Synthesis and application of near-infrared absorbing morpholino-containing aza-BODIPYs

Morpholino-containing aza-BODIPYs at 3,5-positions were synthesized. The maxima absorption and emission of these dyes locate at the near-infrared region. Aza-BODIPY 1 with the morpholino group as a pH-sensitive functionality could be used to be a pH probe, and the dramatic increase in fluorescence intensity at 675 nm by about 1500 folds. Moreover, the singlet oxygen generation of PS 2 with the dibromo groups at 2,6-positions was more effective than that of the parent dye 1.     

Correlation between Boron Isotope of Coral Acropora and pH Value of Seawater Surface

A water circulation system with the almost same element composition and socket type was adopted in coral Acropora culture under different seawater pH value conditions and the data of the relationship between boron isotopic compositions of coral and seawater pH value by thermoelectric ionization mass spectrometer were obtained. According to the correlations between α_carb-3 of coral and the pH value of cultured seawater, α_carb-3 was not a constant but related to pH value, indicating that B(OH)₃ also incorporated carbonate. Therefore, the theoretical formula could not be used to calculate the seawater pH value from the δ¹¹B_carb value of the measured marine biological carbonate. The empirical equations obtained experimentally would be an alternative method to calculate the seawater pH value. In addition, the mixed precipitation of CaCO₃ and Mg(OH)₂ was found in aquaculture tanks with high pH value, and the δ¹¹B of the solid was significantly higher than that of cultured seawater. The result indicated that the presence of Mg(OH)₂ had a significant effect on the boron isotope fractionation, which deserved our attention.     

Temperature and pH dual‐sensitive polyaspartamide derivatives for antitumor drug delivery

The pH‐sensitive tertiary amino groups were introduced to synthesize temperature and pH dual‐sensitive degradable polyaspartamide derivatives (phe/DEAE‐g‐PHPA) containing pendant aromatic structures and ionizable tertiary amino groups. The thermo/pH‐responsive behavior of phe/DEAE‐g‐PHPA polymer can be tuned by adjusting the graft copolymer composition. Due to the pH sensitivity of the phe/DEAE‐g‐PHPA‐g‐mPEG polymer with hydrophilic long PEG chain, the micelles and the anticancer drug‐loaded micelles were prepared by a quick pH‐changing method without using toxic organic solvent. The obtained polymeric micelles, paclitaxel‐loaded micelles and doxorubicin‐loaded micelles were stable under physiological conditions. Both the drug‐loaded micelles showed much faster release at pH 5 than at pH 7.4. The doxorubicin‐loaded micelles showed obvious and better anticancer activity against both HepG2 and HeLa cells than free doxorubicin. Thus these nontoxic, dual thermo‐ and pH‐sensitive phe/DEAE‐g‐PHPA‐g‐mPEG micelles may be a promising anticancer drug delivery system. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 879–888     

Untersuchungen zum Verhalten der Pt-Metalle gegenüber festen und flüssigen Kationenaustauschern mit Hilfe der Radiotracermethode

Mit Hilfe radioaktiver Nuklide wurde die Aufnahme der Pt-Metalle aus chloridhaltigen Lösungen sowoht durch feste (Wofatit KPS) als auch durch flüssige Kationenaustauscher (Bis-2-äthylhexylphosphorsäure) bei Variation des pH-Wertes, der Vorbehandlung sowie der Edelmetallkonzentration bestimmt. Pt und Ir wurden nur geringfügig, Pd und Rh dagegen deutlich stärker adsorbiert. Beide Austauschertypen zeigten qualitativ das gleiche Verhalten. Die gefundenen Abhängigkeiten der Adsorption wurden auf das komplexchemische Verhalten der Pt-Metalle zurückgeführt. Es werden Verfahren zur schnellen radiochemischen Reinigung der benutzten Nuklide angegeben.     

Novel materials for bioanalytical and biomedical applications: Environmental response and binding/release capabilities of amphiphilic hydrogels with shape‐persistent dendritic junctions

The binding and release capabilities of a hydrogel series, constructed of hydrophilic poly(ethylene glycol) segments and hydrophobic dendritic junctions [poly (benzyl ether)s], are evaluated in aqueous media. The environmental response of the amphiphilic networks is also tested in water at three pH values: 1.5, 7.0, and 10.1. The highest swelling ratio is observed under acidic conditions and varies between 3.7 and 6.5, depending on the crosslinking density and dendrimer generation. Gel specimens with embedded indicators react within 3–6 s with a clear color switch to the change in the pH of the surrounding medium. The experiments with model anionic and cationic indicators and stains show that the hydrogels have basic interiors. The gel binding capabilities depend on the water solubility of the substrate and on the size of the incorporated dendritic fragments. Model release studies have been performed at 37 °C and pHs 1.5, 7.0, and 10.1. The observed phenomena are explained by the transformations in the structure and charge that both the networks and the model compounds undergo with the changes in the pH of the aqueous medium. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4017–4029, 2005     

