Novel route to synthesis of allyl starch and biodegradable hydrogel by copolymerizing allyl‐modified starch with methacrylic acid and acrylamide

Maize starch was modified by allyl chloride adopting an interfacial reaction technique with cetyltrimethyl ammonium bromide as a phase‐transfer catalyst and pyridine as an acid acceptor. The degree of substitution was determined from an increasing carbon content of the modified starch. The percentage of carbon and hydrogen of the allyl‐modified starch was estimated by elemental analysis (C, H, and N), and the product characterization was done through ¹H NMR and ¹³C NMR analyses. The allyl‐modified starch was then copolymerized with methacrylic acid and a combination of methacrylic acid and acrylamide at 50 and 70 °C with potassium persulfate as an initiator. The copolymer thus formed swelled in distilled water after neutralization with sodium carbonate. The percentage of absorption capacity of the hydrogels was determined with distilled water and 0.9% NaCl solution. The highest percentage of absorption, 6500%, was achieved for the developed hydrogel containing allyl starch and acrylic monomer in a 1.7:1 w/w ratio and acrylic monomer, namely, methacrylic acid and acrylamide in a 3.2:1 w/w ratio. The study on biodegradability of the developed hydrogel showed that the hydrogel is degradable in the presence of diastase (amylase). © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1650–1658, 2003     

Protonation constant of salicylidene (N-benzoyl)glycyl hydrazone and its coordination behaviour towards some bivalent metal ions

Protonation constant of an unsymmetrical Schiff base, salicylidene(N-benzoyl)glycyl hydrazone (SalBzGH), and formation constants of its complexes have been determined potentiometrically at different temperatures in aqueous dioxane medium. Complexes of SalBzGH with VO(IV), Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Hg(II) have been prepared. Elemental analyses, pH-metric, molar conductance, magnetic susceptibility, electronic, IR, ESR, XRD (powder) and NMR studies have been carried out to study the coordination behaviour of SalBzGH toward these metal ions. pH-metric and 1H NMR studies show the presence of two dissociable protons in the ligand. IR and NMR spectra suggest the tridentate nature of the ligand, coordinating as a uninegative species in the Mn(II) complex and as a dinegative species in all the other complexes. Presence of two different conformers of the ligand at room temperature and stabilization of a single conformer upon complex formation have been established from¹H NMR spectra of the metal-free ligand, Zn(II) and Hg(II) complexes recorded at 296 K. Electronic and ESR spectra indicate highly distorted tetragonal geometry for VO(IV) and Cu(II) complexes. XRD powder patterns of the Zn(II) complexes are indexed for an orthorhombic crystal system.     

Synthesis and characterization of functional gradient copolymers of allyl methacrylate and butyl acrylate

Functional spontaneous gradient copolymers of allyl methacrylate (A) and butyl acrylate (B) were synthesized via atom transfer radical polymerization. The copolymerization reactions were carried out in toluene solutions at 100 °C with methyl 2‐bromopropionate as the initiator and copper bromide with N,N,N′,N″,N″‐pentamethyldiethylenetriamine as the catalyst system. Different aspects of the statistical reaction copolymerizations, such as the kinetic behavior, crosslinking density, and gel fraction, were studied. The gel data were compared with Flory's gelation theory, and the sol fractions of the synthesized copolymers were characterized by size exclusion chromatography and nuclear magnetic resonance spectroscopy. The copolymer composition, demonstrating the gradient character of the copolymers, and the microstructure were analyzed. The experimental data agreed well with data calculated with the Mayo–Lewis terminal model and Bernoullian statistics, with monomer reactivity ratios of 2.58 ± 0.37 and 0.51 ± 0.05 for A and B, respectively, an isotacticity parameter for A of 0.24, and a coisotacticity parameter of 0.33. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5304–5315, 2006     

Ethylene–propylene copolymerization with bis(β‐enaminoketonato) titanium complexes activated with modified methylaluminoxane

Ethylene–propylene copolymerization, using [(Ph)NC(R₂)CHC(R₁)O]₂TiCl₂ (R₁ = CF₃, Ph, or t‐Bu; R₂ = CH₃ or CF₃) titanium complexes activated with modified methylaluminoxane as a cocatalyst, was investigated. High‐molecular‐weight ethylene–propylene copolymers with relatively narrow molecular weight distributions and a broad range of chemical compositions were obtained. Substituents R₁ and R₂ influenced the copolymerization behavior, including the copolymerization activity, methylene sequence distribution, molecular weight, and polydispersity. With small steric hindrance at R₁ and R₂, one complex (R₁ = CF₃; R₂ = CH₃) displayed high catalytic activity and produced copolymers with high propylene incorporation but low molecular weight. The microstructures of the copolymers were analyzed with ¹³C NMR to determine the methylene sequence distribution and number‐average sequence lengths of uninterrupted methylene carbons. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5846–5854, 2006     

