Synthesis of novel mesoporous silica spheres with starburst pore canal structure

Novel spherical mesoporous silica materials with uniform diameters and starburst mesopore structures were synthesized by a simple one-step procedure with ethanol as the co-solvent in dilute aqueous solution and their formation mechanism was proposed. The arrangement of the pore canal and the diameter of the sphere could be tailored by altering the concentration of ethanol.     

高效液相色谱法所用大孔硅胶填料的制备

对国产ＧＹＱＧ球形硅胶施加高压水热处理并进行扩孔，制备了用于高效液相色谱法的大孔硅胶填料，考察了扩孔压力，扩孔温度和扩孔时间对平均孔径和比表面积的影响。并将产品日本ＳＩＬ－３００３×１０＾－８ｍ硅胶进行了物理性质和孔分布的对比实验，结果表明ＧＹＱＧ硅胶扩孔后平均孔径为２０～３０ｎｍ接近日本ＳＩＬ－３００３×１０＾－８ｍ硅前平平均孔径２５ｎｍ。display structure     

Mesoporous Titanium-containing Silicas. Synthesis and geometrical characteristics

Mesoporous titanium-containing silicas with TiO₂ contents from 1 up to 70 mol% were prepared. The obtained samples have been characterized by the powder X-ray diffraction data, the diffuse reflectance infrared Fourier transform method, and nitrogen adsorption at 77 K. Specific surface area, total pore volume, distribution pore volume on pore sizes were determined from nitrogen adsorption isotherm for synthesized titanosilicas. This revised version was published online in August 2006 with corrections to the Cover Date.     

Physico-chemical characterization of nanofiltration membranes.

This study presents a methodology for an in-depth characterization of six representative commercial nanofiltration membranes. Laboratory-made polyethersulfone membranes are included for reference. Besides the physical characterization [molecular weight cut-off (MWCO), surface charge, roughness and hydrophobicity], the membranes are also studied for their chemical composition [attenuated total reflectance Fourier spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS)] and porosity [positron annihilation spectroscopy (PAS)]. The chemical characterization indicates that all membranes are composed of at least two different layers. The presence of an additional third layer is proved and studied for membranes with a polyamide top layer. PAS experiments, in combination with FIB (focused ion beam) images, show that these membranes also have a thinner and a less porous skin layer (upper part of the top layer). In the skin layer, two different pore sizes are observed for all commercial membranes: a pore size of 1.25-1.55 angstroms as well as a pore size of 3.20-3.95 angstroms (both depending on the membrane type). Thus, the pore size distribution in nanofiltration membranes is bimodal, in contrast to the generally accepted log-normal distribution. Although the pore sizes are rather similar for all commercial membranes, their pore volume fraction and hence their porosity differ significantly.     

不同环大小分子筛对钼基分子筛催化剂上甲烷无氧芳构化反应的影响

 钼基分子筛催化剂，由于不同分子筛的孔道大小及孔道形状不同\r\n，对甲烷芳构化反应表现出不同的催化性能．具有8元环孔道结构的小\r\n孔ERS－7分子筛没有催化活性，说明甲烷的芳构化反应离不开分子筛孔\r\n道的择形作用，较小的孔道中不能生成苯等芳烃．具有10元环孔道结构\r\n的ZSM－5，ZSM－11和ZRP－1三种分子筛具有较好的催化性能，但由于\r\n其孔道大小及孔道形状的差别在催化行为上表现出一定的差异．具有1\r\n0元环和12元环孔道结构的MCM－22分子筛，尤其对苯等轻芳烃而言，催\r\n化性能最佳．具有12元环孔道结构的JQX－1以及中孔分子筛SBA－15，\r\n虽然具有一定的催化性能，但活性较低．研究结果表明，孔道大小与苯\r\n分子动态直径相近或孔道稍大的分子筛是催化甲烷芳构化反应的良好载\r\n体，孔道过大或过小都不利于苯和萘等芳烃的生成．     

Steam-carbon gasification catalyzed by calcium: Assessment of the porous structure of active carbons from plum stones and synthetic active carbons

