The crystallization characteristics of polypropylene and low ethylene content polypropylene copolymer with copolyesters

The crystallization characteristics of polypropylene (PP) and low ethylene content PP copolymers with and without nucleating agents were studied by differential scanning calorimetry (DSC). PP and PP copolymers was blended with three different kinds of co[poly(butylene terephthalate-p-oxybenzoate)] copolyesters, designated B28, B46, and B64, with the copolyester level varying from 5 to 15 wt.%. All samples were prepared by solution blending in hot xylene solvent at 50 °C. The crystallization behavior of samples was then studied by DSC. The results indicate that these three copolyesters accelerate the crystallization rate of PP and PP copolymers in a manner similar to that of a nucleating agent. The acceleration of crystallization rate was most pronounced in these blend systems with a maximum level at 5 wt.% of B28. The observed changes in crystallization behavior are explained by the effect of the composition and the amount of copolyester in the blends.     

导电性聚西佛碱的研究：Ⅰ含硫聚西佛碱的合成,性能及表征

采用对氯苯甲醛和联苯二胺为原料,合成了4,4′-二氯代苄叉联苯胺,发现该化合物具有热致液晶性。利用所合成的二氯代化合物与硫化钠在醋酸锂催化下缩取得得到了含硫聚西佛碱探讨了高分子量含硫聚西佛碱的合成方法。测出该含硫聚西佛碱具有3.4×10~(-11)S/cm本征导电率。使用红外光谱、元素分析等方法表征了所合成的聚合物。     

聚（3—丁基噻吩）电导的热稳定性

研究了导电聚合物聚（３－丁基噻吩）（ＰＢＴ）在大气环境下的导电热稳定性。在室温至２２０℃范围内，测试电导率随时间及温度的变化。ＴＧＡ分析以及化学分析的结果表明：掺杂态的ＰＢＴ大约在１４０℃附近有一转化温度，低于或高于这一转化温度，电导率下降的决定因素各不相同。高于转化温度时，电导率下降的主要原因是反离子和高分子主链的解离，进而发生化学反应，影响了高分子主链的结构。ＸＰＳ测试结果表明：经热处理后的Ｐ     

The recent progress of wide bandgap donor polymers towards non-fullerene organic solar cells

The recent progress of wide bandgap (WBG) donor polymers for non-fullerene polymer solar cells (NF-PSCs) were reviewed in detail, which was classified by D-type and D-A type molecular backbones to discuss the related structure-property correlations and put forward an outlook for future innovations.     

含双键侧基的聚氧乙烯与苯乙烯的接枝共聚物及其产物的性质

由环氧乙烷及烯丙基缩水甘油醚合成含双键侧基的聚氧乙烯用苯乙烯接枝共聚,接枝效率可达50％左右.接枝产物经纯化,用IR及~1H NMR表征.该产物与LiClO_4的络合物有较高的室温导电率,其PEO含量在70％及EO/Li=20/1时,25℃的导电率接近10~(-4)S/cm.此外,该接枝共聚物有较高的乳化能力.在Williamson固液反应中具有良好的相转移催化作用.     

有机金属络合物用于高分子富氧膜的研究进展

本文介绍了能够可逆吸附分子氧的有机金属络合物用于高分子富氧膜的研究进展，以及以双重吸附理论进行的膜的促进输送机理。     

复合Fe2O3纳米粒子的高分子微球的结构表征

近年来，复合有机、无机粒子的高分子微球及其特殊性质越来越引起人们的兴趣与关注［1］．获得有机、无机复合微球的方法很多，如在无机粒子存在下的乳液或无皂乳液聚会[2，3]，通过可聚合的表面活性剂在粒子表面形成胶囊化层[4]以及共沉淀法等[5]．这些无机粒子包括氧化钛、氧化铁、氧化铝及氧化硅等．Haga等[6]增发现包覆在聚合物粒子中的CdS与其本体的光电性质不同；单分散的聚合物微球可以在基片上被组装成二维乃至三维有序的结构[7]．这为信息存储、立体印刷等领域提供了新途径．因此，将无机粒子与聚合物复合成为功能化粒子是一项有…     

一种新型联萘基旋光共轭聚合物的圆二色谱和圆偏振荧光光谱

众所周知 ,聚合物的光电性质依赖于聚合物链的构象和 (或 )组成 ,通过在聚合物上引入手性单元 ,采用圆二色谱 ( CD)和圆偏振荧光光谱 ( CPL)等方法可表征聚合物结构 [1] .近年来 ,由于圆偏振光可用作光数据存储和液晶显示器背景光 [2 ] ,人们开始注重共轭聚合物圆偏振光材料的研究 .共轭聚合物的光致和电致圆偏振光的现象由一种带手性侧链的聚噻吩[3 ] 和一种带手性侧链的聚 (对苯撑乙烯 ) [4 ]产生 ,但它们的圆偏振荧光度 (用不对称因子 glum=2 ( IL-IR) / ( IL+IR)表示 ,IL 和 IR 分别指左圆偏振光强度和右圆偏振光强度 )相对较低 …     

带功能基的全氟烷基乙烯基醚的研究——4.四氟乙烯与全氟-3,6-二氧杂-4-甲基-△~7-辛基磺酰氟溶液共聚反应单体竞聚率的测定

在乙烯-四氟乙烯溶液共聚合体系研究中,我们曾编制了一个简易的计算机程序,用于测定二种单体的共聚竞聚率,这一方法计算方便,而且可以避免原先作图法中的误差,结果较为可靠。前文我们报道了四氟乙烯与两个新的全氟烷基乙烯基醚的共聚合反应,并对其中一个新单体——7,7-二氯-3-氧杂-全氟庚烯-1——与四氟乙烯的共聚进行了单体竞聚率的测定。结果表明,这一新的含氟烯醚单体的聚合活性较其它已有报道的同类单体大。为了验证这一