Synthesis of biodegradable copolymers with low‐toxicity zirconium compounds. V. Multiblock and random copolymers of L‐lactide with trimethylene carbonate obtained in copolymerizations initiated with zirconium(IV) acetylacetonate

Using zirconium(IV) acetylacetonate as an initiator of lactide/trimethylene carbonate copolymerization allowed us to obtain high‐molecular‐weight copolymers with high efficiency. The reactivity ratios of the comonomers were 13.0 for lactide and 0.53 for trimethylene carbonate. Despite the large differences between the values of the reactivity ratios, copolymers with randomized chain structures were obtained. This phenomenon occurred as a result of an intensive intermolecular transesterification process proceeding along with the reaction of copolymer chain growth and modifying its final structure. Conducting the copolymerization at the relatively low temperature of about 110 °C, which minimized the influence of intermolecular transesterification, made it possible to obtain semicrystalline copolymers with multiblock structures. Increasing the temperature of copolymerization up to 180 °C was associated with strong intensification of the transesterification reactions. At this temperature, amorphous copolymers were obtained with identical compositions but highly randomized chain structures. An analysis of the chain microstructures of the obtained copolymers, determining the average length of the blocks, the intermolecular transesterification ratio, and the degree of chain randomization, was conducted by means of NMR spectroscopy. For this purpose, very specific signal assignment in the carbonyl and methylene carbon regions of the ¹³C NMR spectra to appropriate comonomer sequences of polymeric chains was performed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3184–3201, 2006     

Copolymerization of N‐vinylcaprolactam and glycidyl methacrylate: Reactivity ratio and composition control

Free‐radical copolymerizations of N‐vinylcaprolactam (VCL) and glycidyl methacrylate (GMA) were investigated to synthesize temperature‐responsive reactive copolymers with minimized compositional heterogeneity. The average copolymer composition was determined by Fourier transform infrared and nuclear magnetic resonance techniques. The reactivity ratios for VCL and GMA were found to be 0.0365 ± 0.0009 and 6.44 ± 0.36 by the Fineman–Ross method and 0.039 ± 0.006 and 6.75 ± 0.29 by the Kelen–Tudos method, respectively. When prepared by batch polymerization, VCL–GMA copolymers had a highly heterogeneous composition and fractions of different solubilities in water. The use of a gradual feeding technique, which included the sequential addition of more reactive GMA monomer into the reaction, yielded copolymers with much more homogeneous composition. The produced copolymers with 0.9 and 0.11 fractional GMA contents preserved their temperature‐responsive properties and precipitated from aqueous solutions when the temperature exceeded 31 °C. The GMA units in the VCL–GMA copolymers were capable of reacting with amino end‐functionalized poly(ethylene oxide) at room temperature to produce poly(N‐vinylcaprolactam)–poly(ethylene oxide) graft copolymers. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 183–191, 2006     

Synthesis and characterization of poly(arylene ether)s containing 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one or 6‐(4‐hydroxyphenyl)pyridazine moieties

A series of novel soluble pyridazinone‐ or pyridazine‐containing poly(arylene ether)s were prepared by a polycondensation reaction. The pyridazinone monomer, 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one ( 1 ), was synthesized from the corresponding acetophenone and glyoxylic acid in a simple one‐pot reaction. The pyridazinone monomer was successfully copolymerized with bisphenol A (BPA) or 1,2‐dihydro‐4‐(4‐hydroxyphenyl)phthalazin‐1(2H)‐one (DHPZ) and bis(4‐fluorophenyl)sulfone to form high‐molecular‐weight polymers. The copolymers had inherent viscosities of 0.5–0.9 dL/g. The glass‐transition temperatures (T_g's) of the copolymers synthesized with BPA increased with increasing content of the pyridazinone monomer. The T_g's of the copolymers synthesized from DHPZ with different pyridazinone contents were similar to those of the two homopolymers. The homopolymers showed T_g's from 202 to 291 °C by differential scanning calorimetry. The 5% weight loss temperatures in nitrogen measured by thermogravimetric analysis were in the range of 411–500 °C. 4‐(6‐Chloropyridazin‐3‐yl)phenol ( 2 ) was synthesized from 1 via a simple one‐pot reaction. 2 was copolymerized with 4,4′‐isopropylidenediphenol and bis(4‐fluorophenyl)sulfone to form high‐T_g polymers. The copolymers with less than 80 mol % pyridazinone or chloropyridazine monomers were soluble in chlorinated solvents such as chloroform. The copolymers with higher pyridazinone contents and homopolymers were not soluble in chlorinated solvents but were still soluble in dipolar aprotic solvents such as N‐methylpyrrolidinone. The soluble polymers could be cast into flexible films from solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3328–3335, 2006     

