ZnO纳米管有序阵列与Cu2O纳米晶核壳结构的光电化学性能及全固态纳米结构太阳电池研究简

采用电化学方法在铟锡氧化物(ITO)导电玻璃基底上制备了高度有序的ZnO纳米管阵列,然后在ZnO纳米管阵列上电化学沉积Cu2O纳米晶颗粒,获得了一维有序Cu2O/ZnO核壳式纳米阵列结构,通过控制Cu2O纳米晶的沉积电量得到不同厚度的Cu2O壳层,并对该核壳式纳米阵列的形貌和结构进行了分析. 以Cu2O/ZnO一维核壳式纳米阵列结构为光电极组装全固态纳米结构太阳电池,研究了Cu2O壳层厚度对光电极光吸收性能、光电性能以及组装电池光伏性能的影响,优化了电池中对电极材料的喷金厚度. 结果表明,以Cu2O沉积电量为1.5 C的Cu2O/ZnO为光活性层,以4 mA电流下真空镀金20~25 min的铜基底为对电极组装的简易太阳电池最高可获得0.013%的光电转换效率.     

ZnO纳米线基MWNTs/PVDF复合热电材料的制备及特性研究

将不同比例的多壁碳管(MWNTs)与聚偏二氟乙烯(PVDF)聚合物混合后,喷涂于n型ZnO半导体纳米线阵列上,制备了一种新型ZnO纳米线基MWNTs/PVDF热电复合材料.与以往采用价格昂贵的p型与n型单壁碳纳米管(SWNTs)与聚合物混合制备的复合热电材料特性相比,这种新型热电复合材料在降低制造成本的同时,利用分散于聚合物中MWNTs的一维电子传输特性及形成的大量界面势垒,加上ZnO半导体纳米线具有的较高载流子密度与迁移率,提高了复合热电材料中电子的输运特性,增加了材料对声子的散射强度.测试发现,在一定的温度梯度下,随着MWNTs添加质量百分比的增加,热电材料的温差电动势和电导率也随之增加,但其Seebeck系数变化量不大.研究表明,这种热电材料有望替代采用p型与n型SWNTs构建的SWNTs/PVDF复合热电材料.研究结果对开发超轻、无毒、廉价、可应用于各种微纳电子领域的新型电源具有重要的参考价值.     

Investigation of the vibrational modes of ZnO grown by MOCVD on different orientation planes

Wurtzite ZnO thin films were prepared on sapphire substrate by metal organic chemical vapor deposition (MOCVD). Raman scattering studies on different crystallographic textures were performed in the backscattering geometry, and polarization effect is investigated in different configurations and . ZnO Raman modes are investigated in each texture. In the case of ZnO thin film deposed on r‐() sapphire plane and using backscattering geometry, new Raman line was observed at 390 cm⁻¹ because this mode has not been noticed in this geometry. It is shown that the frequencies of the quasi‐phonon modes of the examined thin film are in good agreement with the theoretical values calculated within the framework of Loudon model. Copyright © 2014 John Wiley & Sons, Ltd.     

Study on the nanoscale current of ZnO film by photoassisted peak force tunnel atomic force: A novel technique for UV detection

ZnO film-based ultraviolet (UV) detector was fabricated by photoassisted peak force tunnel atomic force (PFTUNA) on fluorine tin oxide (FTO) substrate. The PFTUNA current in dark and in UV light was ~0.1 and 2.0 nA, respectively. The UV sensitivity (photocurrent/dark current) is more than 20. The response time and the recovery time are ~0.12 and 0.32 s, respectively. The UV sensing mechanism is that the holes will transport to the ZnO surface to capture the adsorbed oxygen ions to weaken the depletion layer under UV illumination. The PFTUNA current between the tip and the ZnO film is consistent with the Richardson–Schottky (RS) thermionic emission model.     

