 采用阳离子表面活性剂十六烷基三甲基溴化铵为模板剂，以正硅酸乙酯为硅源，以硫酸铝为铝源，水热合成了以催化油浆窄馏分为添加剂的高比表面积Al－MCM－41介孔分子筛，并利用XRD，HREM，TG－DTA及N2吸附－脱附等测试手段对合成样品进行了表征．合成的Al－MCM－41分子筛的比表面积和孔体积分别达到1295m2／g和1．5cm3／g，其平均孔径为4．3nm．重点研究了Al－MCM－41分子筛结晶度、晶胞参数、比表面积、孔体积及平均孔径等结构性质随催化油浆窄馏分添加量及其组成的变化规律，并从合成机理上进行了解释．     

Spherical Particles of Zirconia-Titania of Hexagonal Structure from a Neutral Amine Route

Through the sol–gel process, using the so-called neutral amine route, spherical particles of 1:1 zirconia–titania were synthesized from zirconium(IV) and titanium(IV) butoxides as well as 1,12-diaminododecane as precursor species. The obtained product exhibited a hexagonal structure, as determinated by X-ray diffraction data. The obtained material was also characterized by thermogravimetry, differential scanning calorimetry, infrared spectroscopy, scanning electron microscopy, and surface area measurements. Despite the release of template molecules on heating, the spherical morphology was retained up to about 1200°C, at which the disruption of the spheres took place.     

制备具有光催化活性的金红石相纳米氧化钛粉体

以TiCl4为原料，通过控制盐浓度和水解温度可以在温和条件下制备出晶粒尺 寸为6nm的金红石相氧化钛粉体，比表面积为175m^2/g。测定了粉体的X衍射、红外 和拉曼光谱。TEM照片显示粉体呈放射状颗粒，其粒径尺寸在200－400nm。苯酚的 光催化降解实验表明它比具有相同比表面积的锐钛矿粉体有更高的光催化活性。其 较大的团聚颗粒尺寸有利于光催化反应后的分离。     

Characterization of Titania/Silica Gel by Means of Low-Pressure Nitrogen Adsorption

Adsorbents synthesized by grafting of titania onto mesoporous silica gel surfaces at different temperatures were studied by means of nitrogen adsorption–desorption and water desorption. The pore size distribution f(R_p) of titania/silica gel depends on the titania concentration (C_TiO2) and the temperature of titania synthesis. Nonuniformity of TiO₂ phase is maximal at a low C_TiO2 value (3.2 wt.% anatase deposited at 473 K), and two peaks of the fractal dimension distribution f(D) are observed at such a concentration of titania, but at larger C_TiO2 values, only one f(D) peak is seen. More ordered filling of pores and adsorption sites by nitrogen, reflecting in the shape of adsorption energy distributions f(E) at different pressures of adsorbate, is observed for adsorbent with titania (rutile+anatase) grafted on silica gel at a higher temperature (673 K).     

新型介孔分子筛KIT-1加氢脱硫催化剂的研究

制备了新型的结构排列无序的介孔分子筛KIT-1和负载Ni, Mo的KIT-1加氢脱硫催化剂。实验结果表明MoO3较易分散在KIT-1的表面,而NiO则容易在其表面形成小晶粒。与以MCM-41和NaY分子筛为载体的Ni, Mo催化剂相比, KIT-1负载催化剂具有较高的加氢脱硫催化活性,因为KIT-1载体具有相互交错的三维孔道结构, 有利于反应物和产物的扩散, 而不容易受孔道堵塞的影响。     

Modification of Surface and Structural Properties of Ordered Mesoporous Silicates

Two simple modification methods for ordered mesoporous silicas were examined and compared. MCM-41 molecular sieve was physically coated with 4-cyano-4-biphenyl [4(4-pentenyloxy)]benzoate (CBPB) and chemically modified using trimethylethoxysilane. The structural and surface properties of the obtained materials were characterized using elemental analysis, thermogravimetry and nitrogen adsorption over a wide pressure range.It was shown that the pore size of the MCM-41 material was not decreased significantly after the coating procedure, even for high loadings of CBPB. Moreover, low pressure adsorption measurements indicated that significant fractions of the MCM-41 surface were not covered by CBPB, even for high CBPB loadings, which suggests that the attained coverage may be very nonuniform. The chemical bonding procedure led to a marked decrease in the pore size and change of surface properties.It was demonstrated that nitrogen adsorption measurements provide a means of a thorough characterization of modified MCM-41 materials, allowing to estimate the surface area, pore volume and pore size distribution. Moreover, low pressure adsorption data can be used to qualitatively or semiquantitatively assess the surface coverage of the coated/bonded organic groups, which may be used to estimate the uniformity of the coverage and therefore, the usefulness of the modification procedure.     

Effect of the rhenium additive to VOx/TiO2 and MoOx/TiO2 catalysts on their properties in oxidative dehydrogenation of propane

VO_x/TiO₂ and MoO_x/TiO₂ catalysts with the addition of Re (Re/V or Mo = 0.5) were synthetized and tested in oxidative dehydrogenation of propane and in reduction by propane. XPS measurements showed depletion of the surface in Re. The Re additive does not affect the total conversion of propane, but increases the selectivity to propene. The effect is more pronounced for the MoO_x/TiO₂ catalyst. The increase in the selectivity to propene is accompanied with the increase in the reducibility of the catalysts.     

The Incorporation of Titania into Modified Silicates for Solar Photodegradation of Aqueous Species

A new class of sol-gel-derived photocatalytic materials has been synthesized and used in solar-assisted photodegradation studies. The materials are comprised of a homogeneous dispersion of commercial TiO₂ powder into silica and organically modified silicate (Ormosil) hosts. The efficiency of the photocatalytic properties of these TiO₂-containing materials was determined by their relative performance in the solar photodecomposition of aqueous rhodamine B. The improved adsorption properties of the modified materials compared to commercial TiO₂ increase the photodecomposition rate and the buoyancy properties, although excess hydrophobicity decreases the wetted section of the catalyst and its photocatalytic performance. These materials can be used as floatable catalysts for solar-assisted water purification.