Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)     

Classical in-plane negative magnetoresistance and quantum positive magnetoresistance in undoped InSb thin films on GaAs (1 0 0) substrates

Magnetoresistance (MR) effects have been investigated in perpendicular and parallel magnetic fields at 300, 80 K and liquid He temperatures for undoped InSb thin films 0.1–2.3 μm thick grown on GaAs(1 0 0) substrates by MBE. At high temperatures, the intrinsic carriers show the parabolic negative MR observable only in magnetic fields parallel to the film. The skipping-orbit effect due to surface boundary scattering in the classical orbits in the plane vertical to the film has been argued to be responsible for the negative MR. At low temperatures (T=80 K), the transport is dominated by the two-dimensional (2D) electrons in the accumulation layers at the InSb/GaAs(1 0 0) hetero interface; MR is positive and shows a logarithmic increase with anisotropy between parallel and perpendicular field orientation, arising from the 2D weak anti-localization (WAL) that reflects the interplay between the spin-Zeeman effect and strong spin–orbit interaction caused by the asymmetric potential at the interface (Rashba term). The zero-field spin splitting energy of Δ₀13 meV, the electron effective mass of m^*0.10m₀ seven times of the band edge mass in bulk InSb and the effective g-factor of |g^*|15 in the accumulation layer have been inferred from fits of MR for the 0.1 μm thick film to the 2D WL theory.     

Light Diffraction of Aligned Polymer Fibers Periodically Dispersed by Phase Separation of Liquid Crystal and Polymer

We have confirmed light diffraction of aligned polymer fibers obtained by a phase separation of an anisotropic-phase solution of liquid crystal and polymer. He—Ne laser light passing through the polymer fibers was scattered in the axis vertical to the fibers, and had two peaks of light intensity symmetrical to the center of the transmitting laser spot. The two peaks were found to be caused by light diffraction due to the periodic polymer-fiber dispersion because the peaks corresponded to values calculated by intervals between the fibers. The periodical fiber networks are considered to be formed by anisotropic spinodal decomposition. This effect can be used to measure the dispersion order of the polymer fibers. © 2004 The Optical Society of Japan     

Photochemical attachment of polymers on planar surfaces with a covalently anchored monolayer of a novel naphthyl ketone photochemical radical generator

A monolayer of covalently anchored, novel, binaphthyl ketone is used as a surface‐confined photochemical radical generator (PRG) for anchoring a variety of polymers to silicon surfaces. The precursor PRG is synthesized by the application of a facile and novel method for the oxidation of sterically hindered benzylic hydrocarbons to carbonyl compounds. Oxidation was carried out with a stoichiometric amount of potassium peroxydisulfate, in the presence of a catalytic amount of copper sulfate in an acetonitrile/water mixture. The PRG synthesized is characterized by ¹H NMR, UV, and Fourier transform infrared (FTIR). The covalently attached monolayers are characterized by X‐ray photoelectron spectroscopy, ellipsometry, and water contact angle measurements. The method developed is applicable to the preparation of a monolayer of a variety of polymers on a wide range of substrates carrying surface hydroxyl groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5413–5423, 2004     

Synthesis and characterization of alt‐bipyridinylene‐phenylene copolymers containing ruthenium(II) complexes

Poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3a ), poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐4,4′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3b ), and poly{bis(2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3c ) were synthesized by the Suzuki coupling reaction. The alternating structure of the copolymers was confirmed by ¹H and ¹³C NMR and elemental analysis. The polymers showed, by ultraviolet–visible, the π–π* absorption of the polymer backbone (320–380 nm) and at a lower energy attributed to the d–π* metal‐to‐ligand charge‐transfer absorption (450 nm for linear 3a and 480 nm for angular 3b ). The polymers were characterized by a monomodal molecular weight distribution. The degree of polymerization was approximately 8 for polymer 3b and 28 for polymer 3d . © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2911–2919, 2004     

Atom transfer radical polymerization of methyl methacrylate by copper(I)‐pyridine‐2‐carboximidate catalysts

