Copolymers containing a spiro orthoester moiety that undergo no shrinkage during cationic crosslinking

A spiro orthoester with an exomethylene group (exoSOE) was radically copolymerized with acrylonitrile or vinyl acetate at several feed ratios to obtain the corresponding copolymers having spiro orthoester moieties in the side chain. The obtained copolymers could be crosslinked via the double ring‐opening polymerization of the spiro orthoester moieties in their side chain by a treatment with BF₃OEt₂. The volume changes upon the crosslinking of the copolymers were evaluated by density measurements with a micromeritics gas pycnometer. The copolymers experienced less than 1% volume expansion instead of volume shrinkage during typical cationic crosslinking, regardless of the copolymer compositions. Negligible shrinkage was observed during the thermal cationic crosslinking of a film cast from a nitrobenzene solution of the copolymers containing a benzylthiophenium salt as a thermally latent cationic initiator. The constantly low volume changes during the crosslinking of the copolymers from exoSOE probably depended on the almost zero volume change during the cationic polymerizations of spiro orthoester derivatives. This indicates that exoSOE is an effective monomer for crosslinkable polymers without volume changes. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3666–3673, 2006     

Synthesis of copolymers containing a spiro orthocarbonate moiety and evaluation of the volume change during their cationic crosslinking

Spiro orthocarbonate (SOC) monomers having either an exomethylene group {3,3‐dimethyl‐9‐methylene‐1,5,7,11‐tetraoxaspiro[5.5]undecane (ExoSOC)} or an allyl group {9‐allyl‐3,3‐dimethyl‐1,5,7,11‐tetraoxaspiro[5.5]undecane (AllylSOC)} were radically copolymerized with vinyl monomers at several feed ratios to obtain the corresponding copolymers having SOC moieties in the side chain. The obtained copolymers were crosslinked via the double ring‐opening polymerization of the SOC moieties by a treatment with boron trifluoride etherate. The volume changes during the crosslinking of the copolymers were evaluated by density measurements with a gas pycnometer. As the SOC moiety composition increased, the volume shrinkage during the crosslinking was suppressed, and that finally changed into volume expansion. The volume changes during the crosslinking of the copolymers from AllylSOC were slightly larger than those of the copolymers from ExoSOC. The higher volume expansions in the crosslinking of AllylSOC‐based copolymers were ascribable to the lower steric hindrance around the SOC moieties. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 7040–7053, 2006     

Block copolymer mediated synthesis of amphiphilic gold nanoparticles in water and an aqueous tetrahydrofuran medium: An approach for the preparation of polymer–gold nanocomposites

The synthesis of polymer‐matrix‐compatible amphiphilic gold (Au) nanoparticles with well‐defined triblock polymer poly[2‐(N,N‐dimethylamino)ethyl methacrylate]‐b‐poly(methyl methacrylate)‐b‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate] and diblock polymers poly(methyl methacrylate)‐b‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate], polystyrene‐b‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate], and poly(t‐butyl methacrylate)‐b‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate] in water and in aqueous tetrahydrofuran (tetrahydrofuran/H₂O = 20:1 v/v) at room temperature is reported. All these amphiphilic block copolymers were synthesized with atom transfer radical polymerization. The variations of the position of the plasmon resonance band and the core diameter of such block copolymer functionalized Au particles with the variation of the surface functionality, solvent, and molecular weight of the hydrophobic and hydrophilic parts of the block copolymers were systematically studied. Different types of polymer–Au nanocomposite films [poly(methyl methacrylate)–Au, poly(t‐butyl methacrylate)–Au, polystyrene–Au, poly(vinyl alcohol)–Au, and poly(vinyl pyrrolidone)–Au] were prepared through the blending of appropriate functionalized Au nanoparticles with the respective polymer matrices {e.g., blending poly[2‐(N,N‐dimethylamino)ethyl methacrylate]‐b‐poly(methyl methacrylate)‐b‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate‐stabilized Au with the poly(methyl methacrylate)matrix only}. The compatibility of specific block copolymer modified Au nanoparticles with a specific homopolymer matrix was determined by a combination of ultraviolet–visible spectroscopy, transmission electron microscopy, and differential scanning calorimetry analyses. The facile formation of polymer–Au nanocomposites with a specific block copolymer stabilized Au particle was attributed to the good compatibility of block copolymer coated Au particles with a specific polymer matrix. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1841–1854, 2006     

