Desorption behavior of a surfactant in a linear low‐density polyethylene blend at elevated temperatures

The desorption behavior of a surfactant in a linear low‐density polyethylene (LLDPE) blend at elevated temperatures of 50, 70, and 80 °C was studied with Fourier transform infrared spectroscopy. The composition of the LLDPE blend was 70:30 LLDPE/low‐density polyethylene. Three different specimens (II, III, and IV) were prepared with various compositions of a small molecular penetrant, sorbitan palmitate (SPAN‐40), and a migration controller, poly(ethylene acrylic acid) (EAA), in the LLDPE blend. The calculated diffusion coefficient (D) of SPAN‐40 in specimens II, III, and IV, between 50 and 80 °C, varied from 1.74 × 10^?11 to 6.79 × 10^?11 cm²/s, from 1.10 × 10^?11 to 5.75 × 10^?11 cm²/s, and from 0.58 × 10^?11 to 4.75 × 10^?11 cm²/s, respectively. In addition, the calculated activation energies (E_D) of specimens II, III, and IV, from the plotting of ln D versus 1/T between 50 and 80 °C, were 42.9, 52.7, and 65.6 kJ/mol, respectively. These values were different from those obtained between 25 and 50 °C and were believed to have been influenced by the interference of Tinuvin (a UV stabilizer) at elevated temperatures higher than 50 °C. Although the desorption rate of SPAN‐40 increased with the temperature and decreased with the EAA content, the observed spectral behavior did not depend on the temperature and time. For all specimens stored over 50 °C, the peak at 1739 cm^?1 decreased in a few days and subsequently increased with a peak shift toward 1730 cm^?1. This arose from the carbonyl stretching vibration of Tinuvin, possibly because of oxidation or degradation at elevated temperatures. In addition, the incorporation of EAA into the LLDPE blend suppressed the desorption rate of SPAN‐40 and retarded the appearance of the 1730 cm^?1 peak. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1114–1126, 2004     

Effects of poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] on the charge distributions of low‐density polyethylene/polystyrene blends

The effect of the triblock copolymer poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] (SEBS) on the formation of the space charge of immiscible low‐density polyethylene (LDPE)/polystyrene (PS) blends was investigated. Blends of 70/30 (wt %) LDPE/PS were prepared through melt blending in an internal mixer at a blend temperature of 220 °C. The amount of charge that accumulated in the 70% LDPE/30% PS blends decreased when the SEBS content increased up to 10 wt %. For compatibilized and uncompatibilized blends, no significant change in the degree of crystallinity of LDPE in the blends was observed, and so the effect of crystallization on the space charge distribution could be excluded. Morphological observations showed that the addition of SEBS resulted in a domain size reduction of the dispersed PS phase and better interfacial adhesion between the LDPE and PS phases. The location of SEBS at a domain interface enabled charges to migrate from one phase to the other via the domain interface and, therefore, resulted in a significant decrease in the amount of space charge for the LDPE/PS blends with SEBS. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2813–2820, 2004     

Mechanical Properties of Blends of Low-Density Polyethylene with Chlorinated Polyethylene

The results of experimental investigation into the mechanical properties of blends of low-density polyethylene (LDPE) with chlorinated polyethylene (CPE) in tension are presented. The specimens of pure LDPE, CPE, and nine types of LDPE/CPE blends, with different content of components at 10 wt.% intervals, were examined. Data on the influence of blend composition on the tensile stress-strain diagram, elastic modulus, yield stress, breaking stress, and ultimate elongation are obtained. The results of investigations of creep are also reported. It is found that the creep compliance (the total current compliance minus the elastic compliance) obeys the power law of creep.__________Translated from Mekhanika Kompozitnykh Materialov, Vol. 41, No. 3, pp. 391–404, May–June, 2005.     

神经网络法计算镉（Ⅱ）,羟基及碳酸根三元体系的形态分布

采用前馈线笥网络ＢＰ算法，计算了Ｃｄ６２＋－ＯＨ＾－ＣＯ＾２－３三元体系的累积稳定常数。用Ｈｏｐｆｉｅｌｄ反馈网络研究了体系中络合物的形态分布。溶液中溶解的ＣＯ２对ｌｇβ１的计算结果有重要影响，对ｌｇβ２，ｌｇβ３，ｌｇβ４的结果影响不大。     

Liquid-liquid phase equilibria of aqueous two-phase systems containing salts and polyethylene glycol

Liquid-liquid phase equilibria of the ternary systems: (a) polyethylene glycol - ammonium sulfate- water and (b) polyethylene glycol - sodium carbonate -water have been determined experimentally at 15°, 25°, 35° and 45°C and for two different molecular weights of the polymer (Avg. M.W. 1000 and 2000). Details of the glass cell and of the equilibration and analytical procedures used are described. Equilibrium data along with phase diagrams are presented. Finally the effect of temperature and of the molecular weight of the polymer are also discussed.     

Synthesis of Dimethyl Carbonate from CO2 , Methanol, and Epoxides Using Re（CO） 5 Cl/K2 CO3 as Catalyst System

IntroductionOver the past few years, dimethyl carbonate(DMC) has been proven to be an efficientmethylating,methoxylating, and methoxycarbonylating agent inorganic syntheses, in which DMC is used to replace thetoxic methyl halides, dimethyl sulfate or carb     

低温等离子体对塑料表面处理——低温等离子体对高密度聚乙烯表面处理的ESR研究

本文研究了不同处理条件(处理功率、处理时间和处理压力)下等离子体气体(Ar、N₂、O₂和空气等)对高密度聚乙烯表面处理产生的自由基的ESR谱。我们观察到等离子体处理产生的自由基是相当稳定的,它的ESR信号强度随处理功率和处理时间增加而增加。但处理压力对它影响不大。我们证明了紫外线对高密度聚乙烯表面产生自由基作用随处理条件而变化。并初步解释了谱的超精细相互作用。     

Annealing behavior of gel‐spun polyethylene fibers at temperatures lower than needed for significant shrinkage

The annealing at 373 K of ultrastrong, gel‐spun polyethylene (PE) has been studied. At this temperature, the fibers show no significant shrinkage. Still, a significant decrease in the mechanical properties is observed. The fibers have been analyzed with differential scanning calorimetry (DSC), temperature‐modulated differential scanning calorimetry (TMDSC), atomic force microscopy (AFM), and small‐angle X‐ray scattering (SAXS). During the annealing, the glass transition of the intermediate phase is exceeded, as shown by DSC. When split for structure analysis by AFM, the annealed fibers undergo plastic deformation around the base fibrils instead of brittle fracture. The quasi‐isothermal TMDSC experiments are compared to the minor structural changes seen with SAXS and AFM. The loss of performance of the PE fibers at 373 K is suggested to be caused by the oriented intermediate phase, and not by major changes in the structure or morphology. The overall metastable, semicrystalline structure is shown by TMDSC to posses local regions that can melt reversibly. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 403–417, 2003     

四溴双酚A锑铝双金属化合物的合成及其阻燃性能

以四溴双酚Ａ（ＴＢＡ）合成了在水和空气中稳定的四溴双酚Ａ合锑铝双金属化合物（ＴＢＡＳＡ）．通过ＩＲ、１ＨＮＭＲ和元素分析予以表征，并研究了其对聚乙烯（ＰＥ）和聚环氧乙烷（ＰＥＯ）的阻燃性能．结果表明，这种分子中含有溴、锑和铝的化合物，对聚乙烯和聚环氧乙烷等高聚物材料有高的阻燃性能与消烟效果．