Cation identity dependence of crown ether photonic crystal Pb<Superscript>2+</Superscript> sensing

We quantitatively modeled the volume phase transition of a hydrogel containing a crystalline colloidal array with a crown ether ligand which binds Pb²⁺. The hydrogel volume response and the wavelength diffracted depend on the Pb²⁺ concentration and on both the ionic strength and the valence of the nonbinding ionic species. We successfully modeled the response of this hydrogel Pb²⁺ sensor to ionic strength and the cation valence of the added salts. Figure Cation identity dependence of crown ether photonic crystal Pb⁺ sensing     

STUDY ON THE PROPERTIES OF BLEND OF NATURAL RUBBER LATEX/METHYL METHACRYLATE GRAFTED RUBBER LATEX BY GAMMA RADIATION

Natural rubber latex(NRL)and methyl methacrylate(MMA)grafted rubber latex were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature.The tensile properties, swelling ratio and permanent set were measured.The maximum tensile strength and modulus at 500% elongation were obtained at an absorbed dose of 8 kGy.Modulus increases from 6.99 MPa to 9.87 MPa for an increase in proportion of MMA grafted rubber from 40% to 60% in the blend at similar absorbed dose.Elongation at break and swelling ratio decrease with increasing absorbed dose as well as the MMA grafted rubber content in the blends.The decreasing trend of permanent set is high up to 5 kGy absorbed dose,and beyond that dose,it becomes almost flat.     

聚乙烯醇硫酸钾水凝胶电机械化学行为研究

通过将交联聚乙烯醇硫酸酯化的方法制备了一种新型电刺激响应性聚乙烯醇硫酸钾(PVSK)智能水凝胶,并探讨了溶液离子强度和pH对PVSK水凝胶的溶胀吸水率、机械性能以及电机械化学行为的影响.结果表明,制备的PVSK水凝胶的平衡溶胀比随NaCl溶液离子强度的增大而减小,在pH2.39～10.83范围内基本不受溶液pH的影响;经不同离子强度和pH的NaCl溶液充分溶胀的PVSK水凝胶具有良好的机械性能,在非接触的直流电场作用下,该水凝胶向电场负极弯曲,凝胶的弯曲速度和弯曲偏转量随外加电场强度的增加而增大,随NaCl溶液离子强度的增大出现临界最大值,但不随溶液pH(2.08～10.53)的改变而改变;在循环电场作用下,PVSK水凝胶的电机械化学行为具有良好的可逆性.     

低温液相合成甲醇及甲酸甲酯用Cu-Cr-M-O催化剂的制备与表征

采用共沉淀法和配合物沉淀法制备了分别添加Ｂａ, Ｍｎ,Ｖ,Ｂｉ,Ｎｉ 和Ｚｎ 的ＣｕＣｒＭＯ三组分催化剂,采用ＢＥＴ,ＸＲＤ和ＴＥＭ 对催化剂进行了表征,并考察了其对合成甲醇及甲酸甲酯反应的活性及选择性． 结果表明,添加第三种金属使催化剂的稳定性及甲酸甲酯选择性有所提高,但使催化活性有所下降． 配合物沉淀法制备的催化剂的比表面积较大,粒径较小． 热分解温度越高,催化剂的比表面积越小． 除ＣｕＣｒＶＯ 催化剂为纳米非晶态之外,其它催化剂均呈晶态． 催化剂的最小平均粒径为３８ ｎｍ , 最大平均粒径为６８ ｎｍ , 属纳米级催化剂．     

用硝酸银溶液沉淀及分步沉淀卤素离子的数字化实验研究*

卤化银难溶电解质的沉淀溶解平衡是中学化学教学的重要知识点。应用本项目组研制的MXLab21先进数字化实验系统,结合银硫离子电极,测定AgNO₃溶液沉淀Cl^-,Br^-,I^-及其混合离子的沉淀曲线,即电动势(E)随AgNO₃溶液体积(V)变化的关系曲线。3种单一离子的沉淀曲线可以直观体现出滴定的电动势突跃范围与相应沉淀的溶度积大小的关系及其规律性变化。通过混合离子的沉淀曲线分析3种离子两两混合或3者混合时分步沉淀的可行性。Cl^-,Br^-,I^-的沉淀及分步沉淀的动态E-V曲线的建立,对中学化学教学具有重要作用,对化学学科核心素养的发展和培养具有重要价值。     

Influence of Carbon Nanotubes on Phase Composition,Thermal and Post-Heating Behavior of Cementitious Composites

