Hydroxyapatite-supported copper(II)-catalyzed azide-alkyne [3+2] cycloaddition with neither reducing agents nor bases in water

Copper(II)-exchanged hydroxyapatite, prepared by ion-exchanging of Ca(II) in calcium hydroxyapatite [Ca₁₀(PO₄)₆(OH)₂] with Cu(NO₃)₂ at 70 °C in water, functions as a reusable heterogeneous catalyst with neither reducing agents nor bases for azide-alkyne [3+2] cycloaddition at 50 °C in water under air.     

还原温度对Fe-Mo催化剂性质及F-T合成性能的影响

研究了还原温度对Fe-Mo催化剂性质及费托(F-T)合成性能的影响。采用N₂物理吸附、X射线衍射、穆斯堡尔谱和H₂程序升温脱附技术对催化剂进行了表征。结果表明,随还原温度升高,金属铁晶粒粒径增大,金属铁上的H₂吸附量先升后降;催化剂还原度提高,反应态催化剂碳化铁含量递增。催化剂F-T合成性能在280 ℃、1.5 MPa、2 000 h^-1、合成气H₂/CO比为2.0条件下在固定床反应器中测试。反应结果表明,随还原温度提高,催化剂接近稳态时的活性和重质烃选择性(C₅⁺)先升后降,而甲烷选择性则先降后升。350 ℃还原催化剂具有最佳F-T合成反应性能。     

SCR脱硝催化剂失活及其原因研究

以运行后的蜂窝型SCR（Selective catalytic reduction）催化剂和新鲜催化剂为研究对象。应用红外光谱、氮气吸脱附、X射线衍射、电镜扫描等手段对新鲜催化剂及运行后催化剂进行表征。结果表明,运行后催化剂表面官能团发生了变化,比表面积严重降低,载体（TiO₂）产生了型变,并且催化剂表面微粒出现了团聚现象。对运行后催化剂活性降低的原因进行了研究,结果表明,脱硝催化剂在运行过程中遭遇了突发性高温(如t> 650℃),导致活性出现劣化。此外,催化剂表面沉积物中水溶性离子及砷、磷等物质也对催化活性产生了影响。     

甲醇在不同结构氧化钨-Pt/C催化剂上的电催化氧化行为

采用水热法合成2种氧化钨（WO3）纳米材料,并利用XRD和电子探针显微分析仪（EPMA）进行了表征。 利用循环伏安法研究了Pt-WO3/C电极对甲醇氧化的电催化活性。 结果表明,Pt-WO3/C催化剂对甲醇氧化的电催化活性优于Pt/C催化剂,且氧化钨质量分数为20%的Pt-氧化钨/C催化效果最好。 与青铜相氧化钨掺杂的Pt/C电极比较,掺杂焦绿石型氧化钨的Pt/C电极催化性能有很大提高,这是由于焦绿石型氧化钨表面具有较多OHads。 质量分数20%的Pt-焦绿石型氧化钨/C在0.5 mol/L CH3OH+1 mol/L H2SO4溶液中对甲醇氧化的峰电流密度达到87.2×10-3 A/cm2。     

沉淀及老化温度对浆态床合成甲醇CuO/ZnO/Al2O3催化剂活性及稳定性的影响

利用浆态床反应器,考察了沉淀及老化温度对CuO/ZnO/Al₂O₃催化剂催化合成甲醇的活性及稳定性的影响,并用XRD、BET、FT-IR以及XPS等技术对前驱体及催化剂进行了表征。结果表明,前驱体物相主要以孔雀石(Cu₂(CO₃)(OH)₂)和类孔雀石((Cu,Zn)₂(CO₃)(OH)₂)为主,其中,70 ℃沉淀和80 ℃老化条件下制备的前驱体具有适当的结晶度,焙烧后的催化剂中CuO分布均匀,Cu元素的电子结合能位移最大,CuO与ZnO之间作用较强,催化剂的性能最佳,时空收率和失活率分别达到了153.3 g/(kg_cat·h)和1.44%/d。     

热扩散法制备MoO3/SiO2催化草酸二甲酯和苯酚酯交换反应

采用热扩散法（TS）和等体积浸渍法制备了MoO₃/SiO₂催化剂用于草酸二甲酯和苯酚酯交换反应.结果表明,热扩散法制备的10%MoO₃/SiO₂-TS催化剂较等体积浸渍法制备的10%MoO₃/SiO₂-C催化剂具有更好的催化性能.运用X射线衍射、Raman光谱、X射线光电子能谱分析、吡啶吸附红外光谱、NH₃程序升温脱附等手段对催化剂进行了表征,发现虽然两种方法制备的催化剂都只有弱Lewis酸中心,钼均以氧化钼单体形式存在,未形成解离和聚合,但是10%MoO₃/SiO₂-TS催化剂较10%MoO₃/SiO₂-C催化剂表面钼含量更高且MoO₃分散得更好.在苯酚用量为0.2mol,10%MoO₃/SiO₂-TS催化剂用量为1.2g,反应温度为180℃,草酸二甲酯与苯酚的摩尔比为2,反应时间为4h的优化条件下,苯酚转化率可达70.9%,甲基苯基草酸酯和草酸二苯酯的收率分别达63.1%和7.7%.     