Effects of the architecture and environment on polymeric molecular assemblies of novel amphiphilic diblock copolynorbornenes with narrow polydispersity via living ring‐opening metathesis polymerization

Diblock copolymers of 5‐(methylphthalimide)bicyclo[2.2.1]hept‐2‐ene (NBMPI) and 1,5‐cyclooctadiene were synthesized by living ring‐opening metathesis polymerization with a well‐defined catalyst {RuCl₂(CHPh)[P(C₆H₁₁)₃]₂}. Unhydrogenated diblock copolymers showed two glass transitions due to poly(NBMPI) and polybutadiene segments, such as two glass‐transition temperatures at ?86.5 and 115.3 °C for poly 1a and ?87.2 and 115.3 °C for poly 1b . However, only one melting temperature could be observed for hydrogenated copolymers, such as 119.8 °C for poly 2a and 121.7 °C for poly 2b . The unhydrogenated diblock copolymer with the longer poly(NBMPI) chain (poly 1a ; temperature at 10% mass loss = 400 °C) exhibited better thermal stability than the one with the shorter poly(NBMPI) chain (poly 1b ; temperature at 10% mass loss = 385 °C). Two kinds of hydrogenated diblock copolymers, poly 2a and poly 2b , exhibited relatively poor solubility but better thermal stability than unhydrogenated diblock copolymers because of the polyethylene segments. Poly[(hydrochloride quaternized 2‐norbornene‐5‐methyleneamine)‐b‐butadiene]‐1 (poly 3a ) was obtained after the hydrolysis and quaternization of poly 1a . Dynamic light scattering measurements indicated that the hydrodynamic diameters of the cationic copolymer (poly 3a ) in water (hydrodynamic diameter = 1580 nm without salt), methanol/water (4/96 v/v; hydrodynamic diameter = 1500 nm without salt), and tetrahydrofuran/water (4/96 v/v; hydrodynamic diameter = 1200 nm without salt) decreased with increasing salt (NaCl) concentration. The effect of temperature on the hydrodynamic diameter of hydrophobically modified poly 3a was also studied. The inflection point of the hydrodynamic diameter of poly 3a was observed at various polymer concentrations around 30 °C. The critical micelle concentration of hydrophobically modified poly 3a was observed at 0.018 g dL^?1. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2901–2911, 2006     

Electrical properties of polypyrrole/p‐InP structure

The polypyrrole/p‐InP structure has been fabricated by the electrochemical polymerization of the organic polypyrrole onto the p‐InP substrate. The current–voltage (I–V), capacitance–voltage (C–V), and capacitance–frequency (C–f) characteristics of the PPy/p‐InP structure have been determined at room temperature. The structure showed nonideal I–V behavior with the ideality factor and the barrier height 1.48 and 0.69 eV respectively. C–f measurements of the structure have been carried out using the Schottky capacitance spectroscopy technique and it has been seen that there is a good agreement between the experimental and theoretical values. Also, it has been seen that capacitance almost show a plateau up to a certain value of frequency, after which, the capacitance decreases. The higher values of capacitance at low frequencies were attributed to the excess capacitance resulting from the interface states in equilibrium with the p‐InP that can follow the a.c. signal. The interface state density N_ss and relaxation time τ of the structure were determined from C–f characteristics. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1572–1579, 2006     

The response of microstructure to processing in a series of poly(siloxaneimide) copolymers

Poly(siloxaneimide) (PSI) segmented copolymers exhibit organized microdomains if the blocks are sufficiently incompatible. As with neat diblock and triblock copolymers, the processing route employed to prepare films of PSI materials is expected to influence the dimensions and/or morphology of the resultant microstructure. In this work, small-angle neutron scattering (SANS) is utilized to characterize the disordered microstructure found in films of a series of PSI copolymers which are subjected to solvent casting and various thermal treatments. Microstructural dimensions such as the periodicity and correlation length are deduced from the Teubner-Strey (TS) model for disordered microemulsions. The scattering intensity of each copolymer up to q = 5.0 nm^?1, where q is the scattering vector, is found to scale as q^?2.8+?0.1. Results indicate that processing the materials as cast films or as melt-pressed films allowed to cool slowly has a small, but discernible, effect on microstructural characteristics. SANS profiles of films quenched from elevated temperatures reveal a clear transition in microdomain periodicity, which correlates well with the glass transition temperature of the imide microphase in these and other materials of similar chemical structure. © 1993 John Wiley & Sons, Inc.     

