Towards advanced circuit board materials: adhesion of copper foil to ultra‐high molecular weight polyethylene composite

Polyethylene based composites are attractive materials for advanced circuit board applications because of their unique combination of properties: low dielectric constant and loss factor, light weight, high flexural modulus and low thermal expansion coefficient controlled in all spatial directions. This investigation describes a process to consolidate chopped fibers of ultra‐high molecular weight polyethylene concurrently with its bonding to a copper foil. Bonding is affected by a thin sheet of low‐density polyethylene, incorporating a crosslinking agent with a concentration gradient across the sheets thickness. In this single step process, the composite material is formed and bonded to the metal foil, achieving good adhesion without the use of extraneous glue. Copyright © 2002 John Wiley & Sons, Ltd.     

Microfiltration of protein solutions at thin film composite membranes

An experimental study of the interaction of the enzyme yeast alcohol dehydrogenase (YADH) with polysulfone thin film composite microfiltration membranes (Dow-Danmark) has been carried out. It was found that the membranes adsorbed only 3/4 of a monolayer of the enzyme under the conditions studied. Even so, under filtration conditions, the membrane permeation rate decreased continuously with time. This decrease in permeation rate was due neither to concentration polarisation nor to protein adsorption alone. However, it could be quantified using the standard blocking filtration law, which describes a decrease in pore volume due to deposition of protein in the interior structure of the membrane. Reversal of the membrane, so that the supporting matrix faced the feed solution, gave more stable permeation rates. Implications for the microfiltration of industrial fermentation broths are discussed.     

PEO-LiClO_4-ZSM5 composite polymer electrolyte (IV): Polarized optical microscopy study

All solid-state lithium polymer batteries may be one of the best choices for the future electrochemical power source, characterized by high energy densities, good cyclability, reliability and safety[1,2]. Owing to its potential capability to replace the t…     

TiO2与ZnO复合纳米结构电极的光电化学研究

利用尿素加压共沉淀法以Ti(SO4)2与Zn(NO3)2为原料制备了TiO2-ZnO复合纳米粒子, 其纳米结构电极的光电化学研究结果表明, 反应物摩尔比为3∶1, 于530 ℃煅烧制备的复合纳米结构电极的光电转换效率最高. 对吸附染料RuL2(SCN)2∶2TBA的纳米结构TiO2和各种复合纳米粒子的纳米结构电极进行光电研究的结果表明, 染料对各纳米结构电极都起到了敏化作用, 其中也是由反应物摩尔比为3∶1, 于530 ℃煅烧制备的纳米结构电极的光电转换效率最高. 对聚3-甲基噻吩修饰的纳米结构TiO2和摩尔比为3∶1, 于530 ℃煅烧的复合纳米粒子构成的纳米结构电极进行光电性能研究, 结果表明, 聚3-甲基噻吩与半导体纳米粒子之间存在p-n结, 在一定条件下p-n结的存在有利于光生电子/空穴的分离, 从而提高了光电转化效率.     

Composite Electrode SnO2／TiO2 for Dye-Sensitized Solar Cells

Composite nanoporous electrode SnO2/TiO2 was fabricated for the dye sensitized solar cell (DSSC) with N3 (Cis-Ru). After introducing of TiO2, the open-circuit photovoltage (Voc) was higher than that of the pure SnO2 electrode, while short-circuit photocurrent (Isc) was varied with the ratio of the TiO2. Appropriate content of the TiO2 can be beneficial to the efficiency of the solar cell, and it gives negative impact on the composite electrode when the content of TiO2 is higher.     

Nanocomposite materials from latex and cellulose whiskers

Composite materials were processed by casting a mixture of aqueous suspensions of latex and microfibrils. These microfibrils, or whiskers, are extracted from a sea animal and are monocrystals of cellulose, with an aspect ratio around 100 and an average diameter of 20 nm. It has been found that the mechanical properties (shear modulus) are increased by more than two orders of magnitude in the rubbery state of the polymeric matrix, when the whisker content was 6% (w/w). This very large effect is discussed on the basis of different types of mechanical models and it is concluded that these whiskers form a rigid network, probably linked by hydrogen bonds. The formation of this network is assumed to be governed by a percolation mechanism.     

