铅在铂电极上的还原电位溶出分析法

研究了以亚铁氰化钾为还原剂铅在铂电极上的还原电位溶出法；讨论了电极的预处理、阳极富集和随后的还原电位溶出及铅测定的干扰。     

纳米Sb2O3的制备与性能研究

由于Sb2O3是一种性能优良的无机阻燃剂,并与卤素阻燃剂有很好的协效作用[1],1998年,全球用于阻燃的Sb2O3达80kt以上,占阻燃剂总耗量的7%[2]。但由于其本身的极性特点,加入到纤维、塑料等高分子材料中,材料的力学性能受到很大损失[3],因此对传统的微米级的Sb2O3进行超细、表面处     

脲基苯乙炔4-′(对甲基苯基)-6-苯基-2,2′-二联吡啶铂(II)络合物的合成

本文通过异氰酸酰化反应合成了含有脲基的苯乙炔新型配体及以它作为辅助配体的4′-(对甲基苯基)-6-苯基-2,2′-二联吡啶铂(II)络合物,初步研究了铂(II)络合物的光物理性质,发现由于脲基的存在,当浓度大于3.32×10-5mol/L时铂(II)络合物能够发生分子间簇集.     

反相微乳液法制备纳米Al2O3颗粒及其形成反应机理的研究

通过聚乙二醇辛基苯基醚(曲拉通X-100)/正丁醇/环己烷/水溶液形成的体系, 采用反相微乳液法合成了Al₂O₃纳米粒子. 对前驱体进行热分析(TG-DTG-DTA), 确定了合适的煅烧温度为1150 ℃. 采用X射线衍射(XRD)、透射电镜(TEM)、紫外可见分光光度法(UV-vis)分别对产物的结构、粒度和形貌进行了表征, 考察了微乳液中水与表面活性剂的物质的量之比(ω_o)、煅烧温度和煅烧时升温速率等关键因素对产物形貌和晶相的影响, 并通过分析进一步揭示了Al₂O₃纳米粒子的形成机理. 结果表明, 控制ω_o为10、煅烧温度为1150 ℃可得到分散性好、粒径分布均匀的Al₂O₃纳米粒子, 且2 ℃/min的升温速率更有利于产物向稳定的α晶相转变.     

Photobioelectronic studies with thylakoid membranes

The research described in this paper presents a method for chemically modifying the surface of plant photosynthetic membranes in such a way that electrical contact can be made. Colloidal platinum was prepared, precipitated directly onto thylakoid membranes from aqueous solution, and entrapped on fiberglass filter paper. This composition of matter was capable of sustained simultaneous photoevolution of hydrogen and oxygen when irradiated at any wavelength (400–700 nm) in the chlorophyll absorption spectrum. Experimental data support the interpretation that part of the platinum metal catalyst is precipitated adjacent to the photosystem-I reduction site of photosynthesis and that electron transfer occurs across the interface between photosystem I and the catalyst. When contacted with metal electrodes, the thylakoid-platinum combination was capable of generating a sustained flow of current through an external load resistor. Procedures for preparing this material and experimental data on its catalytic and electronic properties are presented. Also presented is an analysis of the flow of photocurrent in terms of the interfacial electron transfer reactions that occur at the interfaces of the components of the assembly.     

碳化钨负载S2O8^2-/ZrO2固体超强酸催化剂上的正戊烷反应研究

首次研究了碳化钨负载S2 O2 -8 ZrO2 (PSZ)固体超强酸催化剂 (WC PSZ)上正戊烷的反应情况及影响催化剂活性的各种因素 ,并用GC MS ,XRD ,BET等手段分析了正戊烷反应产物和催化剂的物理化学性质等 .结果表明 :WC PSZ对正戊烷具有异构化和裂解的双重催化作用 .PSZ在负载适量碳化钨后对正戊烷反应的活性和选择性显著提高 ,显示出优于Pt PSZ催化剂的效果 ,碳化钨的负载量为 2 0 %的效果最佳 .适当的焙烧、活化和反应温度等条件是取得良好反应效果的关键     