Influence of the particle size on the antibacterial activity of green synthesized zinc oxide nanoparticles using Dysphania ambrosioides extract,supported by molecular docking analysis

Bacteria-associated infections have increased in recent years due to treatment resistance developed by these microorganisms. Due to the high antibacterial capacity associated with their nanometric size, nanoparticles, such as zinc oxide (ZnO), have proven to be an alternative for general medical procedures. One of the methodologies to synthesize them is green synthesis, where the most commonly used resources are plant species. Using Dysphania ambrosioides extract at various synthesis temperatures (200, 400, 600, and 800 °C), zinc oxide nanoparticles (ZnO-NPs) with average sizes ranging from 7 to 130 nm, quasi-spherical shapes, and hexagonal prism shapes were synthesized. Larger sizes were obtained by increasing the synthesis temperature. The ZnO crystalline phase was confirmed by X-ray diffraction and transmission electron microscopy. The sizes and shapes were observed by field emission scanning electron microscopy. The Zn-O bond vibration was identified by Fourier transform infrared spectroscopy. Thermogravimetry showed the stability of ZnO-NPs. The antibacterial evaluations, disk diffusion test, and minimum bactericidal concentration, demonstrated the influence of particle size. The smaller the nanoparticle size, the higher the inhibition for all pathogenic strains: Staphylococcus aureus, Staphylococcus epidermidis, Escherichia coli, Pseudomonas aeruginosa, and dental pathogens: Streptococcus mutans, Streptococcus sanguinis, Porphyromonas gingivalis, and Prevotella intermedia. The molecular docking study showed a favorable interaction between ZnO-NPs and some proteins in Gram-positive and Gram-negative bacteria, such as TagF in Staphylococcus epidermidis and AcrAB-TolC in Escherichia coli, which led to proposing them as possible targets of nanoparticles.     

Jute stick extract assisted hydrothermal synthesis of zinc oxide nanoflakes and their enhanced photocatalytic and antibacterial efficacy

In this paper, we used green and hydrothermal methodology to prepare zinc oxide (ZnO) nanoflakes (NFs) with jute stick extract (J–ZnO NFs) as growth substrate. The prepared materials were characterized using different analytical techniques including ultraviolet–visible spectroscopy (UV–vis), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), fourier transform infrared (FTIR) spectroscopy, and X-ray photoelectron spectroscopy (XPS). The characteristic absorption peak for ZnO NFs and J–ZnO NFs were observed from the UV–vis spectrum at 373 and 368 nm respectively. The hexagonal wurtzite crystal structure of ZnO NFs and J–ZnO NFs was confirmed by XRD analysis. FESEM and TEM analyses of synthesized J–ZnO NFs confirmed their NFs shape and collectively flower-like structure formation by the assembly of NFs of J–ZnO on cellulose of jute stick extract substrate. The FTIR analysis revealed the functional groups of jute stick extract biomolecules, mainly cellulose, are responsible for the formation of collectivel flower like J–ZnO NFs structure. The XPS analysis revealed the surface and chemical compositions (Zn, C, and O) of J–ZnO NFs. The photocatalytic performance of ZnO NFs and J–ZnO NFs samples was carried out by the degradation of methylene blue (MB) dye solution under UV light irradiation. The degradation efficiency of ZnO NFs and J–ZnO NFs was obtained 79 % and 89 %, respectively, for 5 h. Notably, the degradation efficiency of the J–ZnO NFs was 98 % after 8 h of irradiation, which is very inspiring. The both NFs exhibited first-order kinetics with MB photodegradation. We also examined the possible antibacterial activity of both samples against Escherichia coli (E. coli) pathogens, which demonstrated a significant result with a 17 mm and 19 mm zone of inhibition by ZnO NFs and J–ZnO NFs respectively.     

Green Synthesis and Applications of ZnO and TiO2 Nanostructures

Over the last two decades, oxide nanostructures have been continuously evaluated and used in many technological applications. The advancement of the controlled synthesis approach to design desired morphology is a fundamental key to the discipline of material science and nanotechnology. These nanostructures can be prepared via different physical and chemical methods; however, a green and ecofriendly synthesis approach is a promising way to produce these nanostructures with desired properties with less risk of hazardous chemicals. In this regard, ZnO and TiO₂ nanostructures are prominent candidates for various applications. Moreover, they are more efficient, non-toxic, and cost-effective. This review mainly focuses on the recent state-of-the-art advancements in the green synthesis approach for ZnO and TiO₂ nanostructures and their applications. The first section summarizes the green synthesis approach to synthesize ZnO and TiO₂ nanostructures via different routes such as solvothermal, hydrothermal, co-precipitation, and sol-gel using biological systems that are based on the principles of green chemistry. The second section demonstrates the application of ZnO and TiO₂ nanostructures. The review also discusses the problems and future perspectives of green synthesis methods and the related issues posed and overlooked by the scientific community on the green approach to nanostructure oxides.     

