含纳米添加剂的润滑体系在摩擦过程中的接触电阻研究

采用UMT-2型微摩擦磨损试验机考察了4种纳米颗粒LaF3、Ag、SiO2 及Al2O3作为润滑油添加剂在摩擦过程中的接触电阻随时间变化的情况,并由此监测摩擦副表面的成膜状况;采用X射线光电子能谱仪分析4种纳米添加剂润滑下磨损表面典型元素的化学状态,并结合接触电阻测试结果分析纳米油润滑添加剂的润滑机理.结果表明:接触电阻测试能够适时监测添加剂在摩擦副表面的成膜过程,4种纳米润滑油添加剂在边界润滑条件下均能够在磨损表面沉积成膜,其在试验过程中的化学状态没有发生变化,但4种纳米润滑油添加剂在摩擦过程中的成膜性能不同,Ag和LaF3在摩擦过程中的沉积速率、沉积膜厚度及其在摩擦副表面的结合强度优于SiO2和Al2O3.     

套管磨损三维表面形貌恢复及其机理分析

在DCWT-1000型套管摩擦磨损试验机上进行了套管摩擦磨损试验,研究深井、超深井中"冲击-滑动"复合磨损对套管磨损行为的影响,采用三维表面形貌测试仪、光学显微镜及扫描电子显微镜观察分析了在不同载荷条件下套管磨损表面的微观结构和表面形貌,在此基础上对套管磨损表面进行了三维恢复并计算套管磨损表面的主要形貌参数,探讨了套管磨损表面的磨损机理.结果表明:套管的磨损性能与载荷有关;在不同载荷条件下,套管磨损表面的三维形貌具有不同特点,且主要的表面形貌参数与载荷呈现出较好的相关性,证明了三维形貌分析方法能够真实反映套管磨损表面的情况;当冲击载荷和频率不大时,套管的磨损机制以磨粒磨损为主,兼有粘着磨损,随着冲击载荷和频率增加,套管磨损表面出现明显粘着剥落和疲劳剥落迹象,并出现疲劳裂纹扩展和连通,套管的磨损机制向粘着磨损和疲劳磨损转化,磨损趋向严重.     

Interpretation of Strengthening Mechanism of Densified Wood from Supramolecular Structures

In this study, densified wood was prepared by hot pressing after partial lignin and hemicellulose were removed through alkaline solution cooking. The tensile strength and elastic modulus of densified wood were improved up to 398.5 MPa and 22.5 GPa as compared with the original wood, and the characterization of its supramolecular structures showed that the crystal plane spacing of the densified wood decreased, the crystallite size increased, and the maximum crystallinity (CI) of cellulose increased by 15.05%; outstandingly, the content of O(6)H⋯O(3′) intermolecular H-bonds increased by approximately one-fold at most. It was found that the intermolecular H-bond content was significantly positively correlated with the tensile strength and elastic modulus, and accordingly, their Pearson correlation coefficients were 0.952 (p < 0.01) and 0.822 (p < 0.05), respectively. This work provides a supramolecular explanation for the enhancement of tensile strength of densified wood.     

Role of Natural Compounds and Target Enzymes in the Treatment of Alzheimer’s Disease

Alzheimer’s disease (AD) is a progressive neurological condition. The rising prevalence of AD necessitates the rapid development of efficient therapy options. Despite substantial study, only a few medications are capable of delaying the disease. Several substances with pharmacological activity, derived from plants, have been shown to have positive benefits for the treatment of AD by targeting various enzymes, such as acetylcholinesterase (AChE), butyrylcholinesterase (BuChE), β-secretase, γ-secretase, and monoamine oxidases (MAOs), which are discussed as potential targets. Medicinal plants have already contributed a number of lead molecules to medicine development, with many of them currently undergoing clinical trials. A variety of medicinal plants have been shown to diminish the degenerative symptoms associated with AD, either in their raw form or as isolated compounds. The aim of this review was to provide a brief summary of AD and its current therapies, followed by a discussion of the natural compounds examined as therapeutic agents and the processes underlying the positive effects, particularly the management of AD.     

Salpianthus macrodontus Extracts,a Novel Source of Phenolic Compounds with Antibacterial Activity against Potentially Pathogenic Bacteria Isolated from White Shrimp

This study aimed to evaluate the antibacterial activity in vitro of Salpianthus macrodontus and Azadirachta indica extracts against potentially pathogenic bacteria for Pacific white shrimp. Furthermore, the extracts with higher inhibitory activity were analyzed to identify compounds responsible for bacterial inhibition and evaluate their effect on motility and biofilm formation. S. macrodontus and A. indica extracts were prepared using methanol, acetone, and hexane by ultrasound. The minimum inhibitory concentration (MIC) of the extracts was determined against Vibrio parahaemolyticus, V. harveyi, Photobacterium damselae and P. leiognathi. The polyphenol profile of those extracts showing the highest bacterial inhibition were determined. Besides, the bacterial swimming and swarming motility and biofilm formation were determined. The highest inhibitory activity against the four pathogens was found with the acetonic extract of S. macrodontus leaf (MIC of 50 mg/mL for Vibrio spp. and 25 mg/mL for Photobacterium spp.) and the methanol extract of S. macrodontus flower (MIC of 50 mg/mL for all pathogens tested). Both extracts affected the swarming and swimming motility and the biofilm formation of the tested bacteria. The main phenolic compounds related to Vibrio bacteria inhibition were naringin, vanillic acid, and rosmarinic acid, whilst hesperidin, kaempferol pentosyl-rutinoside, and rhamnetin were related to Photobacterium bacteria inhibition.     