This paper experimentally investigates the influence of carbon nanotubes (CNTs) on phase composition, microstructure deterioration, thermal behavior, and residual mechanical strengths of cementitious composites exposed to elevated temperatures. Cement mortars with small dosages of CNTs, 0.05% and 0.2% by weight of cement, were prepared and then heated at 25 °C, 150 °C, 200 °C, 450 °C, and 600 °C for two hours before being tested. The results show positive impact of the CNTs on the hydration process of cement mortar at room temperature and at higher temperatures up to 200 °C. Decomposition of the hydration products is obvious at 450 °C, whereas sever deterioration in the microstructure occurs at 600 °C. The nano reinforcement and bridging effect of the CNTs are obvious up to 450 °C. Thermal behavior characterization shows that CNTs incorporation enhances the thermal conductivity of the unheated and heat-treated mortar specimens. The decomposition of the hydration products needs more heat in the presence of CNTs. Finally, presence of CNTs significantly enhances the residual compressive and flexural strengths of heated mortar specimens for all studied temperatures.     

钛及钛合金表面羟基磷灰石涂层结合强度及稳定性

钛(Ti)及其合金凭借优异的机械性能和良好的生物相容性,一直是骨和牙种植体的主要临床应用材料。由于钛及其合金自身的生物惰性,不易与周围骨组织进行快速的骨整合,因此其表面的生物活性有待进一步提高。羟基磷灰石(HA)是人体骨和牙齿的主要无机成分,具有良好的生物活性和生物相容性,受其力学性能的制约,常被作为涂层材料覆盖在钛基体表面,用以提高植入体的生物活性。但一直存在涂层与基体界面结合强度低和涂层力学稳定性差的问题,成为限制其临床广泛应用的主要因素。本文从涂层结构设计、成分设计及制备方法等方面,就国内外改善钛基底与HA涂层界面结合性能的研究现状和发展动态作一综述,为高性能钛植入体的制备和应用提供参考。     

丙烯酸水溶液聚合法制备PTFE/PAA/Nafion膜及其性能

采用廉价的多孔聚四氟乙烯(PTFE)膜作为基底, 用少量的Nafion与PTFE膜复合可制备低成本的质子膜. 但疏水性的PTFE膜与亲水性的Nafion膜结合性不佳. 基于此, 本文对疏水性的PTFE膜材料表面进行设计, 先采用丙烯酸对疏水性的PTFE膜表面进行亲水性改性, 再喷涂亲水性Nafion膜, 完成低成本PTFE/PAA/Nafion膜的制备. 实验结果表明, 改性前的PTFE膜材料水接触角为150°, 改性后的膜接触角变为55.6°, 亲水性大幅上升, 膜的机械强度和尺寸稳定性(断裂强度为25.2 MPa, 80 ℃下的溶胀率为11.9%)均优于Nafion117膜, 而 Nafion用量则节省了60%. PTFE/PAA/Nafion膜具有高质子导通率(80 ℃下达到131.9 mS/cm), 接近于Nafion117膜, 最大功率密度可以达到404.2 mW/cm².     

防覆冰涂层构建机理及制备

航空、通信、电力和运输设备的覆冰现象给人们的生产、生活带来许多不便,甚至引起重大经济损失,防覆冰涂层主要通过材料表面特殊物理化学性能与微相形貌来实现抗冰目的,这类材料需要兼具防结冰性和疏冰性,从延长结冰时间和降低冰的附着力两方面来减轻甚至消除冰雪积聚,是目前研究的热点。本文从防覆冰机理入手,深入探讨了防结冰性和疏冰性的影响因素,阐述了防覆冰涂层材料的设计与制备方面的最新进展,并对防覆冰涂层目前存在的问题与发展方向进行了分析和展望。     

沉淀法高效制备聚多巴胺纳米粒子

为得到分散性和稳定性较好的聚多巴胺纳米粒子,利用“沉淀-再分散法”高效制备了聚多巴胺纳米粒子水分散液。 首先利用溶液氧化法制备了分散在水/乙醇中的聚多巴胺纳米粒子,然后向分散液中加入丙酮使聚多巴胺纳米粒子絮凝。 收集沉降物,用丙酮冲洗并干燥后,加水重新分散得到纯化的聚多巴胺纳米粒子水分散液。 丙酮沉淀法得到的聚多巴胺纳米粒子形貌规整,分散性好,粒径分布在250 nm左右,在水中具有良好的储存稳定性和光热性能,与传统的超速离心提纯法相比,产率可提高57.4%。 此方法为其之后在药物载体及光热治疗等方面的应用研究提供了便利。