An ionothermal synthetic approach to porous polyoxometalate-based metal-organic frameworks

Pretty porous POMs: Ionothermal synthesis was applied to prepare porous POM-based open frameworks. The structural integrity remains unchanged until 300?°C; most importantly, the bulky tetrabutylammonium cations within their nanosized channels can be replaced by transition-metal ions through a cation-exchange process, and subsequent gas adsorption measurements confirm their permanent porosity.     

硼、氮共掺杂多孔碳的制备及其超电容性能

分别以含氮菲咯啉、四硼酸钾和醋酸锌为碳源、活化剂和模板,制备了B、N共掺杂多孔碳(BN-PC),并探究模板质量对BN-PC结构和储电性能的影响。当醋酸锌质量为5g时,所得BN-PC₅中B、N杂原子含量分别为 20.21%、18.29%。电化学测试结果表明,以6 mol·L^-1 KOH为电解液,BN-PC₅电极展现出高的比电容(在0.05 A·g^-1电流密度下为255 F·g^-1)、优异的倍率性能(在20A·g^-1电流密度下为188F·g^-1)和卓越的循环稳定性(在5 A·g^-1的电流密度下循环10 000次比电容保持率为97%)。以3 mol·L^-1 ZnSO₄为电解液,在平均功率密度为56W·kg^-1时,BN-PC₅电容器的能量密度可达27Wh·kg^-1。     

表面键联型TiO2/SiO2固定化催化剂的结构及催化性能

 采用浸渍法制备了表面键联型TiO2／SiO2固定化光催化剂．XRD\r\n,FT－IR,XPS和BET比表面积测定结果表明,TiO2通过Ti－O－Si联结\r\n负载于多孔硅胶的表面,由此提出TiO2／SiO2的结构模型．考察了多孔\r\n硅胶的粒度及氧化钛负载量对催化剂活性的影响．对活性艳红K－2G（\r\nR15）的光催化脱色反应,最佳的光催化剂30％TiO2／SiO2（Ims30）比\r\nB－TiO2粉末的催化速率快3倍．随着载体粒度的减小,催化剂的比表面\r\n积增大,催化活性升高;多孔硅胶不仅起着支持体的作用,而且具有分\r\n散的作用;多孔硅胶具有很好的透光性．经ξ－电位测定,所制备催化\r\n剂的等电点为3．0pH单位,表明催化剂表面呈酸性．     

基于中空多孔金纳米/石墨烯复合纳米材料的葡萄糖氧化酶直接电化学及其生物传感研究

采用溶液相牺牲模板法制备中空多孔金纳米粒子（HPAuNPs）,并将该材料与还原氧化石墨烯（rGO）复合,用于葡萄糖氧化酶（GOx）在玻碳电极（GCE）表面的有效固定,构建GOx/HPAuNPs/rGO/GCE传感界面。利用扫描和透射电镜、X射线光电子能谱、X射线衍射谱、红外光谱及电化学等方法对材料的形貌与结构,GOx的固定化过程,以及传感器的直接电化学和电催化性能进行表征。结果表明,HPAuNPs和rGO的协同作用能有效促进GOx与电极之间的直接电子转移（DET）。基于GOx/HPAuNPs/rGO/GCE对葡萄糖的良好电催化性能,该方法有效实现了对葡萄糖的高灵敏度检测,其电流响应的线性范围为0.05～7.0 mmol/L,检出限（S/N=3）为16μmol/L。该传感器具有良好的选择性、重现性及稳定性,对实际样品血清中血糖的测定结果令人满意,回收率为98.0%～103%,相对标准偏差不大于5.0%。     

3D crumbled MXene for high-performance supercapacitors

MXene materials have recently attracted considerable attention in energy storage application owing to their metallic conductivity, 2D structure and tunable surface terminations. However, the restacking of 2D MXene nanosheets hinders the ion transport and accessibility to the surface, resulting in adverse effect on their electrochemical performances. Here, with the assistance of hexamethylenetetramine (C₆H₁₂N₄), 2D Ti₃C₂T_x MXene nanosheets were fabricated into a 3D architecture with crumbled and porous structure through an electrostatic self-assembly followed by annealing. The resultant 3D structure can expose massive active sites and facilitates the ion transport, which is beneficial for sufficient utilization of the outstanding superiorities of the MXene. Therefore, as a pseudocapacitive material, the 3D crumpled and porous Ti₃C₂T_x MXene shows a gravimetric capacitance of 333 F/g at 1 A/g, and maintains 261 F/g and 132 F/g at ultrahigh current densities of 100 A/g and 1000 A/g, respectively, revealing promising potential for application in supercapacitors.     