Sn掺杂ZnO薄膜的室温气敏性能及其气敏机理

采用化学气相沉积方法在预制好电极的玻璃基底上制备出Sn掺杂ZnO薄膜和纯ZnO薄膜. 两种样品典型的形貌为四足状ZnO晶须, 其直径约为150-400 nm, 呈疏松状结构. 气敏测试结果显示Sn掺杂ZnO薄膜具有优良的室温气敏性, 并对乙醇具有良好的气敏选择性, 而纯ZnO薄膜在室温条件下对乙醇和丙酮均没有气敏响应. X射线衍射结果表明两种样品均为六方纤锌矿结构. Sn掺杂ZnO样品中没有出现Sn及其氧化物的衍射峰, 其衍射结果与纯ZnO样品对比, 衍射峰向小角度偏移. 光致发光结果表明, Sn掺杂ZnO薄膜与纯ZnO薄膜均出现紫外发光峰和缺陷发光峰, 但是Sn的掺杂使得ZnO的缺陷发光峰明显增强. 将Sn掺杂ZnO样品在空气中退火后, 其室温气敏性消失, 说明Sn掺杂ZnO样品的室温气敏性可能与其缺陷含量高有关. 采用自由电子散射模型解释了Sn掺杂ZnO薄膜的室温气敏机理.     

Ultrasonic-assisted degradation of phenazopyridine with a combination of Sm-doped ZnO nanoparticles and inorganic oxidants

Pure and samarium doped ZnO nanoparticles were synthesized by a sonochemical method and characterized by TEM, SEM, EDX, XRD, Pl, and DRS techniques. The average crystallite size of pure and Sm-doped ZnO nanoparticles was about 20 nm. The sonocatalytic activity of pure and Sm-doped ZnO nanoparticles was considered toward degradation of phenazopyridine as a model organic contaminant. The Sm-doped ZnO nanoparticles with Sm concentration of 0.4 mol% indicated a higher sonocatalytic activity (59%) than the pure ZnO (51%) and other Sm-doped ZnO nanoparticles. It was believed that Sm³⁺ ion with optimal concentration (0.4 mol%) can act as superficial trapping for electrons in the conduction band of ZnO and delayed the recombination of charge carriers. The influence of the nature and concentration of various oxidants, including periodate, hydrogen peroxide, peroxymonosulfate, and peroxydisulfate on the sonocatalytic activity of Sm-doped ZnO nanoparticles was studied. The influence of the oxidants concentration (0.2–1.4 g L⁻¹) on the degradation rate was established by the 3D response surface and the 2D contour plots. The results demonstrated that the utilizing of oxidants in combination with Sm-doped ZnO resulting in rapid removal of contaminant, which can be referable to a dual role of oxidants; (i) scavenging the generated electrons in the conduction band of ZnO and (ii) creating highly reactive radical species under ultrasonic irradiation. It was found that the Sm-doped ZnO and periodate combination is the most efficient catalytic system under ultrasonic irradiation.     

Ultrasonically induced ZnO–biosilica nanocomposite for degradation of a textile dye in aqueous phase

In the present study, a porous clay-like support with unique characteristics was used for the synthesis and immobilization of ZnO nanostructures to be used as sonocatalyst for the sonocatalytic decolorization of methylene blue (MB) dye in the aqueous phase. As a result, the sonocatalytic activity of ZnO–biosilica nanocomposite (77.8%) was higher than that of pure ZnO nanostructures (53.6%). Increasing the initial pH from 3 to 10 led to increasing the color removal from 41.8% to 88.2%, respectively. Increasing the sonocatalyst dosage from 0.5 to 2.5 g/L resulted in increasing the color removal, while further increase up to 3 g/L caused an obvious drop in the color removal. The sonocatalysis of MB dye over ZnO–biosilica nanocomposite was temperature-dependent. The presence of methanol produced the most adverse effect on the sonocatalysis of MB dye. The addition of chloride and carbonate ions had a negligible effect on the sonocatalysis, while the addition of persulfate ion led to increasing the color removal from 77.8% to 99.4% during 90 min. The reusability test exhibited a 15% drop in the color removal (%) within three consecutive experimental runs. A mineralization efficiency of 63.2% was obtained within 4 h.