The role of As2O3 on the stability and some physical properties of PbO-Sb2O3 glasses

PbO-Sb₂O₃ glasses added with different concentrations of As₂O₃ (10-55 mol%) were prepared to understand their IR spectra, elastic properties (Young's modulus E, Shear modulus G, microhardness H), optical absorption and dielectric properties (constant ε, loss tan δ, ac conductivity σ_ac over a moderately wide range of frequency and temperature and breakdown strength in air medium at room temperature). Results have indicated that the structure of the PbO-Sb₂O₃-As₂O₃ glass is more rigid when the concentration of As₂O₃ is around 40 mol%.     

掺杂两种荧光染料的有机红光电致发光器件

制作了掺杂rubrene和4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9,enyl)-4H-pyran(DCJTB)两种荧光染料的红光有机电致发光器件。N,N’-diphenyl-N,N’-bis(1-naphthyl)-(1,1’-biphenyl)-4,4’-diamine(NPB)和掺杂的Tri-(8-hydroxyquinoline)aluminum(Alq3)分别作为空穴和电子传输层。我们发现掺rubrene和DCJTB的器件性能与只掺DCJTB的器件性能相比有所提高。器件性能的改善是因为掺入的rubrene能够促进从Alq3到DCJTB的能量转移。根据荧光衰减曲线,计算出从Alq3到DCJTB、从Alq3到rubrene以及从rubrene到DCJTB的能量转移速率分别为1.04×109,3.89×109,2.79×109s-1。可以看出能量通过rubrene从Alq3到DCJTB的转移速率是能量直接从Alq3到DCJTB的2.7倍。     

过渡金属表面γ-氨丙基三甲氧基硅烷膜的研究

本文对在过渡金属铁、镍电极表面制备得到的γ-氨丙基三甲氧基硅烷(γ-APS)膜进行了研究。实验中对硅烷膜用X-射线光电子能谱(XPS)、现场表面增强拉曼散射光谱(SERS)和原子力显微镜(AFM)进行了表征。X-射线光电子能谱(XPS)的结果发现存在两个N1s峰,表明γ-APS膜中的氨基有两种存在方式:自由氨基和质子化氨基。实验中还发现现场表面增强拉曼散射光谱(SERS)是研究金属/γ-APS体系中界面层结构非常有效的手段,SERS结果表明硅醇羟基和氨基发生了竞争吸附,且γ-APS分子在外加电位等条件的影响下吸附状态会发生一定变化。原子力显微镜(AFM)的表征结果在微观上显示电极表面的γ-APS膜上形成了一种较规则的微孔结构,这种结构可能与基底的性质有关。     

新核素278113的基态特性及其α衰变链的研究

用形变的相对论平均场模型,Skyrme-Hartree-Fock模型及宏观-微观模型研究了新核素²⁷⁸113及其α衰变链的α衰变能和半衰期.计算的α衰变能同实验数据比较符合,相应的半衰期也在合理的范围内.计算进一步表明形变对超重核的基态性质有重要影响.     

Crystal and Molecular Structure of <Emphasis Type="Italic">Bis</Emphasis>(2,3-pentamethylene-3,4-dihydro-4-oxoquinazolinium) Tetrachlorocuprate(II) Sesquihydrate

The structure of bis-(2,3-pentamethylene-3,4-dihydro-4-oxoquinazolinium) tetrachlorocuprate (II) sesquihydrate, (C₁₃H₁₅N₂O)₂[CuCl₄]·1.5H₂O, was determined by single crystal X-ray diffraction. In contrast to the previously studied analogs, the compound contains crystallization water molecules.Original Russian Text Copyright © 2004 by K. K. Turgunov, B. Tashkhodzhaev, L. V. Molchanov, and Kh. M. Shakhidoyatov__________Translated from Zhurnal Strukturnoi Khimii, Vol. 45, No. 5, pp. 955–959, September–October, 2004.     

