Deposits comprised of amyloid‐β (Aβ) are one of the pathological hallmarks of Alzheimer's disease (AD) and small hydrophobic ligands targeting these aggregated species are used clinically for the diagnosis of AD. Herein, we observed that anionic oligothiophenes efficiently displaced X‐34, a Congo Red analogue, but not Pittsburgh compound B (PIB) from recombinant Aβ amyloid fibrils and Alzheimer's disease brain‐derived Aβ. Overall, we foresee that the oligothiophene scaffold offers the possibility to develop novel high‐affinity ligands for Aβ pathology only found in human AD brain, targeting a different site than PIB.     

表面活性剂辅助合成Y2O2S:Eu3+,Mg2+,Ti4+红色长余辉材料

以表面活性剂十二烷基硫酸钠为均匀分散剂,通过液相与固相相结合的方法制备了Y2O2S∶Eu3+,Mg2,Ti4+红色长余辉材料.采用X射线衍射(XRD)、扫描电镜(SEM)、激发与发射光谱、热释光谱等手段对材料进行了表征.研究结果表明,与高温固相法相比,样品的最低合成温度与最佳合成温度均降低了200～300℃,其发光特性没有改变,表面活性剂的添加影响了样品的形貌.同时,对表面活性剂引入后,Y2O2S∶Eu3+,Mg2+,Ti4+的生长机制和发光机理进行了讨论.     

(Gd,Lu)3Al5O12∶Tb3+,Eu3+透明陶瓷制备与发光性能

通过简单的化学沉淀法制备了纳米前驱体,结合真空烧结工艺,制备了一系列镥稳定钆铝石榴石{(Gd, Lu)₃Al₅O₁₂∶Tb,Eu}透明陶瓷。将透明陶瓷加工成1 mm厚的圆片,对透明陶瓷样品进行了X射线衍射、光致发光、透过率和衰减时间等表征。高温烧结过后,陶瓷样品仍保持稳定的石榴石相。选定313 nm作为透明陶瓷的激发波长,可获得最强的荧光发射。此外,通过对不同样品进行紫外可见荧光测试,获得了由绿光到红光的可调节发射。在313 nm激发,543 nm和591 nm的监测波长下,透明陶瓷样品均具有Eu³⁺的毫秒级衰减时间。     

A One-dimensional Transition Metal Complex Constructed from 24-Membered Hinge-shaped Macrocycles with Salicylic Acid and 1,3-Bis（4-pyridyl）propane

A new 1-D coordination polymer [Cd（Hsal）2（bpp）2] 1 was hydrothermally synthesi- zed by self-assembly of the corresponding metal oxide and salicylic acid （H2sal） with exo-bidentate flexible dipyridyl ligand 1,3-bis（4-pyridyl）propane （bpp）. X-ray crystal structure analysis reveals that complex 1 crystallizes in monoclinic,space group C2/c with a = 18.942（3）,b = 12.9309（19）,c = 16.504（2） A,β = 120.072（2）°,V = 3498.3（9）A^3,Z = 4,C40H38CdN4O6,Mr = 783.14,Dc = 1.487 g/cm^3,μ = 0.679 mm^-1,F（000） = 1608,R = 0.0619 and wR = 0.1435 for 3153 observed reflections （I 〉 2σ（I））. The most remarkable feature of 1 lies in the 1-D chain by repeating [Cd2（bpp）2] units which consist of a 24-membered macrocyclic ring. The 1-D motifs are further connected by C–H… O hydrogen bonds to generate a 2-D structure. In addition,thermal stability and luminescent property of compound 1 were also documented.     

Li+掺杂ZnO基荧光粉的制备、性能研究及其表面包覆

采用草酸根沉淀法制备ZnO∶ Eu3+荧光粉,探讨了Li+对Eu3+的敏化作用,并研究了SiO2的表面包覆对ZnO∶Eu3,Li+荧光粉性能的影响.采用XRD、IR、SEM、PL等分析了样品的物相、形貌及发光性能.结果表明:K+的掺杂能有效的增强Eu3+与ZnO之间的能量传递,提高其发光性能.而表面包覆SiO2使ZnO∶ Eu3+,Li+荧光粉的晶粒间团聚减小,并对其激发光谱产生影响.     

