Fluorinated,crosslinkable terpolymers based on vinylidene fluoride and bearing sulfonic acid side groups for fuel‐cell membranes

The radical terpolymerization of 8‐bromo‐1H,1H,2H‐perfluorooct‐1‐ene with vinylidene fluoride (VDF) and perfluoro(4‐methyl‐3,6‐dioxaoct‐7‐ene) sulfonyl fluoride is presented. Changing the feed compositions of these three fluorinated comonomers enabled us to obtain different random‐type poly[vinylidene fluoride‐ter‐perfluoro(4‐methyl‐3,6‐dioxaoct‐7‐ene) sulfonyl fluoride‐ter‐8‐bromo‐1H,1H,2H‐perfluorooct‐1‐ene] terpolymers containing various sulfonyl fluoride and brominated side groups. Yields higher than 70% were reached in all cases. The hydrolysis of the sulfonyl fluoride group into the ? SO₃Li function in the presence of lithium carbonate was quantitatively achieved without the content of VDF being affected, and so dehydrofluorination of the VDF base unit was avoided. These original terpolymers were then crosslinked via dangling bromine atoms in the presence of a peroxide/triallyl isocyanurate system, which produced films insoluble in organic solvents such as acetone and dimethylformamide (which totally dissolved uncured terpolymers). The acidification of ? SO₃Li into the ? SO₃H function enabled protonic membranes to be obtained. The thermal stabilities of the crosslinked materials were higher than those of the uncured terpolymers, and their electrochemical performances were investigated. According to the contents of the sulfonic acid side functions, the ion‐exchange capacities ranged from 0.6 to 1.5 mequiv of H⁺/g, whereas the water uptake and conductivities ranged from 5–26% (±11%) and from 0.5 to 6.0 mS/cm, respectively. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4566–4578, 2006     

Pd (II)‐catalyzed vinyl addition polymerization of novel functionalized norbornene bearing dimethyl carboxylate groups

Three novel functionalized polynorbornenes (PNB) with pendant dimethyl carboxylate group (carboxylates—acetate, propionate, and butyrate) are synthesized as a vinyl‐type with a palladium (II) catalyst in high yield. The effects of size of substitutents, molar ratio of monomer to catalyst, solvent polarity, reaction time, and temperature on the polymerization of exo‐norbornene dimethyl propionate were systematically investigated. The low molar ratio and temperature, as well as high polarity of solvent, and long reaction time, are favorable for the enhancement of the monomer conversion, especially, the solvent have an obvious effect on the catalyst activity. The resulting poly(cis‐norbornene‐exo‐2,3‐dimethyl carboxylates) (PNB‐dimethyl carboxylates) show good solubility in common organic solvent and high thermal stability up to 360 °C. The glass transition temperature was detected by DMA at 331, 324, and 318 °C for acetate, propionate, and butyrate, respectively. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3391–3399, 2007     

Measurement of small-signal and large-signal responses of packaged laser modules at high temperature

In this paper, the pulsed injection method is extended to measure the chip temperature of various packaged laser modules, such as the DFB laser modules, the FP laser modules, and the EML laser modules. An optimal injection condition is obtained by investigating the dependence of the lasing wavelength on the width and period of the injection pulse in a relatively wide temperature range. The small-signal frequency responses and large-signal performances of packaged laser modules at different chip temperature are measured. The adiabatic small-signal modulation characteristics of packaged LD are first extracted. In the large-signal measurement, the effects of chip temperature, bias current and driving signal on the performances of the laser modules are discussed. It has been found that the large-signal performances of the EML modules depend on the different red-shift speeds of the DFB and EAM sections as chip temperature varying, and the optimal characteristics may be achieved at higher temperature.     

Smaller Output Beam Divergence in the Slowly Opened Q-Switch Operation

The mechanism of the slowly opened Q-switch operation was investigated thoroughly. Maximum energy extraction from the resonator could be optimized, and the smallest output beam divergence could be achieved. In this article, we present a detailed analysis that has numerically verified the mode-selection mechanism in the slowly opened Q-switch operation, and the degree of the smaller output laser beam divergence that has been achieved. The mechanism of the slowly opened Q-switch operation is the inherent advantage of the passive saturable absorber in this operation. We can use the maximum energy extraction and the smallest output beam divergence results of the slowly opened Q-switch operation to design and optimize various passive saturable absorbers: plastic dye sheets, LiF:F₂⁻ color center crystals, Cr4⁺: YAG crystals, RG1000 color glass filters, and the single crystal semiconductor saturable absorber wafers that are in developed in our microchip laser systems.     

