1)/m), and 5 Ln (=5 Nd, 5 Er, and 5 Yb; P1) show each group to be isomorphous regardless of the size of the Ln(3+) ion. All complexes contain eight-coordinate [Ln(eta(2)-tBu(2)pz)(4)] units. These are further linked to the alkali metal by bridging through two (1,2,5 Ln) or three (3,4 Ln) tBu(2)pz groups which show striking coordination versatility. Sodium is coordinated by an eta(4)-PhMe, a micro-eta(2):eta(2)-tBu(2)pz, and a micro-eta(4)(Na):eta(2)(Ln)-tBu(2)pz ligand in 1 Ln, and by one eta(1)-tBu(2)pzH and two micro-eta(3)(Na):eta(2)(Ln) ligands in 5 Ln. By contrast, potassium has one eta(6)-PhMe and two micro-eta(5)(K):eta(2)(Ln) ligands in 2 Ln. Classes 3,4 Ln form polymeric chains with the alkali metal bonded by two micro-eta(3)(NNC-M):eta(2)(Ln)-tBu(2)pz ligands within [MLn(tBu(2)pz)(4)] units which are joined together by eta(1)(C)-tBu(2)pz-Na, K linkages.     

Ti-47Al-1.2Ce合金显微组织及稀土相

ＴｉＡ1金属间化合物以其低密度 ,高比强度和比弹性模量 ,良好的抗蠕变及抗氧化能力等特点 ,已成为航天、航空、能源及汽车工业极具竞争力的高温结构材料。虽然ＴｉＡｌ基合金有众多优点 ,但仍存在室温塑性较低、成形性差、性能不平衡等问题 ,还需要深入研究ＴｉＡｌ基合金的合金化及制备工艺等方面技术 ,以此来控制并改善合金的显微组织 ,提高ＴｉＡｌ基合金的综合性能[1～ 4 ] 。合金化是改善ＴｉＡｌ基合金显微组织和性能的重要途径之一 ,通常添加的合金元素有Ｖ ,Ｃｒ ,Ｎｂ ,Ｗ ,Ｍｏ ,Ｓｉ ,Ｂ等[5～ 7] 。稀土元素一般被用来细化材料…     

新疆阿克提什坎金矿床稀土元素地球化学研究

研究了新疆阿尔泰特地区阿克提什坎金矿床的稀土元素及矿区二长花岗岩平衡的热液中稀土元素的组成特征及配分模型，并应用Grang等位线方法讨论了热液蚀变作用过程中稀土元素的行为。研究表明，在热液蚀变作用过程中，稀土元素保持惰性，成矿热液与岩浆热液关系不大，成矿物质主要来源于围岩。     

负载稀土型酸活化膨润土的酯化催化活性

负载稀土型酸活化膨润土的酯化催化活性李永绣，冯天泽，胡平贵，何小彬，辜子英，廖荣辉（南昌大学化学系南昌３３００４７）关键词稀土，膨润土，催化酯化可用稀土、膨润土单独作酯化催化剂，但活性不高［１～３］。本文将稀土用离子交换的方法负载到酸活化膨润土中，寻...     

醇盐法制备稀土化合物超微粉末

稀土元素具有广泛的用途,在大多数的应用中其效果都与原料的纯度、粒度、粒经分布范围等因素有关。由于超微粉末的比表面积大、化学活性高,因此可以预料,若将稀土化合物制成超微粉末,会使它的催化性能及在各种材料中的性能有明显的改变,也可使稀土有新的、更高的应用价值。     

钇对Ti-1100高温钛合金热稳定性和蠕变行为的影响

量了Ｔｉ１１００和Ｔｉ１１００／０１％Ｙ（质量分数）高温钛合金在６００℃／１００ｈ空气中暴露后的拉伸性能及在６００℃／１５０ＭＰａ／１００ｈ条件下的蠕变性能，利用透射电镜观察了合金室温及蠕变后的组织。结果表明，Ｔｉ１１００合金加入０１％的Ｙ后，由于原始β晶粒得到细化，明显改善了其热稳定性；固溶在基体中的硅原子阻碍位错滑移和攀移，使蠕变中的回复过程难于实现；稀土还抑制α２相的长大，所形成的氧化物也阻碍位错的运动。这些均有利于提高Ｔｉ１１００合金的抗蠕变性能。     

π－烯丙基稀土配合物的合成、结构及其催化烯烃聚合反应机理的研究 Ⅲ．LiLn（π－C_3H_5）_4·nD催化异戊二烯和苯乙烯均聚合反应的研究

本文研究了ＬｉＬｎ（π－Ｃ_３Ｈ_５）_４·ｎＤ（Ｌｎ＝Ｌａ、Ｔｂ，ｎ＝３；Ｌｎ＝Ｃｅ、Ｐｒ、Ｎｄ、Ｓｍ、Ｇｄ、Ｅｒ，ｎ＝２；Ｌｎ＝Ｙ、Ｄｙ，ｎ＝２．５；Ｄ为二氧六环）催化异戊二烯和苯乙烯的均聚合反应．其中，钇配合物的催化活性为最高．聚异戊二烯顺式－１，４链节含量在４３－８１％．聚合体系内少量给电子体的加入使聚合物中３，４－链节含量高达８４％．所得聚苯乙烯为无规结构．     

稀土锰氧化物La0.7Ca0.3Mn1-xCuxO3低场磁电阻及电传输特性研究

采用溶胶-凝胶法制备了系列多晶CMR材料La0.7Ca0.3Mn1-xCuxO3（x=0%,1%,5%,10%,15%,20%）。在77-350 K温度范围内测量了样品的电阻率及磁电阻大小。实验结果发现：系列样品TC随掺杂量增加而递减;系列样品的电阻率峰及磁电阻峰在整个测温范围内随掺杂量的增加均依次被展宽直至消失,当掺杂量为x≥10%时,电阻率随温度的变化在整个测温范围内呈现绝缘相行为;同时还发现,掺杂量为x≥10%时,样品的磁电阻在整个测温区内基本表现为隧穿磁电阻。基于我们采用蒙特卡罗模拟方法提出的逾渗模型及隧穿磁电阻模型,对样品的磁电阻行为进行了很好的解释。对系列样品的ρ-T曲线进行lnρ-T^-（1/4）系拟合,发现掺杂量为x=10%样品在整个温区内的lnρ-T^-（1/4）系基本呈线性。