甲醇制烯烃催化剂失活模型

在固定床反应器中,研究了甲醇制烯烃反应中当SAPO-34分子筛处于失活期时催化剂活性的变化情况,主要考察催化剂活性随反应温度、空速和运行时间的变化,通过对实验数据的分析拟合,得到了催化剂活性与失活时间、反应温度、空速的经验关联式(失活模型),对失活模型的检验表明,该模型与实验数据较为吻合,表明了该式的准确性。 通过对失活模型的分析,获得了当失活速率达到最大时的失活时间与反应时间、空速的关联式,失活过程应服从不均匀表面失活机理,并且当催化剂处于失活区时,失活时间对活性的影响要大于空速和温度。     

Chemoselective hydrogenolysis of tetrahydrofurfuryl alcohol to 1,5-pentanediol over Ir-MoOx/Si02 catalyst

In this work, MoOx promoted Ir/SiO2 catalysts were prepared and used for the selective hydrogenolysis of tetrahydrofurfuryl alcohol （THFA） to 1,5-pentanediol in a continuous flow reactor. The effects of different noble metals （Ir, Pt, Pd, Ru, Rh）, supports and Ir contents were screened. Among the investigated catalysts, 4 wt%Ir-MoOx/SiO2 with a Mo/Ir atomic ratio of 0.13 exhibited the best catalytic performance. The synergy between Ix particles and the partially reduced isolated MoOx species attached on them is essential for the excellent catalytic performance of Ix-MoOx/SiO2. The catalyst exhibited a better hydrogenolysis efficiency of THFA with the selectivity of 1,5-pentanediol of 65%-74% at a conversion of THFA of 70%-75% when the initial THFA concentration is ranging from 20 wt% and 40 wt%. And higher system pressure was also in favor of the conversion of THFA. During a stability test, the conversion of THFA and 1,5-pentanediol yield over Ix-MoOz/SiO2 decreased with reaction time, which can be explained by the leaching of Mo species during the reaction.     

Facile Fabrication of Platinum Nanoparticles Supported on Nitrogen-doped Carbon Nanotubes and Their Catalytic Activity

A facile impregnation method under mild condition is designed for synthesis of highly dispersed Pt nanoparticles with a narrow size of 4-7 nm on nitrogen-doped carbon nanotubes （CNx）. CNx do not need any pre-surface modification due to the inherent chemical activity. The structure and nature of Pt/CNx were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and energy dispersive spectroscopy spectrum. All the experimental results revealed that the large amount of doped nitrogen atoms in CNx was virtually effective for capturing the Pt（IV） ions. The improved surface nitrogen functionalities and hydrophilicity contributed to the good dispersion and immobi- lization of Pt nanoparticles on the CNx surface. The Pt/CNx served as active and reusable catalysts in the hydrogenation of allyl alcohol. This could be attributed to high dispersion of Pt nanoparticles and stronger interaction between Pt and the supports, which prevented the Pt nanoparticles from aggregating into less active Pt black and from leaching as well.     

KCl对Cu-K-La/γ-Al2O3催化剂上HCl氧化反应性能的影响

采用等体积浸渍法制备了Cu-K-La/γ-Al₂O₃催化剂,考察了KCl对该催化剂催化HCl氧化制Cl₂反应性能的影响. 当KCl的负载量为5 wt%时,Cu-K-La/γ-Al₂O₃催化剂表现出较好的催化活性和稳定性,可在较大的原料气空速变化范围内使用. 在0.1 MPa,360 ℃,空速450 L/（kg-cat·h）和HCl/O₂摩尔比为2：1的反应条件下,Cu-K-La/γ-Al₂O₃催化剂上HCl转化率在100 h内保持85%以上. 表征结果表明,Cu,K和La物种均高度分散于γ-Al₂O₃载体表面;一定量KCl的加入可降低Cu²⁺ → Cu⁺的还原温度,从而提高Cu²⁺活性中心的催化活性.