A need for an elaboration of the methods for synthesis and characterization of activated carbons with a requisite porous structure has existed for a long time. One of the methods giving possibility for creating controlled mesopore and micropore structures deals with the steam gasification of various carbon materials. In this work the effects of calcium catalyst on the catalytic steam gasification of active carbons from plum stones and porous polymers are presented. Determination of micropores capacity and specific adsorption in mesopores have been performed by means of the _s method, but adsorption on the heterogeneous solids was described by the integral equation with various local isotherms. This equation has been solved by the regularization method. Based on this method the changes in structural parameters of active carbons depending on the amount of calcium catalyst were estimated.Nomenclature d width of slit-like micropore - F(x) distribution function of the half-width - p vapor pressure of sorbate - p/p _N relative pressure - PSAC Plum Stone Active Carbon - average pore radius, nm - S ₁ relative limit of the validity of experimental point on the adsorption isotherm in the computations by means of regularization method - SAC Synthetic Active Carbon - S _BET specific surface area calculated by means of BET method, m²/g - S _mes mesopore surface area, m²/g - S _mic micropore surface area, m²/g - T absolute temperature, K - V _mes sorption capacity of mesopores, cm³/g - V _mic sorption capacity of micropores, cm³/g - V _p sorption capacity of pores, cm³/g - w/w weight in weight concentration - x half-width of slit-like micropore, nm - x ₁ maximum of half-width of micropore slit, nm - average half-width of slit-like micropore, nm - X _min-X _max integration limits of thex Greek Letters Greek Letters variance of average half-width of slit-like micropore, nm² - local relative filling of micropores - total relative filling of micropores     

Properties and Characterization of Modified HZSM—5 Zeolites

Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673K were investigated.The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desortion (TPD) of ammonia.The structure of the samples was characterized by XRD,and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy(SEM).The XRD results show that the modified samples have no novel crystalline phase,indicating a high dispersion of phosphorus and boron species.After treatment,the microporous volume and surface area of the samples markedly decrease,implying the bolockage of the channel.The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type Ⅰ and Ⅳ，and all hysteresis loops resemble the H4-type in the IUPAC classification.The total acidity of the modified samples,determined by pyrldine adsorption IR and TPD of ammonia,decreases in contrast to that of the parent HZSM-5.The conversion of n-heptane over P and B steammodified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.     

3-D-electron microscopy configuration of TMOS wet silica gels prepared by the quick-freeze,deep-etching-rotary-replication technique

Silica gel provides a useful medium for crystal growth; solution growth is confined to pores left free by the polymer during its development. All growth steps depend on the gel structure, which is not completely known for crystal growth conditions. Therefore, a three-dimensional (3-D) visualization has been performed for two TMOS aqueous gels, which are rather fragile: the quick-freeze, deep-etching, rotary-replication method has been applied for sample preparation. An original surface labeling technique has been used for surface recognition. The results concern the distribution of macropores that are responsible for crystal nucleation; micropores whose total volume is larger have not been visualized due to the limits of the method. These results are discussed in comparison with previous data performed by light scattering.     

Characterization of Titania/Silica Gel by Means of Low-Pressure Nitrogen Adsorption

Adsorbents synthesized by grafting of titania onto mesoporous silica gel surfaces at different temperatures were studied by means of nitrogen adsorption–desorption and water desorption. The pore size distribution f(R_p) of titania/silica gel depends on the titania concentration (C_TiO2) and the temperature of titania synthesis. Nonuniformity of TiO₂ phase is maximal at a low C_TiO2 value (3.2 wt.% anatase deposited at 473 K), and two peaks of the fractal dimension distribution f(D) are observed at such a concentration of titania, but at larger C_TiO2 values, only one f(D) peak is seen. More ordered filling of pores and adsorption sites by nitrogen, reflecting in the shape of adsorption energy distributions f(E) at different pressures of adsorbate, is observed for adsorbent with titania (rutile+anatase) grafted on silica gel at a higher temperature (673 K).