溶胶凝胶法制氧化铝负载铜基超细粒子催化剂的研究

采用溶胶凝胶法制氧化铝负载铜基超细粒子催化剂的制备了氧化铝负载的铜基超细粒子催化剂，用ＴＧ－ＤＴＡ，ＸＲＤ，ＢＥＴ以及ＴＥＭ等技术手段，对催化剂的物相结构，表面孔结构，粒子形貌以及催化性能等进行了研究。结果表明，利用溶胶凝胶法，可以直接帛备出高比表面积，低堆积密度的纤维状纳米级负载型Ｃｕ／Ａｌ２Ｏ３超细粒子；活性组分以远低于纳米级的微晶粒子簇状态，均匀地分散在纳米级氧化铝载体表面上，而且在低于５０     

Ni-B和Ni-Ce-B超细非晶态合金的退火晶化及其催化性能

 采用XAFS,XRD和DTA方法研究了Ni－B和Ni－Ce－B超细非晶态合金在退火过程中的结构变化及其结构与催化性能的关系．活性结果表明,在退火温度为623K时,Ni－B和Ni－Ce－B样品的苯加氢催化反应转化率最高,分别为63％和81％,0．3％Ce的掺入提高了Ni－Ce－B的催化活性．DTA结果表明,Ni－B超细非晶态合金在598和653K有两个晶化峰,而Ni－Ce－B样品有548,603,696和801K四个晶化峰．XAFS和XRD结果进一步说明,在573K退火时,Ni－B样品晶化生成晶态Ni3B和纳米晶Ni,此时Ni－Ce－B仅有少量晶态Ni3B生成．在673K退火时,Ni－B样品中的Ni3B开始分解生成晶态Ni,同时纳米晶Ni聚集并形成大颗粒晶态Ni,而Ni－Ce－B样品晶化生成晶态Ni3B和纳米晶Ni．在773K和更高的温度退火处理后,Ni－B样品中Ni的局域环境结构与金属Ni箔基本一致,但Ni－Ce－B样品晶化生成的Ni晶格有较大畸变,同时Ni3B并未分解．说明0．3％的Ce对提高Ni－Ce－B样品的稳定性有显著作用．本文首次报道了Ni－B和Ni－Ce－B超细非晶态合金中苯加氢催化活性中心为纳米晶Ni和类似于金属Ni的Ni－B非晶态合金．     

CuO/γ-Al2O3单分散催化剂的XAFS研究

采用XAFS方法研究浸渍法制备并于低温焙烧的CuO/γ-Al2O3催化剂的局域结构.对于CuO负载量小于单层分散阈值的CuO/γ-Al2O3(0.4 mmol/100 m2),结果表明,CuO物种是以层状分散的孤立原子簇存在于γ-Al2O3载体表面,其第一近邻Cu－O配位环境的结构与晶态CuO的相似,键长和配位数分别为0.195 nm和4.对于CuO负载量等于单层分散阈值的CuO/γ-Al2O3(0.8 mmol/100 m2),已有少量的CuO纳米颗粒生成.对于CuO负载量大于单层分散阈值的CuO/γ-Al2O3(1.2 mmol/100 m2),其结构与多晶CuO的相近.基于CuO在γ-Al2O3载体上的三种不同分散状态的结构特点,我们提出了CuO/γ-Al2O3催化剂的结构模型.     

Control of optical properties of gel-derived oxide coating films containing fine metal particles

Control of the optical properties of gel-derived oxide films containing fine metal particles is described. The duration of the aging of Si(OC₂H₅)₄-derived sols and the amount of water for hydrolyzing Si(OC₂H₅)₄ were found to greatly affect the size and the shape of Au particles formed in the silica matrix, and accordingly the optical absorption of the Au/SiO₂ composite films. Employing dielectric media with high refractive indices like TiO₂ was shown to shift the absorption peak of Au particles to longer wavelengths. Pd/TiO₂ and Pt/TiO₂ composite films showed absorption in the visible region.     

