Electrocatalytic Reduction of H2O2 and Oxygen on the Surface of Thionin Incorporated onto MWCNTs Modified Glassy Carbon Electrode: Application to Glucose Detection

A new H₂O₂ enzymeless sensor has been fabricated by incorporation of thionin onto multiwall carbon nanotubes (MWCNTs) modified glassy carbon electrode. First 50 μL of acetone solution containing dispersed MWCNTs was pipetted onto the surface of GC electrode, then, after solvent evaporations, the MWCNTs modified GC electrode was immersed into an aqueous solution of thionin (electroless deposition) for a short period of time <5–50 s. The adsorbed thin film of thionin was found to facilitate the reduction of hydrogen peroxide in the absence of peroxidase enzyme. Also the modified electrode shows excellent catalytic activity for oxygen reduction at reduced overpotential. The rotating modified electrode shows excellent analytical performance for amperometric determination of hydrogen peroxide, at reduced overpotentials. Typical calibration at ?0.3 V vs. reference electrode, Ag/AgCl/3 M KCl, shows a detection limit of 0.38 μM, a sensitivity of 11.5 nA/μM and a liner range from 20 μM to 3.0 mM of hydrogen peroxide. The glucose biosensor was fabricated by covering a thin film of sol–gel composite containing glucose oxides on the surface of thionin/MWCNTs modified GC electrode. The biosensor can be used successfully for selective detection of glucose based on the decreasing of cathodic peak current of oxygen. The detection limit, sensitivity and liner calibration rang were 1 μM, 18.3 μA/mM and 10 μM–6.0 mM, respectively. In addition biosensor can reach 90% of steady currents in about 3.0 s and interference effect of the electroactive existing species (ascorbic acid–uric acid and acetaminophen) is eliminated. The usefulness of biosensor for direct glucose quantification in human blood serum matrix is also discussed. This sensor can be used as an amperometric detector for monitoring oxidase based biosensors.     

Highly Sensitive Amperometric Glucose Biosensor Based on Glassy Carbon Electrode with Copper/Palladium Coating

A highly sensitive amperometric glucose biosensor based on immobilizing glucose oxidase in electropolymerized poly(o‐phenylenediamine) film on glassy carbon electrode coated sequentially with copper and palladium layers has been developed. The steady‐state amperometric response to glucose was determined by means of the oxidation of hydrogen peroxide generated by the enzymatic reaction at a potential of either +0.70 or +0.40 V (vs. Ag|AgCl reference). The deposited copper/palladium layer showed great enhancement in the performance of the enzyme electrode, possibly due to its better electrocatalytic activity for hydrogen peroxide oxidation and large surface area. Effects of the relative loading of palladium, enzyme and polymer on the electrode performance were examined in detail. Sensitivity and detection limit for glucose determinations at +0.70 V were about 7.3 μA/mM and 0.1 μM, respectively. A wide linear range up to 6.0 mM glucose could be achieved. Electrode performance was superior to similar works reported in the literature. The response time was less than 2 s and its lifetime was longer than three months. The permeable polyphenylenediamine film also offered good anti‐interference ability to ascorbic acid, uric acid and acetaminophen, especially when a detection potential of +0.40 V was employed.     

Retronasal Aroma of Beef Pate Analyzed by a Chewing Simulator

In retronasal aroma, the targeted aroma compounds are released from food during chewing. The changes in the food structures during chewing strongly influence the release of the compounds, therefore affecting the perception of food. Here, the relationship between retronasal aroma and food deliciousness based on the physicochemical properties of aroma compounds was examined. We considered the consumption of solid foods and the effect of oral parameters in elderly people. Beef pate was used as a model food sample to study the effect of the release of aroma compounds under controlled in vitro mastication and salivation conditions using a chewing simulator. We identified the effects of coexisting ingredients such as beef fat on the time course behavior of the release of aroma compounds. In particular, the release of the middle types of aromas was significantly faster with stronger chewing force, and higher with a high fat content of the sample. In addition, a larger release intensity was observed when soy proteins were partially substituted for beef proteins. Using an appropriate model saliva, a change in the salting-out effect from the saliva composition was found to be a factor, which could explain the lowering of aroma sensation in an elderly person.     

化学气相沉积法制备大面积二维材料薄膜:方法与机制

近年来,二维层状材料由于其丰富的材料体系和独特的物理化学性质而受到人们的广泛关注.后摩尔时代要求器件高度集成化,大面积、高质量的二维材料可以保证器件中结构和电子性能的连续性.要实现二维材料工业级别的规模化生产,样品的可控制备是其前提.化学气相沉积是满足上述要求的一种强有力的方法,已广泛应用于二维材料及其复合结构的生长制...     