Effect of pH on Poly(acrylic acid) Solution Polymerization

The free-radical redox-initiated aqueous solution polymerization of fully and partially neutralized acrylic acid was carried out at room temperature under full exposure to air. The effect of neutralization degree on the polymerization rate and product properties was studied. Increasing neutralization of the reaction mixture with sodium hydroxide resulted in greater conversion of acrylic acid to sodium acrylate. The rate of polymerization, determined from a gravimetric off-line water removal technique, was shown to decrease significantly with decreasing degree of neutralization. Molecular weight also decreased with decreasing degree of neutralization. The glass transition temperature and hydrophilicity of the polymer product decreased with increasing degree of neutralization. In-line infrared monitoring was also used to monitor the reaction progress and was shown to be an effective tool for this purpose.     

Composite of SiO2 and Hydrogel Having Microphase Separated Structure: Physical Properties Dependence on pH

Abstract

Organic-inorganic composite gel was prepared by using PEG-modified urethane acrylate (PMUA) gel and tetraethoxysilane (TEOS). PMUA gel was prepared by the phase-inversion emulsion polymerization of PMUA emulsion. The gelation of PMUA emulsion using this method enables PMUA gel to swell with H₂O, TEOS, and ethanol. Hydrolysis and condensation reaction rates of the sol-gel process are strongly influenced by the pH controlled by catalysts such as HCl and NH₄OH. Additionally, the morphology on the cross section of composite and the amount of silica ingredient incorporated into the composite gel were dependent on solvent, the molar ratio of H₂O to TEOS, as well as the pH value.

As the silica content increased, due to hydrogen bonds interacting between PMUA gel and SiO₂, particles, the tensile strength of composites considerably increased, whereas the elongation at break decreased. The incorporation of silica ingredient in PMUA gel/silica composites was verified with FTIR/ATR and SEM. The amount of the silica component in the composite was indirectly investigated by using TGA thermal analysis.     

Preparation of Poly(N‐isopropylacrylamide) Microgels using Different Initiators Under Various pH Values

Ammonium persulfate (APS), 2,2′‐azobis(amidinopropane) dihydrochloride (V50) and 4,4′‐azobis(4‐cyanovaleric acid) (ACVA) were utilized to prepare temperature‐sensitive poly(N‐isopropylacrylamide) (PNIPAM) microgels by precipitation polymerization under various reaction pH conditions. Their particle sizes and swelling ratios depended on the reaction pH due to the pH dependence on the ionization degree of the decomposed fragments originating from the initiators and their hydrophilicity‐hydrophobicity. The more hydrophobic initiator, under the reaction pH conditions used, could be partitioned to a greater extent into the microgel particles due to the hydrophobicity of PNIPAM chains at the reaction temperature, which led to a more cross‐linked structure inside the microgels resulting in their smaller swelling ratio. pH dependence of surface charge density of the microgels with amidino groups or carboxylic acid groups on their surfaces was evidenced by the variation of their zeta potentials as a function of pH.     

The Copolymerization of Alkenes with Maleic Anhydride

The investigations presented deal with the experimental results of the copolymerization of maleic anhydride (MAn) with alkenes. The course of the reaction is explained by the overall rate of the copolymerization (v _Br), which correlates with the solution viscosity of the copolymer, and the dependence of the v _Br maximum on the mole ratio of the monomers at constant total monomer concentration. The use of solvents with increasing donor power leads to increased complexing of the free MAn molecules and of the MAn radical chain ends. The results demonstrate that, for low 1-alkenes, the addition of the MAn chain radical is the rate-determining step of the copolymerization. As the substituents on the olefinic double bond become larger or the double bond shifts to the 1,2-position, the addition of MAn to the hydrocarbon radical becomes more and more the rate-determining step. On the other hand, an increase of the CT complexation of the MAn polymer radical by use of donor solvents decreases the alkene addition rate.     

Insights into the photophysics,protonation and Cu2+ ion coordination behaviour of anthracene-9,10-dione-based chemosensors

Carboxylic acid–diamine-based Cu²⁺ chromogenic sensors (3 and 4) exhibited colour switching from red to blue with good sensitivity and selectivity towards Cu²⁺ among other physiologically important alkali, alkaline earth and heavy metal ions. This colour-switching phenomenon arises due to selective deprotonation of aryl amine NH by Cu²⁺. Significantly, chemosensor 3 (λ_max 492 nm) shows multiple modes of complexation towards Cu²⁺. It is very much evident from the appearance of blue colour (λ_max 615 nm) at pH >7.0 and yellow colour (λ_max 465 nm) at pH < 4.0. In addition, chemosensor 3 exhibits a unique logic gate system that involves ‘INHIBIT’ and ‘TRANSFER’ logic gates.