MODIFICATION OF TRANSITION METAL CATIONS TO POLYMER-STABILIZED PLATINUM COLLOIDAL CLUSTERS IN ENANTIOSELECTIVE HYDROGENATION OF METHYL PYRUVATE

Modification of transition metal cations to polymer-stabilized Pt colloidal clusters modified with cinchonidine was studied in enantioselective hydrogenation of methyl pyruvate. Compared to the enantiomeric excess (e.e.) value (71.4%) obtained without the presence of metal cations, obvious e.e. enhancement (up to 82.5%) was resulted from the addition of Zn^2 but with a certain decrease in activity. The reaction parameters in the presence of Zn^2 were also studied. It was found that the Pt colloidal catalysts in the presence of metal cations performed very differently from that in the absence of metal cations.     

Synthesis of Polyacrylaminothiourea Chelating Fiber and Properties of Concentration and Separation of Trace Noble Metal Ions from Samples

A novel polyacrylaminothiourea chelating fiber was synthesized simply and rapidly from nitrilon (an acrylonitrile-based synthetic fiber), which was applied to preconcentrate and separate of trace amount of Au(Ⅲ）,Pt(Ⅳ）,Pd(Ⅳ） and Ir (Ⅳ） ions from solution of samples.The analyzed ions can be quantitatively concentrated by the fiber up to a flow rate of 20.0mL/min at pH2, and can also be desorbed with 15 mL of 4mol/L HCl 3% thiourea from the fiber column with recoveries of 96.5%-100%.The chelating fiber can be reused for ten times,the recoveries of these ions are still over 92%,and hundred to thousand times of excess of Fe(Ⅲ）,Al（Ⅲ）,Ca(Ⅱ），Mg（Ⅱ）,Ni(Ⅱ）,Mn（Ⅱ),Cu(Ⅱ），Zn(Ⅱ），and Cd(Ⅱ） cause no interference on the determination of the analyzed ions by inductively-coupled plasma atomic emission spectrometry (ICP-AES).The static saturation adsorption capacities of the fiber for the analytes are in the range of 1.15-2.80mmol/g.The relative standard deviations for the determination of 20.0ng/mL each of Au(Ⅲ）,Pt(Ⅳ）,Pd(Ⅳ）and Ir(Ⅳ） are in the range of 0.7%-3.0%.The recoveries for test from standard additions to real solution samples are between 96% and 100%.The concentration of each ion in powder sample detected by the method is in good agreement with the certified value.     

多壁碳纳米管负载铂的甲苯加氢脱芳催化剂

以多壁碳纳米管(CNTs)为载体制备了负载型Pt催化剂Pt/CNTs并将其用于催化甲苯加氢脱芳(HDA)反应.结果表明,在1.0%Pt/CNTs催化剂上,在0.4MPa,373K,PhCH3/H2摩尔比=6/94和GHSV=120L/(h.g)的反应条件下,甲苯转化率可达100%,比反应速率为0.0523mmol/(s.m2),分别是γ-Al2O3和AC负载各自最佳Pt负载量催化剂1.4%Pt/γ-Al2O3和2.4%Pt/AC上相应值的1.17和1.18倍.甲苯加氢产物全部为甲基环己烷,其他可能的加氢产物均在气相色谱检测限以下.催化剂的表征研究揭示,用CNTs代替γ-Al2O3或AC作为载体并不会引起所负载Pt催化剂上甲苯HDA反应的表观活化能发生明显变化.与γ-Al2O3或AC负载的相应催化剂相比,一方面,CNTs负载的Pt催化剂易于在较低温度下还原活化,并且其工作态催化剂表面催化活性Pt物种(Pt0)所占表面Pt摩尔分率有所提高;另一方面,CNTs负载的Pt催化剂对H2具有较高的吸附/活化和储存能力.这些促进效应对催化剂HDA活性的提高都有重要贡献.