氮硫共掺杂多孔碳材料的制备及其在锂硫电池中的应用

锂硫电池因其较高的理论容量和对环境友好等优势被视为极具发展潜力的储能装置,但是多硫化物的穿梭效应极大地限制了锂硫电池的实际应用。本文以葡萄糖为碳源,离子液体为氮源和硫源,KCl和ZnCl₂为模板剂,KOH为活化剂,通过热解工艺合成了氮硫共掺杂多孔碳（NSPC）。XPS和极性吸附实验表明N、S杂原子成功引入并且提高了碳材料对多硫化物的吸附能力,有效缓解多硫化物的穿梭效应,而较高的比表面积（1290.67 m²·g^-1）有助于提高硫负载量。负载70.1wt.%的硫后（S@NSPC）作为锂硫电池的正极材料表现出了良好的电化学性能。在167.5 mA·g^-1的电流密度下S@NSPC的首次放电容量为1229.2 mAh·g^-1,远高于S@PC的861.6 mAh·g^-1,且S@NSPC循环500圈后容量为328.1 mAh·g^-1。当电流密度从3350 mA·g^-1恢复至167.5 mA·g^-1时,可逆容量达到首圈放电比容量的80%,几乎恢复至其初始值。     

柚子皮衍生类蜂窝状碳材料在同步检测重金属离子中的应用

不含金属的碳材料通过廉价且易获得的柚子皮经KOH活化和高温热解获得,该碳材料具有高比表面积(1 055 m~2·g~(-1))和高石墨化程度的类蜂窝状结构。将多孔碳(PAC)材料修饰后的电极作为工作电极,采用阳极溶出伏安法(SWASV)同步检测Cd~(2+)、Pb~(2+)和Cu~(2+)离子,表现出较高的灵敏度、可重复性、稳定性和较低的检测限。研究认为PAC的微孔和中孔可以充当有效的离子传递通道,从而加速离子的扩散并显著提高交换效率,而高的石墨化程度提高了材料的导电性,加速了电子传输。     

Simultaneous determination of levofloxacin and ciprofloxacin in human urine by ionic‐liquid‐based,dual‐template molecularly imprinted coated graphene oxide monolithic solid‐phase extraction

A novel method was developed to simultaneously determine the ciprofloxacin and levofloxacin levels in human urine using an ionic‐liquid‐based, dual‐molecularly imprinted polymer‐coated graphene oxide solid‐phase extraction monolithic column coupled with high‐performance liquid chromatography. The molecularly imprinted monolithic column was prepared using ciprofloxacin and levofloxacin as templates, 1‐vinyl‐3‐ethylimidazolium bromide as the functional monomer, and graphene oxide as the core material. The resulting imprinted monoliths were characterized by scanning electron microscopy and fourier transform‐infrared spectroscopy. The efficiency and capacity of the ionic‐liquid‐based imprinted monolithic column were investigated by varying the synthesis conditions (ciprofloxacin/levofloxacin ratio and template/functional monomer/cross‐linker ratio). The solid‐phase extraction process was optimized by changing the washing and eluting conditions. The results suggested that the proposed ionic‐liquid‐based molecularly imprinted solid‐phase extraction monolithic‐high‐performance liquid chromatography method could separate ciprofloxacin and levofloxacin efficiently and simultaneously from human urine. The mean recoveries of ciprofloxacin and levofloxacin ranged from 89.2 to 93.8 and 86.7 to 94.6%, respectively. The intra‐ and interday relative standard deviation ranged from 0.9 to 3.2 and 0.8 to 2.9%, respectively. Under the optimized conditions, the recoveries of ciprofloxacin and levofloxacin were more than 93.8%.     

Microporosity of a Guanidinium Organodisulfonate Hydrogen‐Bonded Framework

Guanidinium organosulfonates (GSs) are a large and well‐explored archetypal family of hydrogen‐bonded organic host frameworks that have, over the past 25 years, been regarded as nonporous. Reported here is the only example to date of a conventionally microporous GS host phase, namely guanidinium 1,4‐benzenedisulfonate ( p ‐G₂BDS ). p ‐G₂BDS is obtained from its acetone solvate, AcMe@ G₂BDS , by single‐crystal‐to‐single‐crystal (SC‐SC) desolvation, and exhibits a Type I low‐temperature/pressure N₂ sorption isotherm (SA_BET=408.7(2) m² g^?1, 77 K). SC‐SC sorption of N₂, CO₂, Xe, and AcMe by p ‐G₂BDS is explored under various conditions and X‐ray diffraction provides a measurement of the high‐pressure, room temperature Xe and CO₂ sorption isotherms. Though p ‐G₂BDS is formally metastable relative to the “collapsed”, nonporous polymorph, np ‐G₂BDS , a sample of p ‐G₂BDS survived for almost two decades under ambient conditions. np ‐G₂BDS reverts to zCO₂@ p ‐G₂BDS or yXe@ p ‐G₂BDS (y,z=variable) when pressure of CO₂ or Xe, respectively, is applied.     

蟹壳基氮/氧共掺杂多孔炭的原位制备及其超级电容器性能

采用废弃蟹壳为碳源,KOH为活化剂原位制备了氮/氧共掺杂多孔炭,并研究其作为电极材料在超级电容器中的应用。 固定蟹壳与KOH的质量比为5:3,考察了煅烧温度对所得炭材料产率、孔结构和氮氧含量的影响。 结果表明,蟹壳基炭材料的孔结构和氮/氧含量可通过改变煅烧温度调变。 随着煅烧温度从500 ℃上升至700 ℃,多孔炭的比表面积和孔体积逐渐增大,而氮/氧含量随温度升高则降低。 采用循环伏安和恒流充放电对所得材料的电化学性能进行测试。 结果表明,所得多孔炭的电化学性能取决于其孔结构与氮/氧表面性质的协同作用,其中煅烧温度为600 ℃所得的多孔炭比表面积为612 m²/g,氮和氧含量分别为3.53%和32.8%,在50 mA/g的电流密度下比电容达到310 F/g,循环1000次比电容仍然保持95%以上,展现出良好的电化学性能。