H2SO4-H2O中硝酸铜对脱硫石膏晶须生长的影响

以处理后的脱硫石膏为原料,在H₂SO₄-H₂O体系中以Cu(NO₃)₂为晶形控制剂采用水热法制备脱硫石膏晶须,探讨了Cu(NO₃)₂对脱硫石膏晶须生长的影响机理。结果表明:Cu(NO₃)₂对脱硫石膏有明显促溶作用,其中Cu²⁺可减小溶液中各离子的活度系数,使溶液中的Ca²⁺浓度增大。NO^-₃通过静电作用在Ca²⁺周围聚集并对SO^2-₄产生屏蔽作用,导致脱硫石膏继续溶解并使Ca²⁺和SO^2-₄的浓度处于相对稳定状态,有利于半水脱硫石膏晶体的形核与生长。此外,Cu²⁺还可在晶须的生长过程中选择性吸附在晶须表面,生成CuSO₄,促进了脱硫石膏的结晶生长,最终在Cu(NO₃)₂用量为2.0%(质量分数)时制备的脱硫石膏晶须长径比约为73。     

Natural Products in Preventing Tumor Drug Resistance and Related Signaling Pathways

Drug resistance is still an obstacle in cancer therapy, leading to the failure of tumor treatment. The emergence of tumor drug resistance has always been a main concern of oncologists. Therefore, overcoming tumor drug resistance and looking for new strategies for tumor treatment is a major focus in the field of tumor research. Natural products serve as effective substances against drug resistance because of their diverse chemical structures and pharmacological effects. We reviewed the signaling pathways involved in the development of tumor drug resistance, including Epidermal growth factor receptor (EGFR), Renin-angiotensin system (Ras), Phosphatidylinositol-3-kinase/protein kinase B (PI3K/Akt), Wnt, Notch, Transforming growth factor-beta (TGF-β), and their specific signaling pathway inhibitors derived from natural products. This can provide new ideas for the prevention of drug resistance in cancer therapy.     

LBO晶体超光滑表面抛光机理

胶体SiO2抛光LBO晶体获得无损伤的超光滑表面,结合前人对抛光机理的认识,探讨了超光滑表面抛光的材料去除机理,分析了化学机械抛光中的原子级材料去除机理.在此基础上,对胶体SiO2抛光LBO晶体表面材料去除机理和超光滑表面的形成进行了详细的描述,研究抛光液的pH值与材料去除率和表面粗糙度的关系.LBO晶体超光滑表面抛光的材料去除机理是抛光液与晶体表面的活泼原子层发生化学反应形成过渡的软质层,软质层在磨料和抛光盘的作用下很容易被无损伤的去除.酸性条件下,随抛光液pH值的减小抛光材料的去除率增大;抛光液pH值为4时,获得最好的表面粗糙度.     

前驱体法制备氮氧化硅纳米线及其光学性能研究

在Ni催化剂的存在下,通过SiCl4的水解氨解反应并在1300℃氨气气氛中进行热氮化处理制得了无定形氮氧化硅纳米线.产物经X射线衍射(XRD)、热重-差示扫描量热(TG-DSC)、扫描电镜(SEM)、透射电镜(TEM)、能量色散谱(EDS)和选区电子衍射(SAED)等表征手段进行分析,结果表明纳米线为无定形结构,直径为100～150nm.在波长为220nm的光激发下,产物的光致发光光谱(PL)在563nm和289nm处分别出现了一个强的绿光发光峰和一个弱的紫光发光峰.对纳米线的生长机理进行分析,表明纳米线的生长遵循气-液-固(VLS)机制控制模式.     

不同形貌氮化硅纳米结构的制备与表征

分别通过VLS和VS生长机制得到了Si3N4纳米线和纳米带.产物经X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)等表征手段进行了分析.FTIR图谱表明它们在800～1100cm-1的波数范围内有一个宽的吸收带,这是Si-N键伸缩振动模式的典型吸收带.它们的室温光致发光图谱显示,在420nm左右都有一很强的发射带,表明其将在纳米光电器件中有潜在应用.另外,Si3N4纳米线发光峰与纳米带的发光相比有少许蓝移(蓝移约4nm),这可能和晶须尺寸的少许差别有关.至于纳米带的发光强度大于纳米线的原因,可能是纳米带的比表面积相对较大,有利于悬键的形成,从而导致材料结构内缺陷的浓度较大.