超分子化合物(C_(12)H_(10)N_4)(C_7H_6O_3)_2的合成、晶体结构及荧光性质

合成了超分子化合物(C_(12)H_(10)N_4)(C_7H_6O_3)_2,并进行了元素分析、红外光谱、紫外光谱表征和单晶X射线衍射分析.构筑单元之间通过多重氢键和π-π堆积作用的协同效应形成超分子化合物,并研究了化合物的固体荧光性能.研究表明:该晶体属于单斜晶系P2_1/c空间群,晶胞参数为:a=0.3974(1) nm,b=2.0330(2) nm,c=1.4343(1) nm, β=94.892(2)°,V=1.15440(19) nm~3,d_c=1.400 g/cm~3,Z = 2,μ= 0.102 mm~(-1),F_((000))=508,R_1=0.0359,wR_2=0.0893 [I>2σ(I)].     

M2B5O9X：Eu，Tb（M=Ca,Sr;X=Cl,Br）荧光体的光谱特征

利用Eu^3 和Tb^3 稀土离子之间存在电子组态共轭性的特征,将其双掺于同一基质中,由于电子转移而产生Eu^2 ,使Eu^3 ,Tb^3 和Eu^2 共存于同一体系中,在空气中合成了M2B5O9X：Eu,Tb荧光粉,研究了其发光特征及影响作用。结果表明,Eu^3 ,Tb^3 和Eu^2 共存于同一基质中,且稀土离子的掺杂量对其光谱产生影响。     

MgF2对Mn4+掺杂锗酸盐红色荧光粉发光的影响

3.5MgO·0.5MgF₂·GeO₂∶Mn⁴⁺作为优异热稳定性和良好发光性能的红色荧光粉而被市场应用,然而,该粉体中MgF₂的作用影响机理尚不明晰,阻碍其性能进一步优化和发展。采用高温固相法制备了系列Mn⁴⁺激活的锗酸盐荧光粉,通过对比加入MgF₂、H₃BO₃(助熔剂),研究了该粉体的结构、形貌、发光性能等变化规律,阐明了MgF₂的发光影响作用。研究表明,加入MgF₂、H₃BO₃和不加任何助熔剂时的样品,其最佳烧结温度分别为1 150、1 250和1 350 ℃,上述温度下发光强度均为最佳值,其中加入MgF₂、H₃BO₃的样品在最佳温度处生成了纯相。MgF₂的添加,一方面同H₃BO₃一样作为助熔剂对生成纯相、提高样品结晶度起了积极的作用;另一方面,通过研究分析,确认F^-离子成功掺杂进入晶格,促使样品生成的晶体结构为Mg₁₄Ge₅(O,F)₂₄。加入MgF₂、H₃BO₃在最佳烧结温度的样品的荧光寿命分别为0.93和0.75 ms。     

水热制备Sr（MoO4）x（WO4）1-x固溶体微晶及其发光性能

采用水热法制备了Sr（MoO₄）_x（WO₄）_1-x固溶体微晶。通过X射线粉末衍射（XRD）、傅里叶变换红外光谱（FT-IR）、扫描电镜（SEM）和荧光分析（FA）表征了微晶的结构、表面形貌和发光性能。XRD和FT-IR结果表明制备的Sr（MoO₄）_x（WO₄）_1-x微晶皆呈现典型的四方晶相白钨矿结构。SEM结果表明制备的微晶为表面光滑且粒径均匀的球形颗粒。荧光发射光谱显示,在275 nm紫外光激发下,随着x值的增加,Sr（MoO₄）_x-（WO₄）_1-x固溶体微晶在350 nm处的发射逐渐减弱,470 nm处的发射逐渐增强。