A numerical and experimental investigation of the interactions between a non‐uniform planar array of incompressible free jets

The interaction between multiple incompressible air jets has been studied numerically and experimentally. The numerical predictions have been first validated using experimental data for a single jet configuration. The spreading features of five unequal jets in the configuration of one larger central jet surrounded by four smaller equi‐distant jets, have been studied, for different lateral spacing ratios of 1.5, 2.0 and 2.5 and a central jet Reynolds number of 1.24×105 (corresponding to a Mach number of 0.16). Flow of five equal jets has also been simulated, for the sake of comparison. The jet interactions commence at an axial distance of about 3–4 diameters and complete by an axial distance of about 10 diameters for the lowest spacing ratio of 1.5. For larger spacing ratios, the length required for the start and completion of jet interaction increase. Peripheral jets bend more towards the central jet and merge at a smaller distance, when their sizes are smaller than that of the central jet. The entrainment ratio for multiple jets is higher than that for a single jet. Excellent agreement is observed between the experimental data and theoretical predictions for both mean flow field and turbulent quantities, at regions away from the jet inlet. The potential core length and initial jet development, however, are not predicted very accurately due to differences in the assumed and actual velocity profiles at the jet inlet. Copyright © 2004 John Wiley & Sons, Ltd.     

Biopolymers for biocatalysis: Structure and catalytic mechanism of hydroxynitrile lyases

Hydroxynitrile lyases catalyze the reversible cleavage of α-cyanohydrins to yield hydrocyanic acid and the corresponding aldehyde or ketone. Besides its biological interest, this class of enzymes is also of relevance in industrial biocatalysis for the enantioselective condensation of HCN with a variety of aldehydes and ketones. Several distinctly different types of hydroxynitrile lyases (HNLs) are known, which must have originated through convergent evolution from different ancestral proteins. Three-dimensional structural data are known for three classes of hydroxynitrile lyases. Insights into the reaction mechanisms emerged from a combination of structural, enzyme kinetic, spectroscopic, and molecular modeling data. For all three types of HNLs, mechanisms involving acid–base catalysis were proposed. In members belonging to the α,β-hydrolase type, the amino acid residues of the catalytic triad presumably act as general acid/base, whereas for flavine adenine dinucleotide (FAD)-dependent HNLs a single histidine residue fulfills this function. In the third type of HNL—which is related to carboxypeptidase—acid–base catalysis involves the carboxylate of the C-terminal residue. The catalytic relevance of a positive electrostatic potential in the active site was suggested in some of the mechanistic proposals. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 479–486, 2004     

Stereological simulations of asymmetric polymerization in channels of bile acid inclusion compounds: A detailed analysis of the monomer arrangements in the channels

We studied simulations by computer graphics to estimate the steric mechanism of the asymmetric polymerization of prochiral diene monomers in channels of inclusion compounds of steroidal bile acids, such as deoxycholic acid (DCA) and cholic acid. We applied a hierarchization method to interpret the crystal structures of bile acids, clarifying that the chiral host molecules associated to form characteristic 2₁-helical assemblies with uneven surfaces. A detailed analysis of the uneven channels in a close-packing state indicated that there were many possible arrangements of the monomers in the channels. The plausible arrangements in the channel could explain a previous study, which showed that the polymerization in the DCA channel yielded chiral polymers with a predominant configuration from prochiral diene monomers, such as 2-methyl-trans-1,3-pentadiene. On the basis of such simulation studies of the arrangements of guest monomers in the channel, we examined a plausible steric mechanism for asymmetric inclusion polymerization. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4648–4655, 2004     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Self-bonding in an amorphous polymer below the glass transition: A T-peel test investigation

Films of amorphous polystyrene (PS) with a weight-average molecular weight (M_w) of 225 × 10³ g/mol were bonded in a T-peel test geometry, and the fracture energy (G) of a PS/PS interface was measured at the ambient temperature as a function of the healing time (t_h) and healing temperature (T_h). G was found to develop with (t_h)^1/2 at T_h = T_g-bulk − 33 °C (where T_g-bulk is the glass-transition temperature of the bulk sample), and log G was found to develop with 1/T_h at T_g-bulk − 43 °C ≤ T_h ≤ T_g-bulk − 23 °C. The smallest measured value of G = 1.4 J/m² was at least one order of magnitude larger than the work of adhesion required to reversibly separate the PS surfaces. These three observations indicated that the development of G at the PS/PS interface in the temperature range investigated (<T_g-bulk) was controlled by the diffusion of chain segments feasible above the glass-transition temperature of the interfacial layer, in agreement with our previous findings for fracture stress development at several polymer/polymer interfaces well below T_g-bulk. Close values of G = 8–9 J/m² were measured for the symmetric interfaces of polydisperse PS [M_w = 225 × 10³, weight-average molecular weight/number-average molecular weight (M_w/M_n) = 3] and monodisperse PS (M_w = 200 × 10³, M_w/M_n = 1.04) after healing at T_h = T_g-bulk − 33 °C for 24 h. This implies that the self-bonding of high-molecular-weight PS at such relatively low temperatures is not governed by polydispersity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1861–1867, 2004