Synthesis of poly(p‐phenylene sulfide) from bis(4‐bromophenyl) disulfide

Improved reaction conditions for the preparation of poly(p‐phenylene sulfide) (PPS) directly from bis(4‐bromophenyl) disulfide (BBD) have been established. Heating BBD with magnesium metal afforded only a low molecular weight polymer. PPS with a melting temperature around 280 °C was obtained from BBD in the presence of sodium carbonate or zinc metal. The best results were obtained with the addition of a catalytic amount of KI to the zinc–BBD mixture. Polymers prepared by the above methods are semicrystalline and dissolve in 1‐chloronaphthalene and have properties comparable to commercial PPS. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 900–904, 2006     

Chemically modified proton‐conducting membranes based on sulfonated polyimides: Improved water stability and fuel‐cell performance

A series of branched/crosslinked sulfonated polyimide (B/C‐SPI) membranes were prepared and evaluated as proton‐conducting ionomers based on the new concept of in situ crosslinking from sulfonated polyimide (SPI) oligomers and triamine monomers. Chemical branching and crosslinking in SPI oligomers with 1,3,5‐tris(4‐aminophenoxy)benzene as a crosslinker gave the polymer membranes very good water stability and mechanical properties under an accelerated aging treatment in water at 130 °C, despite their high ion‐exchange capacity (2.2–2.6 mequiv g^?1). The resulting polymer electrolytes displayed high proton conductivities of 0.2–0.3 S cm^?1 at 120 °C in water and reasonably high conductivities of 0.02–0.03 S cm^?1 at 50% relative humidity. In a single H₂/O₂ fuel‐cell system at 90 °C, they exhibited high fuel‐cell performances comparable to those of Nafion 112. The B/C‐SPI membranes also displayed good performances in a direct methanol fuel cell with methanol concentrations as high as 50 wt % that were superior to those of Nafion 112. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3751–3762, 2006     

Lithographic design of photosensitive polyarylates based on reaction development patterning

The factors affecting pattern‐forming properties in reaction development patterning were examined with polyarylates with various bisphenol moieties. The developability of the photosensitive polyarylates was dependent on the properties of the subtituent (R) in the bisphenol moieties. The development time decreased in the following order: R?C(CH₃)₂ > fluorenyl unit ? phenolphthalein unit > C(CF₃)₂ > SO₂. This order agreed with that of the reactivity between the polyarylates and ethanolamine, and these orders can be explained by pK_a of the bisphenol used to prepare the polyarylates. The development with NH₂? R′? OH resulted in successful positive‐tone pattern formation. However, pattern formation with the developers containing NH₂? R′? OCH₃ was unsuccessful. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2694–2706, 2006     

Investigation of sulfonated poly(ether ether ketone sulfone)/heteropolyacid composite membranes for high temperature fuel cell applications

The sulfonated poly(ether ether ketone sulfone) (SPEEKS)/heteropolyacid (HPA) composite membranes with different HPA content in SPEEKS copolymers matrix with different degree of sulfonation (DS) were investigated for high temperature proton exchange membrane fuel cells. Composite membranes were characterized by Fourier transfer infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). FTIR band shifts suggested that the sulfonic acid groups on the copolymer backbone strongly interact with HPA particles. SEM pictures showed that the HPA particles were uniformly distributed throughout the SPEEKS membranes matrix and particle sizes decreased with the increment of copolymers' DS. The holes were not found in SPEEKS‐4/HPA30 (consisting of 70% SPEEKS copolymers with DS = 0.8 and 30% HPA) composite membrane after composite membranes were treated with boiling water for 24 h. Thermal stabilities of the composite membranes were better than those of pure sulfonated copolymers membranes. Although the composite membranes possessed lower water uptake, it exhibited higher proton conductivity for SPEEKS‐4/HPA30 especially at high temperature (above 100 °C). Its proton conductivity linearly increased from 0.068 S/cm at 25 °C to 0.095 S/cm at 120 °C, which was higher than 0.06 S/cm of Nafion 117. In contrast, proton conductivity of pure SPEEKS‐4 membrane only increased from 0.062 S/cm at 25 °C to 0.078 S/cm at 80 °C. At 120 °C, proton conductivity decreased to poor 0.073 S/cm. The result indicated that composite membranes exhibited high proton conductivity at high temperature. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1967–1978, 2006     

Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF‐TrFE) were exposed to vacuum UV (115–300 nm VUV) and γ‐radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after γ‐irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV‐irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV‐irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d₃₃ piezoelectric coefficients and D‐E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D‐E loops after exposure to either γ‐ or VUV‐radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV‐irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV‐radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3253–3264, 2006     

Polymer electrolyte membranes for the direct methanol fuel cell: A review

The direct methanol fuel cell (DMFC) has the potential to replace lithium‐ion rechargeable batteries in portable electronic devices, but currently experiences significant power density and efficiency losses due to high methanol crossover through polymer electrolyte membranes (PEMs). Numerous publications document the synthesis and characterization of new PEMs for the DMFC. This article reviews this research, transport phenomena in PEMs, and experimental techniques used to evaluate new PEMs for the DMFC. Although many PEMs do not show significant improvements over Nafion®, the benchmark PEM in DMFCs, experimental results show that several new PEMs exhibit lower methanol crossover at similar proton conductivities and/or higher DMFC power densities. These results and recommendations for future research are discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Parts B: Polym Phys 44: 2201–2225, 2006