Synthesis of poly(ethylene oxide) with pending 2,2,6,6‐tetramethylpiperidine‐1‐oxyl groups and its further initiation of the grafting polymerization of styrene

A new stratagem for the synthesis of amphiphilic graft copolymers of hydrophilic poly(ethylene oxide) as the main chain and hydrophobic polystyrene as the side chains is suggested. A poly(ethylene oxide) with pending 2,2,6,6‐tetramethylpiperidine‐1‐oxyls [poly(4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl‐co‐ethylene oxide)] was first prepared by the anionic ring‐opening copolymerization of ethylene oxide and 4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl, and then the graft copolymerization of styrene was completed with benzoyl peroxide as the initiator in the presence of poly(4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl‐co‐ethylene oxide). The polymerization of styrene was under control, and comblike, amphiphilic poly(ethylene oxide)‐g‐polystyrene was obtained. The copolymer and its intermediates were characterized with size exclusion chromatography, ¹H NMR, and electron spin resonance in detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3836–3842, 2006     

Vinyl copolymers containing pendant 1,4‐distyrylbenzene and 1,3,4‐oxadiazole chromophores: Preparation and optoelectronic properties

We prepared two vinyl copolymers P1 and P2 containing pendant distyrylbenzene and aromatic 1,3,4‐oxadiazole derivatives, respectively, from their precursor poly(styrene‐ran‐4‐vinylbenzyl chloride) (M_w = 11,400, PDI = 1.18), which had been prepared by the controlled radical polymerization (RAFT). Two main chain polymers containing similar isolated distyrylbenzene ( P3) and aromatic 1,3,4‐oxadiazole ( P4 ) chromophores were also synthesized for comparative study. The resulted copolymers ( P1 – P4 ) are soluble in common organic solvents and are basically amorphous materials with 5% weight‐loss temperature higher than 360 °C. The PL spectral results reveal that the architecture of P1 prevents the formation of inter‐ or intramolecular interaction. The HOMO and LUMO levels of P2 , estimated from cyclic voltammetric data, are ?5.96 and ?3.81 eV, respectively, which are much lower than those of P1 (?5.12 and ?3.11 eV). The emission of blend from P1 and P2 are contributed mainly from distyrylbenzene fluorophore (～450 nm) owing to efficient energy transfer. Moreover, the blend exhibits three kinds of redox behavior depending on their weight ratios. The luminance and current efficiency of the EL device lpar;ITO/PEDOT/ MEH ‐ PPV + P2 /Al) are 503 cd/m² and 0.11 cd/A, which can be improved to 1285 cd/m² and 0.44 cd/A, respectively, as the weight ratio of P2 increases from 0 to 20%. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5362–5377, 2006     

Effect of excess halide on the palladium‐catalyzed insertion‐triggered radical copolymerization of methyl acrylate and 1‐hexene

[Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) is a very efficient initiator of the radical polymerization of methyl acrylate, but it is not active in the polymerization of methyl methacrylate or in the copolymerization with 1‐hexene. The addition of an excess of NBu₄Cl to solutions of [Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) provides an initiator system that copolymerizes methyl acrylate and 1‐hexene by an insertion‐triggered radical mechanism. Random copolymers are obtained with 11% incorporation of 1‐hexene in moderate yields (about 35%). Studies of the decomposition products obtained after the first insertion of methyl acrylate in the Pd? C₆F₅ bond of 1 show that the addition of excess halide in the presence of monomer favors the homolytic cleavage of the Pd? C bond, and the generation of the radicals that are active species in the polymerization, versus alternative evolution pathways. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5682–5691, 2006