核-壳型聚丙烯酸酯复合乳液

简述了核-壳型聚丙烯酸酯复合乳液的合成方法、形态及其影响因素与判断方法、结构与性能等方面的研究进展;认为核-壳型复合乳液膜机械性能优良的原因是:核、壳两相间存在的过渡区适当地抑制了二者的相分离。     

Core/shell particles containing 3-(methacryloxypropyl)-trimethoxysilane in the shell: synthesis, characterization, and application

In comparison to the corresponding single-component counterparts, core/shell particles are widely used due to their better physical and chemical properties. The surface properties of core/shell particles evidently play an important role in the process of application. It is easy to deduce that surface properties mostly depend on the properties of the component in the shell. Therefore, desirable materials of shell are very significant for the study of composite materials, especially in core/shell field. It is well known that polysiloxane has excellent properties, such as the water repellency, high flexibility, low surface energy, and biocompatibility. Its application, however, is limited due to poor cohesiveness and poor film-forming properties. Recently, much endeavor has been made to overcome such flaws. It is found that polyacrylate is commonly considered for its good cohesiveness and excellent film-forming property. The combination of polysiloxane and polyacrylate has been shown to be important in the composite material field, especially as core/shell particles. Unfortunately, their hydrophobicity is considerably different and thus, the core/shell particles consisting of polyacrylate (PA)/polysiloxane (PSi) are hard to prepare by general seeded emulsion polymerization, and are also scarcely available in the literature. In this study, the new core/shell PA/PSi particles with poly(butyl methacrylate) (PA) as the core and poly(3-(methacryloxypropyl)-trimethoxysilane) (PSi) as the shell were prepared by dispersion polymerization under the kinetically controlled conditions. The characterization of the particles by TEM, DSC, particle size analyzer as well as static contact angle confirmed the formation of core/shell structure. The application of core/shell (PA/PSi) particles also has been considered and discussed here.TEM micrographs of core/shell (PA/PSi) particles.     

水合醋酸铈直接热分解制备超细氧化铈及其抛光性能

Ultra fine ceria was prepared by calcining hydrate cerium acetate. The effects of pyrolysis temperature on the particle size, morphology, specific surface area and loose packing density of ceria were investigated, and the removal rate of optical glasses polishing by ceria was determined. The results show that with the increase of pyrolysis temperature, the loose deposit density and crystallinity increases and the specific surface area decreases, however, the particle size decreases firstly and then increases, the minimum medium particle size D₅₀ is 0.47 μm at pyrolysis temperature of 1 000 ℃. The SEM images of ceria prepared by the decomposition at 800 ℃ or at 1 100 ℃ show porous powders or quasi-sphere small particles with loosely agglomeration, respectively. It was found that the removal rate varied with pyrolysis temperature in preparation of ceria and the property of glass polished. The removal rate for three kinds of glasses was in the order of ZF7> F1> K9, and the maximum value appeared at around 1 000 ℃ for ZF7 and F1, and at around 1 100 ℃ for K9.     

Preparation and characterization of NiFe bimetallic micro-particles and its composite with silica shell

Magnetic NiFe particles were synthesized through hydrothermal method using hydrazine as reductant. Composite particles with core-shell structure were further achieved by depositing silicon dioxide generated via carbonation decomposition of sodium silicate solution on the surface of magnetic cores. Characterized by XRD, the Ni₉Fe particles are of fcc-type structure, and the structure of magnetic cores in composite particles was maintained despite being covered by SiO₂ shell. The existence of SiO₂ shells in the composite particles were demonstrated by SEM, EDS and IR. The results from TG and VSM indicated that the shell structure affected the physiochemical properties. The composite particles exhibited remarkable resistance to oxidation in comparison with Ni₉Fe particles due to being protected by SiO₂ shell. Meanwhile, both of them are soft magnetic materials, but Ms, Mr and Hc in Ni₉[email protected]₂ particle decreased compared with magnetic NiFe particles. The formation mechanisms of Ni₉Fe micro-particles and composite Ni₉Fe particles were discussed.     

Thermal Emulsion Polymerization without any Conventional Initiators and Emulsifiers

Stable poly(styrene-co-sodium styrene sulfonate) (P(St-NaSS) nanoparticles with broader size distribution were synthesized by thermal emulsion polymerization without any conventional initiators and emulsifiers. The obtained polymer nanoparticles have higher ξ potential, and the particle sizes have broad distribution. The stability of polymer particles originated from the addition of small amounts of ionic comonomer, NaSS, which can act as an emulsifier in somewhat. The monomer conversion could reach up to about 28 wt% in 48 h, and did not increase by further polymerization when higher polymerization temperature (120 ℃) was employed. This polymerization system may be give some further understand for mechanism of emulsion polymerization.     

A New Kind of Void Soap-free P（MMA-EA-MAA） Latex Particles

Soap-flee P(MMA-EA-MAA) particles with narrow size distribution were synthesized by seeded emulsion polymerization of methyl methacrylate (MMA), ethyl acrylate (EA) and methacrylic acid (MAA), and large voids inside the particles were generated by alkali posttreatment in the presence of 2-butanone. Results indicated that the size of void and theparticle volume were related with the amount of 2-butanone. The generation mechanism of voids was proposed.