低温缓冲层对氧化锌薄膜质量的影响

利用金属有机化学气相沉积(MOCVD)法,在Si衬底上外延生长ZnO薄膜。为了改善氧化锌薄膜的质量,首先在Si衬底上生长低温ZnO缓冲层,然后再生长高质量的ZnO薄膜。通过XRD、SEM、光致发光(PL)光谱的实验研究,发现低温ZnO缓冲层可有效降低ZnO薄膜和Si衬底之间的晶格失配以及因热膨胀系数不同引起的晶格畸变。利用低温缓冲层生长的ZnO薄膜的(002)面衍射峰的强度要比直接在Si上生长的ZnO薄膜样品的高,并且衍射峰的半高宽也由0.21°减小到0.18°,同时有低温缓冲层的样品室温下的光致发光峰也有了明显的增高。这说明利用低温缓冲层生长的ZnO薄膜的结晶质量和光学性质都得到了明显改善。     

薄膜生长速率对有机光伏器件性能的影响

采用真空热蒸发镀膜的方法制备了酞菁铜(CuPc)和富勒烯(C60)构成的平面异质结结构光伏器件,并初步研究了CuPc薄膜生长速率对器件光伏性能的影响,我们发现以较大薄膜生长速率制备的器件表现出较大的短路电流和能量转换效率。X射线衍射和原子力显微镜观察的结果表明生长速率较大的CuPc薄膜结晶相含量较少,薄膜结构较均匀、致密、平整,这可能使得CuPc薄膜激子扩散和载流子迁移特性得到提高,也可能改善其与C60受主薄膜和ITO阳极的接触,并有利于载流子的分离和收集,从而表现出较好的光伏特性。     

甲烷浓度对碳化硅基底金刚石薄膜摩擦性能影响

利用热丝化学气相沉积法(HFCVD)在碳化硅基底上制备金刚石薄膜,采用场发射扫描电子显微镜、拉曼光谱仪、原子力显微镜研究了在不同甲烷浓度条件下制备的金刚石薄膜表面形貌及物相组成,在干摩擦条件下通过往复式摩擦磨损实验测试并计算了已制备金刚石薄膜的摩擦系数和磨损率,结合物相分析及摩擦磨损实验结果分析了甲烷浓度的改变对金刚石薄膜摩擦磨损性能的影响。结果表明,由于甲烷气体含量的升高,金刚石薄膜结晶质量下降,薄膜由微米晶向纳米晶转变。摩擦磨损实验结果显示:3%甲烷浓度条件下制备的金刚石薄膜耐磨性较好,磨损率为2.2×10^-7 mm³/mN;5%甲烷浓度条件下制备的金刚石薄膜摩擦系数最低(0.032),磨损率为5.7×10^-7 mm³/mN,制备的金刚石薄膜的耐磨损性能相比于碳化硅基底(磨损率为9.89×10^-5 mm³/mN)提升了两个数量级,显著提高了碳化硅基底的耐磨性。     

平台式和斜坡式表面放电辐射源放电特性的比较

 介绍了平台式和斜坡式两种结构的表面放电辐射源,研究了在1.0 μF和1.5 μF储能电容、15~30 kV充电电压等实验条件下两种辐射源的放电特性,并对实验结果进行了比较分析。得到如下结论：对于斜坡式辐射源,增加电极间距可导致放电回路面积增大,因此等效电阻和等效电感也将增加;在相同电压及电容值条件下,斜坡式辐射源的放电电流、平均沉积功率均小于平台式辐射源的相应值,但放电沉积效率略大;电压升高使放电周期、电流达到峰值时间及放电沉积效率呈减小趋势,对于同一种辐射源,使用1.5 μF电容时放电回路参数更加匹配,放电沉积效率得到提高。     

采用旋转涂膜法制备基底生长的定向碳纳米管阵列

 采用化学气相沉积技术,利用旋转涂膜法制备催化剂基底材料,通过对涂膜过程中的角速度、旋转时间以及基底还原过程中温度的控制改变催化剂颗粒的分布状态,获得了粒径均匀分布的催化剂基底,该基底上催化剂颗粒集中分布在47～62 nm区间,再利用该基底生长出定向碳纳米管阵列。运用扫描电镜、透射电镜、拉曼光谱仪对样品进行了表征。结果表明旋转涂膜法制备的基底平整性好于普通的滴膜法,且较其它基底制备方法具有简单易控、可使催化剂均匀分散等特点。利用该基底制备的碳纳米管阵列定向性良好。     

Dielectric Properties Investigation of Metal–Insulator–Metal (MIM) Capacitors

This study presents the construction and dielectric properties investigation of atomic-layer-deposition Al₂O₃/TiO₂/HfO₂ dielectric-film-based metal–insulator–metal (MIM) capacitors. The influence of the dielectric layer material and thickness on the performance of MIM capacitors are also systematically investigated. The morphology and surface roughness of dielectric films for different materials and thicknesses are analyzed via atomic force microscopy (AFM). Among them, the 25 nm Al₂O₃-based dielectric capacitor exhibits superior comprehensive electrical performance, including a high capacitance density of 7.89 fF·µm⁻², desirable breakdown voltage and leakage current of about 12 V and 1.4 × 10⁻¹⁰ A·cm⁻², and quadratic voltage coefficient of 303.6 ppm·V⁻². Simultaneously, the fabricated capacitor indicates desirable stability in terms of frequency and bias voltage (at 1 MHz), with the corresponding slight capacitance density variation of about 0.52 fF·µm⁻² and 0.25 fF·µm⁻². Furthermore, the mechanism of the variation in capacitance density and leakage current might be attributed to the Poole–Frenkel emission and charge-trapping effect of the high-k materials. All these results indicate potential applications in integrated passive devices.