提高非贵金属临氢脱腊催化剂异构化能力的研究

通过水热条件下合成分子筛试验条件的考察,获得了合成条件和性能良好的ZSM-8分子筛。采用无定形硅铝和ZSM-8分子筛制备出复合载体型的非贵金属临氢脱腊催化剂,通过锌和钨改性组分的添加,提高现有工业催化剂的异构化能力。实验结果表明,不同复合载体、改性组分对催化性能有较大影响,但改性组分的添加次序无明显作用。与以前β沸石基催化剂性能相比,ZSM-8基催化剂不仅提高了润滑油收率,而且产品润滑油的粘度指数也明显提高。催化性能的改进可以归结为改性后催化剂异构化能力的提高。     

Redox behavior of V/MgO catalyst in H2S wet oxidation at room temperature

The room temperature wet catalytic oxidation was conducted in a batch reactor with V/MgO catalyst. The XRD study of the catalyst used indicated that V/MgO could not only oxidize H2S to sulfur selectively, but also prevent the sulfidation of metal oxide effectively at the room temperature. The XPS study indicated that the H2S oxidation with V/MgO could proceed by a redox mechanism (V⁵⁺↔ V⁴⁺) and that V³⁺ formation (V⁴⁺→ V³⁺), was responsible for the deactivation of V/MgO. This revised version was published online in June 2006 with corrections to the Cover Date.     

New coordination catalysts based on rare earth compounds for polymerization of 1-octene

The study of rare earth coordination catalysts for polymerization of 1-octene has been successfully carried out for the first time. Some features and kinetic behavior of polymerization of 1-octene by Nd(naph)₃–AIEt₃ catalyst system in tetrachloro-methane are described. The overall polymerization activation energy E_a measured was 74.5 kJ/mol and the rate equation could be expressed as R_p = k_p [Nd] [M] (k_p = 3.21 × 10^?3 L/mol s, at 50°C). The catalytic activity of various rare earth elements in Ln (naph)₃ and ligands in NdL₃ for the polymerization was compared. A 1-octene oligomer with double bonds was obtained. It is either a white or pale yellow waxy semi-solid. Its number-average molecular weight is about 10³ and the molecular weight distribution is less than 2.     

Palladium-catalyzed and organozinc-promoted synthesis of dienes from allylic esters possessing an acyloxy or alkoxy group

Organozinc and a Pd catalyst promoted formation of dienes from allylic esters possessing a leaving group such as acyloxy and alkoxy groups next to the allyl moiety. The reaction proceeded with high regio- and stereoselectivity when applied to secondary allylic substrates.     

Zirconyl chloride promoted highly efficient solid phase synthesis of amide derivatives

An efficient solid phase route for the synthesis of amide derivatives by the reaction of carboxylic acids with urea in the presence of catalytic amount of zirconyl chloride under microwave irradiation conditions was described.In this way,a range of interesting amide derivatives was obtained in good to excellent yields.The catalyst was recycled with fresh reactants and it gave almost similar results without significant loss of activity up to the third run.     

硅胶担载四核羰基钴催化剂的EXAFS和IR研究

本文以透射法EXAFS和IR等手段研究了四核羰基钴金属簇Co_4(CO)_(10)(PPh)_2担载在SiO_2上以后及用于烯烃醛化反应前后的变化,确定了相应的结构参数并探讨了催化活性与结构的关系。     

NdOx作为助催化剂对PtRu/C电催化氧化甲醇活性的影响

采用沉积-还原法制备了PtRu-NdOx/C催化剂, 借助TEM、EDS和XRD等测试手段对其进行了微结构和组成的表征. 结果表明, 催化剂中Pt与Ru以合金形式存在, 而Nd的氧化物则以无定形形态存在. 催化剂粒子的平均粒径在2 nm左右, 晶胞参数为0.3896 nm, Nd氧化物的加入对PtRu合金的晶体结构影响不明显. 采用循环伏安法和计时电流法, 比较了PtRu-NdOx/C催化剂和PtRu /C催化剂对甲醇氧化的电催化活性, 结果表明, 加入Nd的氧化物作为助催化剂能明显提高PtRu /C催化剂对甲醇氧化的电催化性能.     

Hydrothermal Synthesis of Mo-Based Oxide Catalysts and Selective Oxidation of Alkanes

Mo-V-M(=Al, Ga, Bi, Sb and Te)–O mixed oxide catalysts were synthesized hydrothermally for the first time, characterized structurally, and tested for ethane and propane oxidation after activation by various ways. These catalysts were black solids of rod-shaped (fiber like) crystals, which had a layer structure in the direction of fiber axis and a high dimensional arrangement of metal octahedra in the cross-section plane. These fresh crystalline materials became active for catalytic oxidation of alkanes after heat-treatment at 600 °C and subsequent grinding in order to increase exposed plane of the cross-section. The resulting catalysts were very active for an oxidative dehydrogenation of ethane with 80% of the ethylene selectivity in the reaction temperature range of 300 to 400 °C and also showed about 50% selectivity to acrylic acid in the propane oxidation. Multi-functional character which derived from the high dimensional structure of the catalysts and mechanism of the selective alkane oxidation were discussed.     

甲烷在Mo/HZSM-5催化剂上的脱氢聚合反应

对不同Mo含量的Mo／HZSM－5催化剂的结构进行了表征，并对这些催化剂的甲烷非氧气氛下的转化反应进行了考察．催化剂的BET比表面积及酸性随Mo含量的增加而降低，当Mo含量大于5％时，Mo对ZSM－5分子筛的晶型有影响，并出现MoO3物相．甲烷在700℃时可高选择性地生成苯和乙烯，最佳Mo含量大约为2％．纯的MoO3或HZSM－5上该反应几乎不进行，因此，可能是分散的钼氧离子和分子筛的酸中心是甲烷转化的活性中心，只有二者的协同作用才能促进甲烷的转化．反应后催化剂中的钼物种被还原了．催化剂上的积炭可能是催化剂失活的主要原因之一，烧炭后催化剂活性基本恢复．     

丙烯气相直接环氧化Au/TiO2催化剂的研究

在H2和O2共存条件下，金催化剂催化丙烯气相直接环氧化反应是近年来发展起来的一种新型环氧丙烷(PO)合成技术．本文采用沉积沉淀法制备了一系列Au／TiO2催化剂，考察了反应溶液的pH值、Au负载量、沉淀剂以及焙烧温度等因素对催化剂丙烯环氧化催化性能的影响．结果表明制备条件对催化性能有明显影响：反应溶液的pH值为7．5及Au负载量为2．4％时所得催化剂活性最好；当以Na2CO3、NaOH等含Na^ 物质作为沉淀剂时，催化性能明显优于Li^ 、K^ 等其它碱金属离子；400℃焙烧制得的催化剂活性较好，在50℃低温反应条件下，环氧丙烷得率可达1．3％．HRTEM结果表明，催化剂中Au组分高度分散于载体表面，且随着焙烧温度的增加Au粒因发生聚集而变大，从而影响了催化剂的活性．表面XPS分析证实，活性较好的Au／TiO2催化剂中活性组分Au除部分呈氧化态外，主要是以金属态的形式存在．