Partial molal heat capacities of aqueous tetraalkylammonium bromides as functions of temperature

Enthalpies of solution have been measured from 5 to 85°C for aqueous tetraethyl- and tetrapropylammonium bromides, and the integral heat method is employed to evaluate for these electrolytes over a wide temperature range. Data taken from the literature have been used to evaluate for aqueous Bu₄NBr over a similar temperature range. These data, along with similar data for Me₄NBr, previously reported, have been used to evaluate absolute ionic heat capacities. While the absolute values agree only qualitatively with two other methods of division, the temperature dependences of the three methods essentially agree up to 65°C. Heat capacities due to structural effects on the solvent, obtained by subtracting the inherent heat capacities of the ions, are extraordinarily positive for all four tetraalkylammonium ions and have negative temperature coefficients, indicating that all four ions, including the tetramethylammonium ion, are structure-making ions.     

Zircon SHRIMP age of Mesoarchaean meta-argilloarenaceous rock in the Anshan area and its geological significance

In order to better understand the early continental evolution of the Anshan area, one ofthe typical Precambrian distribution areas of the North China Craton, the geochronology and REEcomposition of the zircons from the meta-argillo-arenaceous rock occurred as enclave in 3.1 GaLishan trondhjemite are studied by using SHRIMP ll ion microprobe. It is indicated that the Pa-leoarchaean is a very important continental formation period in the Anshan area and 3.2 Ga can beregarded as the boundary between the Paleoarchaean and Mesoarchaean.     

Freezing temperatures and densities of solutions of some hydrocarbons and sodium oleate inN-methylacetamide. Evidence for a solvophobic interaction

The freezing temperatures and densities (at 31°C) of solutions of octane, nonane, decane, 3,3-diethylpentane, and sodium oleate inN-methylacetamide (NMA) have been measured. The molality of the freezing solution was calculated from the density. The solubilities of octane, nonane, and decane inN-methylacetamide are also reported. Apparent molal volumes calculated from the densities are close to the values in the pure hydrocarbons and are not strong functions of the concentration. This indicates the absence of any unusual packing effect. The calculated free energies of transfer of the hydrocarbons from pure hydrocarbon to NMA solution are much less negative than the corresponding values for water, showing that the bulk solvophobic interaction inN-methylacetamide is smaller than in water. This is consistent with the freezing temperatures of sodium oleate which show that micelles do not form below 0.1 mole-kg^–1. The osmotic coefficients of the hydrocarbons calculated from the freezing temperatures showed negative deviations from ideality that were larger for the hydrocarbons with the higher molecular weights. Two estimates of the pairwise solvophobic interaction inN-methylacetamide indicate that it is also smaller than in water. The solvophobic effect in this solvent does not include the large entropy and enthalpy effects found in aqueous solutions.     

Solid state reactions of nitrogenous heterocyclic compounds(Ⅰ)——Solid state reactions of 3-methyl-l-phenyl-5-pyrazolone with carbonyl compounds

The solid state reaction of 3-methyl-1-phenyl-5-pyrazolone (MPP) with aromatic aldehydes and ke-tones benzil derivatives and imides,and the solid state Michael addition reaction of MPP with 4-arylidene-3-methyl-1-phenyl-5-pyrnzolone 2 were investigated.Some new solid state reactions between the reactants were found,from which a series of new compounds were obtained The structures of the products were identified by IR,1H NMR,MS,elemental analyses and also by X-ray crystal analysis,and the reaction mechanism of MPP with aromatic aldehydes and ketones was proposed