Pyridine‐2‐carboximidates [methyl ( 1a ), ethyl ( 1b ), isopropyl ( 1c ), cyclopentyl ( 1d ), cyclohexyl ( 1e ), n‐octyl ( 1f ), and benzyl ( 1g )] were prepared from the reaction of 2‐cyanopyridine with the corresponding alcohols. Cyclopentyl‐substituted 1d was found to be a highly effective ligand for copper‐catalyzed atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA). For example, the observed rate constant for a CuBr/ 1d catalytic system was found to be nearly twice as high as the cyclohexyl‐substituted CuBr/ 1e catalytic system [k_obs = (1.19 vs 0.56) × 10^?4 s^?1). The effects of the solvents, temperature, catalyst/initiator, and solvent/monomer ratio on the ATRP of MMA were studied systematically for the CuBr/ 1d catalytic system. The optimum condition for the ATRP of MMA was found to be a 1:2:1:400 [CuBr]_o/[ 1d ]_o/[ethyl 2‐bromoisobutyrate]_o/[MMA]_o ratio at 60 °C in veratrole solution, which yielded well‐defined poly(MMA) with a narrow molecular weight distribution of 1.14. The catalytically active copper complex 2d was isolated from the reaction of CuBr with 1d . Narrow molecular weight distributions as low as 1.06 were achieved for the CuBr/ 1d catalytic system by employing 10% of the deactivator CuBr₂. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2747–2755, 2004     

Strain hardening of polycarbonate in the glassy state: Influence of temperature and molecular weight

This study is concerned with the temperature and molecular weight dependence of the strain-hardening behavior of polycarbonate. It is shown that the strain-hardening modulus reduces with increasing temperature and decreasing molecular weight. This result is interpreted in terms of temperature accelerated relaxation of the entanglement network. Moreover, it is shown that frozen-in orientations, induced by homogeneous deformations above the glass transition temperature, lead to anisotropic yield behavior that can be fully rationalized (and modelled) in terms of a superimposed stress contribution of the prestrained network. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2041–2049, 2004     

Metallo‐supramolecular block copolymer micelles: Improved preparation and characterization

Micelles prepared from amphiphilic block copolymers in which a poly(styrene) segment is connected to a poly(ethylene oxide) block via a bis‐(2,2′:6′,2″‐terpyridine‐ruthenium) complex have been intensely studied. In most cases, the micelle populations were found to be strongly heterogeneous in size because of massive micelle/micelle aggregation. In the study reported in this article we tried to improve the homogeneity of the micelle population. The variant preparation procedure developed, which is described here, was used to prepare two “protomer”‐type micelles: PS₂₀‐[Ru]‐PEO₇₀ and PS₂₀‐[Ru]‐PEO₃₇₅. The dropwise addition of water to a solution of the compounds in dimethylformamide was replaced by the controlled addition of water by a syringe pump. The resulting micelles were characterized by sedimentation velocity and sedimentation equilibrium analyses in an analytical ultracentrifuge and by transmission electron microscopy of negatively stained samples. Sedimentation analysis showed virtually unimodal size distributions, in contrast to the findings on micelles prepared previously. PS₂₀‐[Ru]‐PEO₇₀ micelles were found to have an average molar mass of 318,000 g/mol (corresponding to 53 protomers per micelle, which is distinctly less than after micelle preparation by the standard method) and an average hydrodynamic diameter (d_h) of 18 nm. For PS₂₀‐[Ru]‐PEO₃₇₅ micelles, the corresponding values were M = 603,000 g/mol (31 protomers per micelle) and d_h = 34 nm. The latter particles were found to be identical to the “equilibrium” micelles prepared in pure water. Both micelle types had a very narrow molar mass distribution but a much broader distribution of s values and thus of hydrodynamic diameters. This indicates a conformational heterogeneity that is stable on the time scale of sedimentation velocity analysis. The findings from electron microscopy were in disagreement with those from the sedimentation analysis both in average micelle diameter and in the width of the distributions, apparently because of imperfections in the staining procedure. The preparation procedure described also may be useful in micelle formation from other types of protomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4458–4465, 2004     

Studies of photooxidative degradation of poly(vinyl chloride)/poly(ethylene oxide) blends

The photooxidative degradation of blends (in a full range of compositions) of amorphous poly(vinyl chloride) (PVC) with semicrystalline poly(ethylene oxide) (PEO) in the form of thin films is investigated using absorption spectroscopy (UV–visible and Fourier transform infrared) and atomic force microscopy (AFM). The amount of insoluble gel formed as a result of photocrosslinking is estimated gravimetrically. It is found that the PVC/PEO blendsí susceptibility to photooxidative degradation differs from that pure of the components and depends on the blend composition and morphology. Photoreactions such as degradation and oxidation are accelerated whereas dehydrochlorination is retarded in blends. The photocrosslinking efficiency in PVC/PEO blends is higher than in PVC; moreover, PEO is also involved in this process. AFM images showing the lamellar structure of semicrystalline PEO in the blend lead to the conclusion that the presence of PVC does not disturb the crystallization process of PEO. The changes induced by UV irradiation allow the observation of more of the distinct PEO crystallites. This is probably caused by recrystallization of short, more mobile chains in degraded PEO or by partial removal of the less stable amorphous phase from the film surface. These results confirm previous information on the miscibility of PVC with PEO. The mechanism of the interactions between the components and the blend photodegradation are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 585–602, 2004