N-TiO2/ZnO复合纳米管阵列的掺杂机理及其光催化活性

以ZnO纳米柱阵列为模板, 采用溶胶-凝胶法制备出TiO2/ZnO和N掺杂TiO2/ZnO的复合纳米管阵列. 扫描电镜(SEM)、X射线光电子能谱(XPS)和紫外-可见漫反射吸收光谱(UV-Vis)的结果表明: 两种阵列的纳米管均为六角形结构, 直径约为100 nm, 壁厚约为20 nm; 在N-TiO2/ZnO复合纳米管阵列中, 掺入的N离子主要是以N-Ox、N-C和N-N的形式化学吸附在纳米管表面, 仅有少量的N离子以取代式掺杂的方式占据TiO2晶格O的位置; 表面N物种形成的表面态能级和取代式掺杂导致带隙的窄化, 增强了纳米管阵列的光吸收效率, 促进了光生载流子的分离. 光催化实验结果表明, N离子的掺杂有利于N-TiO2/ZnO复合纳米管阵列光催化活性的提高.     

Surface and interface characterization of polyester‐based polyurethane/nano‐silica composites

Polyester‐based polyurethane/nanosilica composites were prepared via in situ polymerization and investigated by contact angle measurement, transmission electron microscopy (TEM), atomic force microscopy (AFM) and peel testing in an Instron testing machine. The contact angle and surface free energy results show that nanosilica tended to enrich at the interface between nanocomposite polymers and the substrates, TEM indicated that nanosilica particles were evenly dispersed in the bulk and AFM demonstrated that nanoparticles were located at both the surfaces and interfaces of nanocomposite polymers and that the roughness of both the surfaces and interfaces had a decreasing tendency as the nanosilica content increased, as did the adhesion strength between the nanocomposite polymers and substrates. Copyright © 2003 John Wiley & Sons, Ltd.     

液化石油气水蒸气重整镍催化剂新型载体研究

以共沉淀法合成了硅铝系载体（AS和SA），并采用改性天然高铝石为原料合成了矿物质载体（MC-1和MC-2）,采用浸渍法合成了镍负载型催化剂。用常压固定床管式反应器，考察了液化石油气水蒸气重整反应活性，通过XRD、物理吸附等手段对催化剂进行了表征。结果表明，以MC-1、MC-2和SA、AS为载体的催化剂的水蒸气重整活性明显高于目前普遍使用的Ni/α-Al2O3催化剂。以SA为载体，负载5%镍的催化剂具有最好的水蒸气重整活性。在750 ℃，水碳比为2.0的条件下转化率达100％，C1选择性达94.46％。XRD分析结果表明1 300 ℃焙烧后的SA载体中存在α-Al2O3晶型和莫来石结构。硅、铝添加次序对水蒸气重整活性影响较大，硅-铝添加次序的催化剂样品的活性高于铝-硅添加次序的样品，C1选择性提高12.7％。     

Au/Ag复合纳米笼在表面增强拉曼光谱中的应用

表面增强拉曼光谱（SERS）技术是一种基于贵金属纳米结构基底对被检测物进行高灵敏度检测的一种方法.具有特殊纳米结构的贵金属表面受到激光的照射时，金属表面的自由电子会受到极大的振荡，当入射光频率与振荡频率相近时，则会发生表面等离子体共振现象（SPR），使金属表面的局域电场强度极大增强，入射光强度和散射光强度都得到成倍的放大，从而使吸附在贵金属纳米结构表面的分子的拉曼散射信号得到有效的增强.使用NaBH₄还原-酸刻蚀模板法，制备了八面体Au/Ag复合纳米笼，其形貌规整，尺寸均匀约为600 nm，无Cu₂O模板的残留，Au元素均匀负载在Ag纳米笼上，质量分数约为16.8%；Au/Ag复合纳米笼的紫外可见吸收峰相对于Ag纳米笼发生了红移，更重要的是，Au和Ag元素协同赋予了复合纳米笼超高的SERS灵敏度和重复性，Au/Ag复合纳米笼实现了对罗丹明6G的痕量检测（5×10^-14 mol/L），通过时域有限差分法（FDTD）模拟证实：这主要归因于等离子共振作用产生的高电磁场强度；此外，Au元素的加入使Au/Ag复合纳米笼具有优异的抗氧化性和化学稳定性，即使在1%的H₂O₂溶液中浸泡3 h，仍然能够保持优异的SERS性能.八面体Au/Ag复合纳米笼有望成为一种具有应用前景的高灵敏度、高稳定性的SERS基底.