SiO_2负载钼催化剂的合成及其催化乙烯二聚、同系化和歧化的反应性能

从单核及双核二甲胺钼络合物出发,制备了SiO_2负载的钼催化剂。程序升温分解实验(TPDE)及红外测试表明,双核钼络合物与SiO_2作用生成双钼中心物种,此物种可催化乙烯的二聚反应。280℃活化后此双钼中心物种变成单钼中心物种,单钼物种只催化乙烯的同系化及歧化反应。     

配位聚合载体化催化剂ESR研究进展

本文概述了配位聚合载体化催化剂的ESR研究进展,介绍了载体研究、活性中心研究及计算机模拟技术研究方面的发展概况.     

新型大环醚的合成——1,7-N,N′双取代-1,7-二氮-4,10,13-三氧环十五烷的合成

我们曾报道1,10-N,N’-双取代-1,10-二氮-4,7,13,16-四氧环十八烷(1)及1,7-N,N’-双取代-1,7-二氮-4,10-二氧环十二烷(2)二类大环聚醚的合成及其对碱金属离子的络合性能。     

Oxidative coupling of methane over Na-Mn-W/SiO2 catalyst at higher pressure

Na-Mn-W/SiO₂ catalysts were prepared and their catalytic performance for oxidative coupling of methane (OCM) was evaluated in a stainless-steel microreactor at elevated pressure. The results show that a CH₄ conversion of 15.1% with a C₂₊ selectivity of 71.8% was obtained under 750^oC, 1.0×10⁵h^-1 GHSV, CH₄/O₂ ratio of 8 and 1.0 MPa. Moreover, 17.3% CH₄ conversion with 51.6% C₂ selectivity and 23.6% C₃-C₄ selectivity was obtained under 750^oC, 2.0×10⁵h^-1 GHSV, CH₄/O₂ ratio of 8 and 1.0 MPa.     

含双键侧基的聚氧乙烯与苯乙烯的接枝共聚物及其产物的性质

由环氧乙烷及烯丙基缩水甘油醚合成含双键侧基的聚氧乙烯用苯乙烯接枝共聚,接枝效率可达50％左右.接枝产物经纯化,用IR及~1H NMR表征.该产物与LiClO_4的络合物有较高的室温导电率,其PEO含量在70％及EO/Li=20/1时,25℃的导电率接近10~(-4)S/cm.此外,该接枝共聚物有较高的乳化能力.在Williamson固液反应中具有良好的相转移催化作用.     

铜离子交换改性的沸石催化剂上甲烷的非氧芳构化

已有研究表明，ＭｏＯ３／ＨＺＳＭ５是甲烷非氧芳构化的优良催化剂，在９７３Ｋ下甲烷转化率达６％～８％，苯选择性高于８０％，这为非氧气氛下甲烷的芳构化反应展示了非常诱人的前景［１～１２］．但是，该催化剂的活性和稳定性尚有待进一步提高，目前已有使用Ｐｔ，...     

铜基催化剂的结构、物性及其对混合碳四选择加氢反应的催化性能

 用XRD，XPS，SEM和H2－TPR等手段研究了铜基负载型催化剂的结\r\n构和物性及其对混合碳四加氢脱炔的催化性能．结果表明，在负载铜催\r\n化剂中加入一定量的Co可提高催化剂的加氢脱炔活性，而Co含量较少时\r\n加入少量的Ce也能提高催化剂的活性和选择性．Cu和Co之间存在着相互\r\n协同作用，使得活性组分在催化剂表面偏析，CuO在催化剂表面呈非晶\r\n相分散状态，催化剂颗粒粒径变小，催化剂更容易被还原，从而改善了\r\n催化剂的催化性能．     

聚合物载体－稀土金属络合物的研究ⅩⅤ．聚（苯乙烯－丙烯酰胺）载体－氯化钕络合物对异戊二烯聚合的催化行为

研究了聚（苯乙烯－丙烯酰胺）（ＰＳＡＣ）载体－氯化钕（ＮｄＣｌ３）络合物对异戊二烯（Ｉｐ）聚合的催化行为．ＰＳＡＣ·ＮｄＣｌ３络合物保留了小分子稀土催化剂对双烯烃聚合的催化规律和高度的定向效应．络合物的催化活性随着Ｎｄ／Ｉｐ和Ａｌ／Ｎｄ比的增加而增加，所得聚异戊二烯的特性粘数［η］却随之下降．聚异戊二烯的顺式－１，４结构含量达９５％．此外，ＰＳＡＣ·ＮｄＣｌ３络合物的活性受ＰＳＡＣ和ＰＳＡＣ·ＮｄＣｌ３的组成与结构的影响．在一定的条件下，络合物的活性随着ＰＳＡＣ中功能团含量的增加而下降．ＰＳＡＣ中单体链节交替分布的程度越低，络合物的活性越高     

A Novel Cu-Mo／ZSM-5 Catalyst for NOx Catalytic Reduction with Ammonia

The Cu-Mo/ZSM-5 catalysts with different Cu/Mo ratios were prepared by wet impregnation method, and their catalytic performance for selective catalytic reduction of NOx was studied. The results showed that Cu-Mo/ZSM-5 is a very effective catalyst for NOx catalytic reduction with ammonia, especially when Cu/Mo molar ratio is about 1.5. It not only exhibited the extremely high catalytic activity, but also showed good stability for 02. The bulk phase structure of Cu-Mo/ZSM-5 catalysts was determined by XRD technique, and the results indicated that there is a maximum dispersion for Cu species when Cu/Mo molar ratio is 1.5, and an interaction between Cu and Mo along with HZSM-5 may be present in Cu-Mo/ZSM-5, which may possibly result in a special structure favorable for the catalytic reduction of NOx over Cu-Mo/ZSM-5 catalyst.     

合成气制低碳烯烃K－Fe－MnO／MgO催化剂的研究Ⅰ．MnO助剂的作用

采用ＣＯ加氢反应、ＣＯ－ＴＰＤ、ＣＯ／Ｈ＿２－ＴＰＳＲ及Ｃ＿２Ｈ＿４／Ｈ＿２－ＴＰＳＲ等手段，研究合成气制低碳烯烃反应Ｋ－Ｆｅ－ＭｎＯ／ＭｇＯ催化剂中ＭｎＯ的助剂作用。结果表明ＭｎＯ能大幅度提高低碳烯烃的选择性，尤其是乙烯的选择性；ＭｎＯ能抑制催化剂表面的乙烯加氢，因而有利于提高低碳烯烃的选择性及烯／烷的比值。